Positive lead paste of storage battery and preparation method thereof

A battery and lead paste technology, which is applied to battery electrodes, circuits, electrical components, etc., can solve the problems of poor performance of battery high-current discharge and low-current deep discharge, low comprehensive performance of battery, and insufficient material analysis, so as to reduce the extreme The effect of board scrap rate, increase of deep discharge time, and extension of deep discharge time

Active Publication Date: 2014-03-26
HENAN CHAOWEI POWER SUPPLY
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] For the raw material composition of lead-acid battery lead paste, various materials have multiple structures. Many manufacturers only pay attention to one of the structures or do not mix well the different structures of the materials. The material analysis is not delicate enough, resulting in the overall performance of the battery. Not high, there are short boards, such as: lead paste is easy to fill but the strength of the plate is poor; the battery capacity is high but the life is short, the battery discharges well with high current but poor deep discharge performance at low current, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The battery positive lead paste of this embodiment contains the following raw materials in parts by weight: 500 parts of high oxidation degree lead powder, 500 parts of low oxidation degree lead powder, 25 parts of red lead, 25 parts of yellow lead, 10 parts of tetrabasic lead sulfate, meteorological two 2 parts of silicon oxide, 2 parts of nano-silica, 0.5 part of 1-2mm polyester staple fiber, 0.5 part of 3-5mm polyester staple fiber, 1.5g / cm 3 50 parts of sulfuric acid solution, 1.2g / cm 3 50 parts of sulfuric acid solution.

[0032] The oxidation degree of the high oxidation degree lead powder is 80-85%, and the apparent density is 1.25g / cm 3 ; The oxidation degree of the low oxidation degree lead powder is 65-70%, and the apparent density is 1.5g / cm 3 ; The specific surface area of ​​the meteorological silica is 150~250m 2 / g, the specific surface area of ​​the nano-silica is 600-800m 2 / g; the apparent density of the resulting lead paste is 4.4g / cm 3 .

Embodiment 2

[0034] The battery positive lead paste of this embodiment contains the following raw materials in parts by weight: 490 parts of high oxidation degree lead powder, 490 parts of low oxidation degree lead powder, 22 parts of red lead, 22 parts of yellow lead, 8 parts of tetrabasic lead sulfate, meteorological two 1 part of silicon oxide, 1 part of nano-silica, 0.3 part of 1-2mm polyester staple fiber, 0.3 part of 3-5mm polyester staple fiber, 1.4g / cm 3 45 parts of sulfuric acid solution, 1.1g / cm 3 45 parts of sulfuric acid solution.

[0035] The oxidation degree of the high oxidation degree lead powder is 80-85%, and the apparent density is 1.25g / cm 3 ; The oxidation degree of the low oxidation degree lead powder is 65~70%, and the apparent density is 1.45g / cm 3 ; The specific surface area of ​​the meteorological silica is 150~250m 2 / g, the specific surface area of ​​the nano-silica is 600-800m 2 / g; the apparent density of the resulting lead paste is 4.5g / cm 3 .

Embodiment 3

[0037] The battery positive lead paste of this embodiment contains the following raw materials in parts by weight: 510 parts of high oxidation degree lead powder, 510 parts of low oxidation degree lead powder, 28 parts of red lead, 28 parts of yellow lead, 12 parts of tetrabasic lead sulfate, meteorological two 3 parts of silicon oxide, 3 parts of nano-silica, 0.7 parts of 1-2mm polyester staple fiber, 0.7 part of 3-5mm polyester staple fiber, 1.6g / cm 3 55 parts of sulfuric acid solution, 1.3g / cm 3 55 parts of sulfuric acid solution.

[0038] The oxidation degree of the high oxidation degree lead powder is 80-85%, and the apparent density is 1.3g / cm 3 ; The oxidation degree of the low oxidation degree lead powder is 65-70%, and the apparent density is 1.5g / cm3 ; The specific surface area of ​​the meteorological silica is 150~250m 2 / g, the specific surface area of ​​the nano-silica is 600-800m 2 / g; the apparent density of the resulting lead paste is 4.3g / cm 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Apparent densityaaaaaaaaaa
Apparent densityaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of storage batteries, and particularly relates to positive lead paste of a storage battery and a preparation method thereof. The positive lead paste comprises following raw materials: 490-510 parts of high-oxidizability lead powder, 490-510 parts of low-oxidizability lead powder, 22-28 parts of red lead, 22-28 parts of yellow lead, 8-12 parts of tetrabasic lead sulfate, 1-3 parts of fumed silica, 1-3 parts of nano-silica, 0.3-0.7 part of terylene staple fiber having a length of 1-2 mm, 0.3-0.7 part of terylene staple fiber having a length of 3-5 mm, 45-55 parts of a sulfuric acid solution having a concentration of 1.4-1.6 g / cm<3> and 45-55 parts of a sulfuric acid solution having a concentration of 1.1-1.3 g / cm<3>. The lead paste is capable of facilitating preparation, filling and coating processes, enhancing the strength of polar plate, reducing the rejection rate of the polar plate, improving the battery capacity, increasing the deep discharging time, prolonging the service lifetime of the battery and improving the comprehensive performances of the battery. According to the lead paste and the preparation method thereof, the method and the design are reasonable, operation is simple, and the production efficiency is largely increased.

Description

technical field [0001] The invention belongs to the technical field of accumulators, and in particular relates to a positive lead paste for lead-acid accumulators and a preparation method thereof. Background technique [0002] For the raw material composition of lead-acid battery lead paste, various materials have multiple structures. Many manufacturers only pay attention to one of the structures or do not mix well the different structures of the materials. The material analysis is not delicate enough, resulting in the overall performance of the battery. Not high, there are shortcomings, such as: lead paste is easy to fill but the strength of the plate is poor; the battery capacity is high but the life is short, the battery discharges well with high current but poor deep discharge performance at low current, etc. Contents of the invention [0003] In view of the above problems, the present invention provides a positive lead paste for lead-acid batteries and a preparation m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/57
CPCH01M4/57H01M4/62Y02E60/10
Inventor 李松林柴成雷
Owner HENAN CHAOWEI POWER SUPPLY