Method for improving ash content of paper-making process reconstituted tobaccos

A technology of reconstituted tobacco leaves and papermaking method, which is applied in the field of preparation of reconstituted tobacco leaves by papermaking method, can solve problems such as no systematic research, and achieve remarkable effects, reasonable methods, and simple operations

Inactive Publication Date: 2014-03-26
HUBEI XINYE TOBACCO SLICE DEV
View PDF11 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above invention patents have improved or optimized the cell wall filling process and retention technology of the filler, they often discuss and study a single influencing factor without systematic research, and often need to add a small amount of water-soluble polymer. Polymers (the use of high molecular weight polymers in reconstituted tobacco leaves is strictly regulated)
[0007] At present, CaCO has not been adopted at home and abroad. 3 Related reports on increasing the ash content of reconstituted tobacco leaves by papermaking process by filling the cell lumen of tobacco pulp fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] After the tobacco raw material is extracted, the solid-liquid separation is carried out, and the liquid part of the tobacco is refined, concentrated and added to make a coating liquid for future use.

[0020] 1) The solid part of the tobacco is subjected to beating treatment, and the beating degree is controlled at 30±2°SR to obtain tobacco pulp fibers, and CaCO is added to the tobacco pulp fibers 3 , the CaCO 3 The pits of tobacco pulp fibers are filled in the cell lumen of tobacco pulp fibers, among which, CaCO 3 The particle size is 300 mesh, the mixing time is 10min, the mechanical stirring speed is 500rpm, the processing temperature is 20℃, the tobacco pulp fiber and CaCO 3 The weight ratio is 7:1;

[0021] 2) Mix the tobacco pulp fiber filled with the above-mentioned cell cavity with the added fiber pulp according to the weight ratio of 4:1, and the beating degree of the added added fiber pulp is 44±2°SR, and then sent to the paper machine for paper forming , p...

Embodiment 2

[0025] After the tobacco raw material is extracted, the solid-liquid separation is carried out, and the liquid part of the tobacco is refined, concentrated and added to make a coating liquid for future use.

[0026] 1) The solid part of the tobacco is subjected to beating treatment, and the beating degree is controlled at 30±2°SR to obtain tobacco pulp fibers, and CaCO is added to the tobacco pulp fibers 3 , the CaCO 3 The pits of tobacco pulp fibers are filled in the cell lumen of tobacco pulp fibers, among which, CaCO 3 The particle size is 1500 mesh, the mixing time is 30min, the mechanical stirring speed is 3000rpm, the treatment temperature is 60℃, the tobacco pulp fiber and CaCO 3 The weight ratio is 7:1;

[0027] 2) Mix the above cell lumen filled tobacco pulp fibers with the added fiber pulp at a weight ratio of 4:1, the degree of beating of the added added fiber pulp is 44±2°SR, and the needles and The ratio of the broad leaves is 3:1, and then sent to the paper ma...

Embodiment 3

[0031] After the tobacco raw material is extracted, the solid-liquid separation is carried out, and the liquid part of the tobacco is refined, concentrated and added to make a coating liquid for future use.

[0032] 1) The solid part of the tobacco is subjected to beating treatment, and the beating degree is controlled at 30±2°SR to obtain tobacco pulp fibers, and CaCO is added to the tobacco pulp fibers 3 , the CaCO 3 The pits of tobacco pulp fibers are filled in the cell lumen of tobacco pulp fibers, among which, CaCO 3 The particle size is 1500 mesh, the mixing time is 30min, the mechanical stirring speed is 3000rpm, the treatment temperature is 60℃, the tobacco pulp fiber and CaCO 3 The weight ratio is 7:1;

[0033] 2) Mix the tobacco pulp fiber filled with the above cell lumen with the added fiber pulp at a weight ratio of 4:1, and the beating degree of the added added fiber pulp is 44±2°SR, and then sent to the paper machine for paper forming , prepared into reconstit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for improving the ash content of paper-making process reconstituted tobaccos. The method includes the steps that after tobacco raw materials are extracted, solid-liquid separation is carried out, tobacco liquid is partially refined, concentrated and charged and then is manufactured into coating liquid, pulping treatment is partially conducted on the tobacco solid part, so that tobacco slurry fibers are obtained, CaCO3 is added into the tobacco slurry fibers, and the CaCO3 is filled into cell cavities of the tobacco slurry fibers through pits of the tobacco slurry fibers; afterwards, the tobacco slurry fibers and additional fiber slurry are mixed according to the weight ratio of 4 to 1, and then paper manufacturing with pulp is carried out to manufacture reconstituted tobacco sheets; the coating liquid is made to coat the reconstituted tobacco sheets, so that the paper-making process reconstituted tobaccos are manufactured. According to the method, the technology that the CaCO3 is filled into the cell cavities of the tobacco slurry fibers is applied to the preparation technology of the paper-making process reconstituted tobaccos, any chemical agent such as a high-molecular polymer is not added, and the purposes that the ash content is improved and meanwhile the strength performance of the paper-making process reconstituted tobacco sheets is improved can be achieved.

Description

technical field [0001] The invention relates to the preparation of reconstituted tobacco leaves by papermaking method, in particular to a method for increasing the ash content of reconstituted tobacco leaves by papermaking method. Background technique [0002] The production of reconstituted tobacco leaves by papermaking means that the tobacco raw materials such as tobacco stems, tobacco dust and some low-grade tobacco leaves produced in the process of threshing and redrying and cigarette production are first extracted with a solvent (usually water), and then separated from solid and liquid. Part of it is processed into a substrate (base paper) according to the papermaking method, and the liquid part is refined and purified, concentrated and flavored to prepare a coating liquid, and then the coating liquid is applied to the substrate by double-roller coating, etc., and heated by hot air. After drying and slicing, it is finally made into a sheet-like substance close to natura...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A24B3/14
Inventor 孙德平王亮姚元军王凤兰刘志昌王磊
Owner HUBEI XINYE TOBACCO SLICE DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com