Aliphatic chain ester metal complex modified material for macromolecule injection molding magnetic material

A technology for injection molding magnetic materials and metal complexes, which is applied in the field of material science and can solve problems such as reduced dispersion uniformity, phase dispersion of magnetic powder and binder, and difficulty in forming magnetic materials.

Inactive Publication Date: 2014-04-23
上海葆硕磁性材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The higher the magnetic powder content, the better the magnetic properties, but too high magnetic powder filling will increase the viscosity of the magnetic powder and binder mixture, the fluidity will be poor, and the dispersion uniformity will be reduced, making it difficult to process the mixture during injection molding. Difficulty forming magnetic materials
At present, most of the solutions use the method of adding modified materials to solve the problem of homogeneous dispersion of magnetic powder and binder. For example, the Chinese invention patent CN1645526A discloses a formula for injection molding ferrite permanent magnet materials, using organic external lubricants and Inorganic internal lubricants cooperate with each other to improve the fluidity of the pellets. Although this formula solves the problem of using nylon 12 as a binder to a certain extent, the lubricant used is conventional and has a good compatibility with polymers. Capacitive materials, but there is no effective interaction with metal magnetic powder, and the effect on improving the uniform dispersion of different components in the product is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: Starting from the ferrocene raw material, ferrocene formic acid was synthesized according to the scheme step 1, and the reaction temperature was 50 degrees Celsius. The obtained ferrocenecarboxylic acid is blended with n=8 fatty alcohol in a ratio of 1:1 according to the scheme step 2, and the catalyst ZnO (mass fraction 1%) is added, and the reaction temperature is 90 degrees Celsius, and the reaction generates ferrocenecarboxylic acid fatty alcohol ester in the form of liquid state. The obtained ferrocenecarboxylic acid fatty alcohol ester is the fatty chain ester metal complex modification auxiliary agent.

Embodiment 2

[0013] Embodiment 2: Starting from the ferrocene raw material, ferrocene formic acid was synthesized according to the scheme step 1, and the reaction temperature was 70 degrees Celsius. The obtained ferrocenecarboxylic acid is blended with n=36 fatty alcohol in a ratio of 1:1 according to the scheme step 2, and the catalyst ZnO (mass fraction 3%) is added, and the reaction temperature is 110 degrees Celsius, and the reaction generates ferrocenecarboxylic acid fatty alcohol ester in the form of solid state. The obtained ferrocenecarboxylic acid fatty alcohol ester is the fatty chain ester metal complex modified solid material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an aliphatic chain ester metal complex modified material for a macromolecule injection molding magnetic material, which aims at solving the problem of homodisperse of mixture of magnetic powder and binder in production of injection molding magnetic material. The aliphatic chain ester which is compatible to macromolecule is grafted on ferrocene so as to prepare the aliphatic chain ester metal complex modified material. Due to the added modified material, macromolecule and metal magnetic powder are mixed and are compatible more effectively, so that the dispersing evenness is improved, and the processability and usability of the product are further improved.

Description

technical field [0001] The invention belongs to the field of material science, and in particular relates to an aliphatic chain ester metal complex modified material for polymer injection molding magnetic materials. Background technique [0002] Injection magnetic material is a kind of magnetic material widely used at present. Injection magnetic material is a kind of bonded magnetic material, which is characterized in that polymer material (such as polymer, PPS, etc.) is used as binder and magnetic powder (such as ferrite magnetic powder, NdFeB magnetic powder) is mixed, Compared with sintered magnetic materials, the injection method in the polymer processing technology is used for production molding. Compared with sintered magnetic materials, the molding process of bonded magnetic materials is simple, and it is easy to manufacture magnetic material products with high dimensional accuracy and no need for secondary processing. The production efficiency is high and the cost is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K5/101C07F17/02
Inventor 耿保山刘淑英黄然
Owner 上海葆硕磁性材料有限公司