Manufacturing method of non-woven jointless annular elastic bandage

An elastic bandage, jointless technology, applied in the direction of non-woven fabrics, bandages, non-adhesive dressings, etc., can solve the problems of lack of protection, uneven stress, relaxation or deformation, etc., to achieve significant development and elastic durability Good, good protective effect

Inactive Publication Date: 2014-01-01
WUHAN TEXTILE UNIV +1
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The common feature of these two is that it will loosen or deform after a long time, and it will not play a good protective role.
The addition of elastic fibers will affect and woven bandages will have uneven stress due to stitching problems, which will affect the use effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of preparation method of nonwoven jointless annular elastic bandage, it comprises the steps:

[0027] 1) According to the mass percentage of each raw material: polyolefin elastomer 60%, silicone rubber 35%, radiation sensitizer 4.9%, antioxidant 0.1%;

[0028] Select polyolefin elastomer, silicone rubber, radiation sensitizer and antioxidant to mix, send into twin-screw extruder, control the temperature in each zone between 150-200°C, extrude and pelletize to obtain polyolefin mixed masterbatch;

[0029] The polyolefin elastomer is a block copolymer of ethylene and octene POE (ExxonMobil, USA, brand 8230); the silicone rubber is vinyl-terminated polydimethylsiloxane (Jilin City Xiangyou Polymer Material Co., Ltd., brand XY-202-B); radiation sensitizer is triallyl isocyanurate; antioxidant is hindered phenolic (CHEMNOX1010) antioxidant.

[0030] 2) Send the polyolefin masterbatch into the hopper of the melt spinning machine. The temperature of each zone of the me...

Embodiment 2

[0035] A kind of preparation method of nonwoven jointless annular elastic bandage, it comprises the steps:

[0036] 1) According to the mass percentage of each raw material: polyolefin elastomer 70%, silicone rubber 25%, radiation sensitizer 4.9%, antioxidant 0.1%;

[0037] Select polyolefin elastomer, silicone rubber, radiation sensitizer and antioxidant to mix, send into twin-screw extruder, control the temperature in each zone between 150-200°C, extrude and pelletize to obtain polyolefin mixed masterbatch;

[0038] The polyolefin elastomer is a block copolymer of ethylene and octene POE (ExxonMobil, USA, brand 8230); the silicone rubber is vinyl-terminated polydimethylsiloxane (Jilin City Xiangyou Polymer Materials Co., Ltd., brand XY-202-B); radiosensitizer is triallyl isocyanurate; antioxidant is hindered phenols (CHEMNOX1010).

[0039] 2) Feed the polyolefin mixed masterbatch into the hopper of the melt spinning machine. The temperature of each zone of the melt spinning...

Embodiment 3

[0044] A kind of preparation method of nonwoven jointless annular elastic bandage, it comprises the steps:

[0045] 1) According to the mass percentage of each raw material: polyolefin elastomer 75%, silicone rubber 20%, radiation sensitizer 4.9%, antioxidant 0.1%;

[0046] Select polyolefin elastomer, silicone rubber, radiation sensitizer and antioxidant to mix, feed into twin-screw extruder, control the temperature in each zone between 120-170°C, extrude and pelletize to obtain polyolefin mixed masterbatch;

[0047] The polyolefin elastomer is made of propylene-based copolymer POE (ExxonMobil, USA, brand VM6202); the silicone rubber is vinyl-terminated polydimethylsiloxane (Jilin Xiangyou Polymer Material Co., Ltd., brand XY-202-B); radiation sensitizer is acrylate; antioxidant is hindered phenols (CHEMNOX1076).

[0048] 2) Send the polyolefin masterbatch into the hopper of the melt spinning machine. The temperature of each zone of the melt spinning machine is controlled be...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elastic recovery rateaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of novel materials for textiles, particularly relates to a manufacturing method of a non-woven jointless annular elastic bandage. The manufacturing method includes steps of 1), according to weight, feeding 59.8-90% of polyolefin elastomer, 5-40% of silicone rubber, 0.1-5% of radiation sensitizer and 0.1-0.5% of antioxidant into a double-screw extruder and extruding and pelleting to obtain polyolefin mixed master batch; 2), feeding the polyolefin mixed master batch into a hopper of a melt spinning machine, jetting out by a spinning jet, cooling through a side-blowing passage, winding on a roll to obtain a primary bandage by a winding device; 3), feeding the primary bandage into a hot rolling machine to be hot-rolled; 4), disposing the hot-rolled primary bandage in an irradiation environment, irradiating under certain irradiation dose to obtain the non-woven jointless annular elastic bandage. The non-woven jointless annular elastic bandage has the advantages of direct forming, no joints and lasting elasticity.

Description

technical field [0001] The invention belongs to the field of new textile materials, in particular to a method for preparing a non-woven jointless annular elastic bandage. Background technique [0002] Bandages are usually elastic tubular fabrics that support and protect the joints they are worn on, such as knee or elbow pads during sports or ankle bandages that act in a protective or supportive manner. There are generally two types of traditional elastic bandages. One is the loom fabric obtained from elastic fibers, which is shaped into the shape of the protected limb through special sewing techniques; the other is directly formed into the shape of the protected limb by knitting technology. shaped bandage. The common feature of these two types is that they will loosen or deform after a long time, and they will not play a good protective role. The addition of elastic fibers will affect and woven bandages will have uneven stress due to stitching problems, which will affect t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61F13/00D04H3/007D04H3/16D06C25/00A61L15/26A61L15/24A61L15/42D06M10/00
CPCA61F13/00987
Inventor 王晓广张会娟黄年华周晓洁张尚勇
Owner WUHAN TEXTILE UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com