Regenerated cellulose fabric after-finishing agent and after-finishing process
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A regenerated cellulose and post-finishing technology, applied in fiber treatment, plant fiber, wear-resistant fiber, etc., can solve the problems of easy wrinkling, difficult recovery, and easy deformation of fabrics
Active Publication Date: 2020-11-03
HUAFANG +1
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
But the regenerated cellulose fabric also has the following disadvantages: because the moisture regain of the regenerated cellulose fabric is 12%-15%, the swelling degree in water reaches more than 50%, and the highest can reach 140%, so it is in the washing process. It is easy to absorb moisture and swell, and the fabric will feel hard; in terms of strength, the strength of this type of fabric will decrease by about 40% after wetting, and it is easy to deform and difficult to recover under a small load, and the elasticity is also poor. The fabric is easily damaged under severe washing conditions. Therefore, the fabric is easy to wrinkle and has poor abrasion resistance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0023] A finishing agent for regenerated cellulose fabrics, the finishing agent uses water as a solvent, including 20g / L of anti-shrinkage and anti-wrinkle processing resin, 20g / L of catalyst, 30 / L of fiber protection agent, 20 / L of water-based polyurethane and softener 30 / L, of which,
[0024] The resin is GL-45 resin;
[0025] Catalyst is F-M catalyst;
[0026] Fiber protection agent is PA-6 fiber protection agent;
[0027] The softener is HF-10R and silicone oil CGF softener with a weight ratio of 2:1.
Embodiment 2
[0029] A post-finishing process for regenerated cellulose fabrics. The post-finishing process is to soak the fabric in the post-finishing agent of Example 1 and roll the resin, and bake and cross-link the fibers in a non-expanded state after drying, wherein,
[0030] In the step of rolling resin, the surplus rate is 60%;
[0031] In the drying step, the drying temperature is 80°C;
[0032] In the baking step, the baking step is 175° C., and the baking time is 3 minutes.
Embodiment 3
[0034] A finishing agent for regenerated cellulose fabrics, the finishing agent uses water as a solvent, including 30g / L of anti-shrinkage and anti-wrinkle processing resin, 30g / L of catalyst, 40 / L of fiber protection agent, 30 / L of water-based polyurethane and softener 40 / L, of which,
[0035] The resin is GL-45 resin;
[0036] Catalyst is F-M catalyst;
[0037] Fiber protection agent is PA-6 fiber protection agent;
[0038] The softener is HF-10R and silicone oil CGF softener with a weight ratio of 7:1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the technical field of textiles, in particular to a regenerated cellulose fabric after-finishing agent and an after-finishing process. The after-finishing agent comprises shrink-proof and crease-resistant processing resin, a catalyst, a fiber protective agent, waterborne polyurethane and a softener. The after-finishing process comprises the following steps of soaking the fabric in the after-finishing agent, rolling the resin, drying, and baking and crosslinking in a fiber non-puffing state. By using the after-finishing agent and the after-finishing process, the regenerated cellulose fabric can be prevented from swelling and hardening in wet water, the wet strength is improved, the wearability of the regenerated cellulose fabric can be greatly improved, and a foundation is laid for wide application of the regenerated cellulose fabric.
Description
technical field [0001] The invention relates to the technical field of textiles, in particular to a finishing agent for regenerated cellulose fabrics and a finishing process. Background technique [0002] With the development of society and the continuous progress of science and technology, people's awareness of environmental protection has gradually increased, and the requirements for textiles have also shown a trend of natural, diversified and functional. Regenerated cellulose fiber has been favored by people because of its biodegradable characteristics. widespread favor. The emergence of regenerated cellulose fiber has also alleviated the current situation of scarcity of social resources, and has become an indispensable and important component of fabric composition, with broad development prospects. [0003] Regenerated cellulose fiber refers to fibers made of natural cellulose such as wood, cotton linters, hemp, bamboo, etc., including viscose fiber, modal fiber, cupro ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more