An inorganic thermal insulation and slurry technology, applied in the field of construction slurry, can solve problems such as leakage, affecting project quality and normal use, wall cracking, etc., and achieve the effects of remarkable effect, remarkable fire prevention, thermal insulation and energy saving, and simple preparation method.

Inactive Publication Date: 2014-04-23
QINGDAO WUWEI THERMAL INSULATION MATERIAL
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The wall materials used in construction projects generally have serious wall cracking and leakage problems, which seriously affect the quality of the project and normal use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 40 kg of slag cotton, 15 kg of white cotton, 12 kg of aluminum silicate fiber, 8 kg of aluminum powder, 20 kg of sepiolite, 15 kg of floating beads, 15 kg of gypsum powder, 5 kg of zinc borate, and 25 kg of sawdust.

[0017] After the above-mentioned raw materials are dried and pretreated, they are put into a mixer and stirred for 15-25 minutes. After being stirred evenly, they are packaged and put into storage, and the aluminum silicate fibers are packaged separately.

Embodiment 2

[0019] 30 kg of slag cotton, 12 kg of white cotton, 12 kg of aluminum silicate fiber, 6 kg of aluminum powder, 15 kg of sepiolite, 15 kg of floating beads, 10 kg of gypsum powder, 5 kg of zinc borate, and 20 kg of sawdust.

[0020] After the above-mentioned raw materials are dried and pretreated, they are put into a mixer and stirred for 15-25 minutes. After being stirred evenly, they are packaged and put into storage, and the aluminum silicate fibers are packaged separately.

Embodiment 3

[0022] 40 kg of slag cotton, 10 kg of white cotton, 8 kg of aluminum silicate fiber, 8 kg of aluminum powder, 20 kg of sepiolite, 15 kg of floating beads, 10 kg of gypsum powder, 3 kg of zinc borate, and 15 kg of sawdust.

[0023] After the above-mentioned raw materials are dried and pretreated, they are put into a mixer and stirred for 15-25 minutes. After being stirred evenly, they are packaged and put into storage, and the aluminum silicate fibers are packaged separately.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses heat-insulating inorganic heat-preservation slurry and a preparation method thereof; the slurry is characterized by comprising the following raw materials by weight: 25-40 parts of mineral cotton, 5-15 parts of white cotton, 5-12 parts of alumina silicate fibers, 5-8 parts of aluminium powder, 10-20 parts of meerschaum, 5-15 parts of floating beads, 5-15 parts of gypsum powder, 2-5 parts of fire retardants, and 15-25 parts of sawdust powder. The heat-insulating inorganic heat-preservation slurry provided by the invention is applicable to heat insulation, heat preservation and energy saving of various building wall surfaces.

Description

technical field [0001] The invention relates to the field of construction slurry, in particular to a thermal insulation inorganic thermal insulation slurry and a preparation method thereof. Background technique [0002] Building energy consumption in a broad sense includes the energy consumption caused by the whole process of building material production, building construction, use and maintenance. Energy consumption in a narrow sense refers to the energy consumption of buildings. Generally speaking, building energy efficiency refers to reducing the energy consumption of buildings. Aiming at the problem of large building energy consumption in our country, a lot of research has been carried out, and many new high-efficiency thermal insulation materials have been produced, which can be roughly divided into two types: organic thermal insulation materials and inorganic thermal insulation materials. [0003] Building functional mortar, as a new type of green building material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B14/38
Inventor 李本明
Owner QINGDAO WUWEI THERMAL INSULATION MATERIAL