4032 aluminum alloy spectroscopic and chemical standard sample and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A standard sample, aluminum alloy technology, applied in the preparation of test samples, etc., can solve the problem of not having 4032 high-silicon aluminum alloy materials, and achieve a wide range of applications
Active Publication Date: 2013-12-25
NORTHEAST LIGHT ALLOY CO LTD
View PDF8 Cites 12 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, there are no aluminum alloy spectrum and chemical standard samples suitable for 4032 high-silicon aluminum alloy m...
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment approach 1
[0017] Specific implementation mode 1: In this specific implementation mode, the 4032 aluminum alloy spectrum and chemical standard samples are specifically composed of the following ingredients according to the mass percentage ratio: 4.5-13.5%Si, 0.13%-0.9%Fe, 0.07%-1.74 %Cu, 0.023%~0.316%Mn, 0.35%~1.85%Mg, 0.006%~0.053%Sn, 0.023%~0.161%Cr, 0.049%~1.26%Ni, 0.04%~0.270%Zn, 0.02%~0.17% Ti, 0.010% to 0.088% Pb, 0.0019% to 0.013% Na and the balance is Al.
specific Embodiment approach 2
[0018] Embodiment 2: In this embodiment, the 4032 aluminum alloy spectrum and chemical standard sample differ from Embodiment 1 in that it is composed of the following ingredients according to the mass percentage ratio: 4.52% Si, 0.13% Fe, 1.74 %Cu, 0.023%Mn, 0.38%Mg, 0.0068%Sn, 0.023%Cr, 1.26%Ni, 0.04%Zn, 0.17%Ti, 0.088%Pb, 0.0019%Na and the balance is Al. The rest are the same as in the first embodiment.
specific Embodiment approach 3
[0019] Specific embodiment three: The 4032 aluminum alloy spectrum and chemical standard sample in this specific embodiment differ from specific embodiment one or two in that it consists of the following ingredients according to the mass percentage ratio: 7.57%Si, 0.28%Fe , 0.332%Cu, 0.06%Mn, 0.70%Mg, 0.0087%Sn, 0.161%Cr, 0.19%Ni, 0.053%Zn, 0.051%Ti, 0.064%Pb, 0.0040%Na and the balance is Al. The rest are the same as the specific embodiment one or two.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a 4032 aluminum alloy spectroscopic and chemical standard sample and a preparation method thereof, relating to an aluminum alloy spectroscopic and chemical standard sample and a preparation method thereof. Aiming to solve the problem that no aluminum alloy spectroscopic and chemical standard sample suitable for a 4032 high-silicon aluminum alloy material exists at present, the invention provides an aluminum alloy spectroscopic and chemical standard sample suitable for the 4032 high-silicon aluminum alloy material and a preparation method of the aluminum alloy spectroscopic and chemical standard sample. A final component data verification result is obtained through component designing, weighting, smelting, casting, initial uniformity check, processing and forming, spectroscopic standard sample uniformity check, chemical standard sample uniformity check, value defining and treaty revising according to GB8170. The preparation method disclosed by the invention is used for preparing aluminum alloy spectroscopic and chemical standard samples suitable for 4032 high-silicon aluminum alloy materials; a multi-element aluminum alloy spectroscopic and chemical standard sample prepared by using the method disclosed by the invention is used for correcting a 4032 aluminum alloy quality control detecting instrument.
Description
technical field [0001] The invention relates to an aluminum alloy spectral and chemical standard sample and a preparation method thereof. Background technique [0002] 4032 high-silicon aluminum alloy materials are mainly used for heat-resistant forged aluminum alloys, such as heat-resistant parts such as pistons and automotive parts. As we all know, this century is the era of rapid development of China's automobile industry, so its application is wider and its consumption is larger. The quality control of products depends on instrument detection. In recent years, various enterprises have purchased instruments such as photoelectric direct reading spectrometers and inductively coupled plasma emission spectrometers from abroad. The aluminum alloy spectra and chemical standard samples used for instrument calibration are in demand in my country. The volume is increasing year by year. Especially after entering the international market, in order to be in line with international st...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more