Metal surface color gradient treatment method and metal material prepared by same
A treatment method and color gradient technology, which can be applied to the device for coating liquid on the surface, special surface, pre-treatment surface, etc., can solve the problems such as the inability to realize the gradient effect, and achieve the effect of improving the decorative effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0039] Example 1
[0040] Place the aluminum metal workpiece in the alloy degreasing powder with a concentration of 50g / L, and perform degreasing and dewaxing treatment at a temperature of 60±10℃ for 4 minutes, and then in a NaOH solution with a concentration of 60g / L and a temperature of 70±10℃ Carry out alkaline etching treatment for 15 seconds, and then place it in a 40% nitric acid solution for neutralization treatment to fully clean the surface.
[0041] Then anodize the aluminum alloy workpiece in the anodizing solution; the concentration of sulfuric acid in the anodizing solution is 180g / L, the concentration of aluminum ion is 6g / L, the temperature of the anodizing solution is 19-20℃, and the DC voltage is set to 15V, oxidation time is 40 minutes.
[0042] Use automatic spraying equipment to make a single-color radial gradient sample, and spray water-soluble ink containing dye on the surface of the workpiece. The main component of the dye is the blue dye of model 419 produced...
Example Embodiment
[0044] Example 2
[0045] Place the aluminum metal workpiece in the alloy degreasing powder with a concentration of 50g / L, and perform degreasing and dewaxing treatment at a temperature of 60±10℃ for 4 minutes, and then in a NaOH solution with a concentration of 60g / L and a temperature of 70±10℃ Carry out alkali etching treatment for 15 seconds, and then place it in a 40% nitric acid solution for neutralization treatment to fully clean the surface.
[0046] Then anodize the aluminum alloy workpiece in the anodizing solution; the concentration of sulfuric acid in the anodizing solution is 160g / L, the concentration of aluminum ion is 5g / L, the temperature of the anodizing solution is 19-20℃, and the DC voltage is set to 13V, oxidation time is 35 minutes.
[0047] Use automatic spraying equipment to make single-color radial gradient samples, and spray water-soluble ink containing dyes on the surface of the workpiece. The main component of the dye is the red dye of model 102 produced b...
Example Embodiment
[0049] Example 3
[0050] Place the aluminum metal workpiece in the alloy degreasing powder with a concentration of 50g / L, and perform degreasing and dewaxing treatment at a temperature of 60±10℃ for 4 minutes, and then in a NaOH solution with a concentration of 60g / L and a temperature of 70±10℃ Carry out alkaline etching treatment for 15 seconds, and then place it in a 40% nitric acid solution for neutralization treatment to fully clean the surface.
[0051] Then anodize the aluminum alloy workpiece in the anodizing solution; the sulfuric acid concentration in the anodizing solution is 200g / L, the aluminum ion concentration is 10g / L, the temperature of the anodizing solution is 19-20℃, and the DC voltage is set to 16V, oxidation time is 30 minutes.
[0052] Take out the work piece, wash it thoroughly, and then dry it in an oven at a temperature of 85°C for 6 minutes.
[0053] Use automatic spraying equipment to make single-color radial gradient samples, and spray water-soluble ink...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap