Method for improving crease resistance and shrinkage resistance of Lyocell bamboo fiber

A bamboo fiber and performance technology, applied in fiber processing, plant fiber, textile material processing and other directions, can solve the problems of high shrinkage, easy wrinkling, dimensional instability, etc., to achieve low cost, reduce deformation, and improve wrinkle resistance. The effect of shrinking performance

Active Publication Date: 2014-01-15
SHANGHAI UNIV OF ENG SCI
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the shortcomings of Lyocell bamboo fiber and its blended products such as large shrinkage, unstable size, and easy wrinkling, and to develop a fast, easy, no additional catalyst, fast baking speed, and low release of formaldehyde. A functional processing technology that can greatly improve the anti-wrinkle and anti-shrinkage performance of Lyocell bamboo fiber, so that the treated Lyocell bamboo fiber and its blended products have good dimensional stability and non-ironing finishing effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving crease resistance and shrinkage resistance of Lyocell bamboo fiber
  • Method for improving crease resistance and shrinkage resistance of Lyocell bamboo fiber
  • Method for improving crease resistance and shrinkage resistance of Lyocell bamboo fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Changes in anti-wrinkle and anti-shrinkage properties of Lyocell bamboo fiber fabrics under different finishing conditions

[0025] Take the resin finishing agent A with a concentration of 50g / L, and the penetrating agent JFC at 2g / L, and double-dip and second-roll the fabric (the squeeze rate is 80%) with the finishing agent → drying (90°C, 6min) → baking (150°C, 3min ) → post-processing

[0026] Take concentration as 60g / L2D resin (dimethylol dihydroxyethylene urea) finishing agent, add 12g / L catalyst MgCl 2 , 2g / L penetrating agent JFC, two-dipping and two-rolling of the fabric (rolling liquid rate 80%) finishing agent → drying (80°C, 8min) → baking (150°C, 4min) → post-treatment

[0027] Determination of changes in anti-wrinkle and anti-shrinkage properties of Lyocell bamboo fiber fabrics.

[0028] Table 1 Effects of different finishing agents on the anti-wrinkle and anti-shrinkage properties of Lyocell bamboo fiber fabrics

[0029]

[0030] It can be seen fro...

Embodiment 2

[0032] Release of formaldehyde from Lyocell bamboo fiber fabrics treated with different finishing agents

[0033] Take the resin finishing agent A with a concentration of 50g / L, and the penetrating agent JFC at 2g / L, and double-dip and second-roll the fabric (the squeeze rate is 80%) with the finishing agent → drying (90°C, 6min) → baking (150°C, 3min ) → post-processing

[0034] Take concentration as 60g / L2D resin (dimethylol dihydroxyethylene urea) finishing agent, add 12g / L catalyst MgCl 2 , 2g / L penetrating agent JFC, two-dipping and two-rolling the fabric (rolling liquid rate 80%) finishing agent → drying (80°C, 8min) → baking (150°C, 4min-5min) → post-treatment

[0035] Determination of changes in anti-wrinkle and anti-shrinkage properties of Lyocell bamboo fiber fabrics.

[0036] Table 2 Effects of different baking temperatures on the anti-wrinkle and anti-shrinkage and formaldehyde release of Lyocell bamboo fiber fabrics

[0037]

Embodiment 3

[0039] Changes in anti-wrinkle and anti-shrinkage properties of Lyocell bamboo fiber fabrics after adding softener

[0040] Take the concentration of 50g / L resin finishing agent A, 15g / L silicone body fatty alcohol softener CFC, penetrating agent JFC 2g / L, two-dipping and two-rolling the fabric (rolling liquid rate 80%) finishing agent → drying (90 ℃ , 6min)→baking (150℃, 3min)→post-processing

[0041] Take concentration as 60g / L2D resin (dimethylol dihydroxyethylene urea) finishing agent, add 12g / L catalyst MgCl 2 , 15g / L silicone fatty alcohol softener CFC, 2g / L penetrating agent JFC, the fabric is dipped and rolled twice (80% of liquid rolling rate) finishing agent→drying (80°C, 8min)→baking (150°C , 4min) → post-processing

[0042] Determination of changes in anti-wrinkle and anti-shrinkage properties of Lyocell bamboo fiber fabrics.

[0043] Table 3 The effect of softener on the anti-wrinkle and anti-shrinkage performance of Lyocell bamboo fiber fabric

[0044]

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for improving crease resistance and shrinkage resistance of a Lyocell bamboo fiber. The method comprises the steps that Lyocell bamboo fiber fabric is subjected to two immersion and two rolling in a finishing liquid, and a drying treatment technology, a baking treatment technology and an aftertreatment technology are adopted sequentially, wherein the finishing liquid comprises the following components in parts by weight: 40-60 parts of finishing agent, 2-3 parts of penetrating agent, and 940-960 parts of water. Compared with the prior art, the method adopts a rapid finishing method, and is low in cost, high in baking speed and ultra-low in methanal release; no catalyst is required; and the crease resistance and the shrinkage resistance of the Lyocell bamboo fiber can be improved greatly. In addition, when a softening agent is added during finishing, the draping (smooth in hand feeling) and the air permeability of the fabric can be improved, and the softening agent has no significant influence on the strength of the fabric.

Description

technical field [0001] The invention relates to the application field of printing and dyeing finishing technology in textile materials, in particular to a method for improving the anti-wrinkle and anti-shrinkage performance of Lyocell bamboo fiber. Background technique [0002] Bamboo pulp fiber has a series of good properties and has been loved by consumers. But the bamboo pulp fiber that uses more at present all is the viscose fiber that replaces cotton pulp with bamboo pulp substantially. Because the viscose bamboo pulp fiber adopts the traditional viscose production process, while maintaining the excellent performance of viscose fiber, it also has the same disadvantages as ordinary viscose fiber, such as insufficient wet strength, hard water, easy deformation of the fabric, and environmental impact Larger etc. Shanghai Leo Fiber Enterprise Development Co., Ltd. has successfully developed Lyocell bamboo pulp fiber with bamboo pulp as raw material by using solvent spinni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/432D06M13/513D06M15/643D06B3/18D06M101/06
Inventor 王黎明黄熠佴智渊沈勇
Owner SHANGHAI UNIV OF ENG SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap