Preparation method of bone charcoal

A technology of bone charcoal and bone charcoal, applied in the field of bone charcoal manufacturing, can solve the problems of high acquisition cost, complicated processes of animal bone manufacturing bone charcoal, etc., and achieve the effect of low cost and low pollution

Inactive Publication Date: 2014-04-30
梅河口市红梅骨炭有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Natural bone charcoal is made from animal bones by high-temperature calcination. The process of making bone charcoal from animal bones is complicated and the purchase cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] There are many bone gelatin factories in China, and their by-products are mainly calcium hydrogen phosphate made from bone. This product has the same element composition as the natural bone charcoal fired from animal bones, but the ratio is different. During the manufacturing process of bone gelatin, the loss of calcium element is caused, and the lost calcium is supplemented to make it close to natural bone charcoal.

[0008] The process of making bone charcoal by using calcium hydrogen phosphate made from bone is: batching----mixing----molding----calcination. Specifically: (1) add bone calcium hydrogen phosphate and light calcium carbonate or heavy calcium carbonate at a weight ratio of 100: (10-40) (weight percentage); (2) mix evenly. (3) Add carboxymethyl cellulose (5% solution) accounting for 5-10% of the total amount, and continue to mix evenly. (4) The mixed material is pressurized into a certain shape by a molding machine; (5) After drying, it is calcined in a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for preparing bone charcoal. The bone charcoal is prepared from bone-made calcium hydrogen phosphate which is a by-product in the preparation of bone gelatin. The method comprises the steps of material portioning, mixing, molding and calcining; specifically, the method comprises the following steps: 1, adding bone-made calcium hydrogen phosphate and light calcium carbonate or heavy calcium carbonate according to the weight ratio being 100:(10-40) (wt%); 2, evenly mixing; 3, adding carboxymethyl cellulose (5% solution) accounting for 5% to 10% of the total weight and evenly mixing; 4, pressing the mixed material into a certain shape by a molding machine; and 5, drying and then calcining in a kiln for no less than 30 minutes at 1200 DEG C to 1400 DEG C; and cooling. Compared with the firing of animal bones, waste gases released during the calcining process of the method provided by the invention are less, so that the pollution is reduced; and the method provided by the invention is low in cost. In the current industrial experiment, the natural bone charcoal taking the replacement quantity of 30% to 80% according to different processes is used for manufacturing ceramic products.

Description

technical field [0001] The invention relates to the field of bone char production. Background technique [0002] At present, the price of bone charcoal has been at a high level, which directly pushes up the raw material cost of bone china. Natural bone charcoal is made from animal bones by high-temperature calcination. The process of making bone charcoal from animal bones is complicated and the purchase cost is high. In recent years, the price of animal bones is still rising. The ceramic industry is already making a small profit, and the increase in costs has further reduced its profit margins. People long for a new raw material to replace animal bone to make bone char. Contents of the invention [0003] In order to reduce the cost of bone charcoal manufacture, the present invention provides a method for producing bone charcoal as follows: the bone charcoal is prepared by using bone calcium hydrogen phosphate, a by-product of producing bone gelatin. [0004] Bone charco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/447
Inventor 吴云岭苗术佶
Owner 梅河口市红梅骨炭有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products