Pearlescent ink, and preparation method and printing method thereof

A pearlescent ink and pearlescent powder technology, applied in printing, ink, printing device, etc., can solve problems such as difficulty, pearlescent ink can not meet the requirements of gravure printing, etc., and achieve the effect of preventing floating, stable pearlescent color and uniform surface effect.

Active Publication Date: 2014-05-07
惠州市立美特环保油墨有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In particular, the existing screen printing effect needs to be realized by gravure printing, which is more difficult
[0003] That is, the existing pearlescent ink cannot meet the requirements of gravure printing on light-colored substrates, especially the requirement that the effect of screen printing should be realized by gravure printing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pearlescent ink, and preparation method and printing method thereof
  • Pearlescent ink, and preparation method and printing method thereof
  • Pearlescent ink, and preparation method and printing method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0063] Correspondingly, the present invention also discloses a preparation method of pearlescent ink, comprising: pre-mixing and soaking pearlescent powder I, pearlescent powder II, pearlescent powder III and n-propyl ester; first adding nitrocellulose resin liquid, Wetting and dispersing agent, stirring at low speed for 5-30 minutes; then under low-speed stirring, add the pre-soaked pearl powder Ⅰ, pearl powder Ⅱ and pearl powder Ⅲ in sequence, and stir at 1000-1500 rpm for 5-20 minutes; then add Stir the anti-sedimentation agent evenly; finally filter with a filter screen to obtain the finished pearlescent ink of the present invention.

[0064] Preferably, the pre-mixed soaking time of the pearl powder I, pearl powder II, pearl powder III and n-propyl ester is 1-5 hours; the stirring time of the nitrocellulose resin liquid and the wetting and dispersing agent is 15 minutes; the The stirring time of pearl powder I, pearl powder II and pearl powder III is 10 minutes.

[0065]...

Embodiment 1

[0084] 1. Raw materials: 25 parts of nitrocellulose resin liquid, 25 parts of pearl powder I (with a particle size of 700 mesh to 1500 mesh), 12 parts of pearl powder II (with a particle size of 500 mesh to 1000 mesh), 12 parts of pearl powder III (with a particle size of 300 mesh to 700 mesh) 8 parts, 2 parts of wetting and dispersing agent, 2 parts of anti-sedimentation agent, 26 parts of n-propyl ester.

[0085] 2. Preparation method: pre-mix and soak pearl powder Ⅰ, pearl powder Ⅱ, pearl powder Ⅲ and n-propyl ester for 1 hour; add nitrocellulose resin solution, wetting and dispersing agent in turn in ink production, and stir at low speed for 15 minutes; then Under low-speed stirring, add pre-soaked pearl powder Ⅰ, pearl powder Ⅱ and pearl powder Ⅲ in sequence, and stir at 1000-1500 rpm for 10 minutes; then add anti-settling agent and stir well; finally filter with a 200-mesh filter to obtain The pearlescent ink finished product of the present invention.

Embodiment 2

[0087] 1. Raw materials: 45 parts of nitrocellulose resin liquid, 14 parts of pearl powder I (with a particle size of 800 mesh to 1400 mesh), 8 parts of pearl powder II (with a particle size of 500 mesh to 900 mesh), 8 parts of pearl powder III (with a particle size of 400 mesh to 700 mesh) 7 parts, wetting and dispersing agent 1.2 parts, anti-sedimentation agent 0.4 parts, n-propyl ester 24.4 parts.

[0088] 2. Preparation method: pre-mix and soak pearl powder Ⅰ, pearl powder Ⅱ, pearl powder Ⅲ and n-propyl ester for 2 hours; add nitrocellulose resin solution, wetting and dispersing agent in sequence in the production of ink, and stir for 15 minutes at low speed; then Under low-speed stirring, add pre-soaked pearl powder Ⅰ, pearl powder Ⅱ and pearl powder Ⅲ in sequence, and stir at 1000-1500 rpm for 10 minutes; then add anti-settling agent and stir well; finally filter with a 200-mesh filter to obtain The pearlescent ink finished product of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses a pearlescent ink which is especially used for intaglio printing of light-color substrates. The pearlescent ink is mainly prepared from the following raw materials in parts by weight: 25-65 parts of nitrocellulose resin liquid, 8-25 parts of pearlescent powder I, 3-12 parts of pearlescent powder II, 2-8 parts of pearlescent powder III, 0.1-3 parts of wetting and dispersing agent, 0.1-3 parts of anti-settling agent and 5-40 parts of n-propyl ester. Correspondingly, the invention also discloses a preparation method of the pearlescent ink and a printing method of the pearlescent ink. The pearlescent ink can satisfy the requirements for intaglio printing on light-color substrates, and has favorable printing effect.

Description

technical field [0001] The invention relates to the field of inks, in particular to a pearlescent ink, a preparation method and a printing method thereof. Background technique [0002] Pearlescent pigments are widely used in the printing of various packaging materials due to their soft and shimmering effects, but due to their light color and poor hiding power, it is difficult to print solidly on light-colored substrates (the so-called surface printing effect is "faint". The phenomenon). Therefore, it is necessary to print a thick and full pearlescent effect on light-colored substrates, which is usually achieved by thicker roller coating or screen printing, while thinner gravure printing is rarely used. In particular, the existing screen printing effect needs to be realized by gravure printing, which is more difficult. [0003] That is, the existing pearlescent ink cannot meet the requirements of gravure printing on light-colored substrates, especially the requirement that ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/037C09D11/14B41M1/10
Inventor 朱常春张传海肖又平
Owner 惠州市立美特环保油墨有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap