Production method of transparent sound-proof film

A technology of soundproof film and production method, which is applied in the direction of film/sheet adhesive, adhesive, graft polymer adhesive, etc., can solve the problems of less attention, achieve easy operation, improve selectivity, and produce The effect of concise and clear process

Inactive Publication Date: 2014-05-07
TIANJIN SUNRAY PLASTIC PROD
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing laminated glass (glass film) generally focuses on the aesthetic effect of decoration, and invests in research and development in terms of color, pattern, etc., but pays less attention to other performance indicators, such as sound insulation performance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The production method of the transparent soundproof film of the present invention comprises the following steps, (1) the step of copolymerizing polystyrene and butyl acrylate into styrene-acrylic resin, the glass transition temperature of the formed styrene-acrylic resin is 15°C, and the damping coefficient is 0.45; (2) The step of coating the styrene-acrylic resin into a film with a hot-melt coating machine, and the thickness of the film is 0.3mm; (3) The step of laminating ordinary glass films on both sides of the styrene-acrylic resin film by thermal lamination.

[0012] Among them, the polymerization process in step (1) is selected as a suspension polymerization method; both sides of the styrene-acrylic resin film obtained in step (2) are protected by release paper, and the release paper is removed before the thermal composite processing in step (3); The common glass film described in step (3) is EVA glass film.

Embodiment 2

[0014] The production method of the transparent soundproof film of the present invention comprises the following steps, (1) the step of copolymerizing polystyrene and butyl acrylate into styrene-acrylic resin, the glass transition temperature of the formed styrene-acrylic resin is 25°C, and the damping coefficient is 0.42; (2) The step of coating the styrene-acrylic resin into a film with a hot-melt coating machine, and the thickness of the film is 0.6mm; (3) The step of laminating ordinary glass films on both sides of the styrene-acrylic resin film by thermal lamination.

[0015] Among them, the polymerization process in step (1) is selected as a solution polymerization method; both sides of the styrene-acrylic resin film obtained in step (2) are protected by release paper, and the release paper is removed before the thermal composite processing in step (3); The common glass film described in step (3) can be EVA glass film.

Embodiment 3

[0017] The production method of the transparent soundproof film of the present invention comprises the following steps, (1) the step of copolymerizing polystyrene and butyl acrylate into styrene-acrylic resin, the glass transition temperature of the formed styrene-acrylic resin is 25°C, and the damping coefficient is 0.56; (2) The step of coating the styrene-acrylic resin into a film with a hot-melt coating machine, and the thickness of the film is 0.4mm; (3) The step of laminating ordinary glass films on both sides of the styrene-acrylic resin film by thermal lamination.

[0018] Among them, the polymerization process in step (1) is selected as a solution polymerization method; both sides of the styrene-acrylic resin film obtained in step (2) are protected by release paper, and the release paper is removed before the thermal composite processing in step (3); The common glass film described in step (3) is PVB glass film.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of glass film production, and particularly relates to a production method of a transparent sound-proof film. The production method comprises the following steps: (1) copolymerizing polystyrene and butyl acrylate so as to synthesize styrene-acrylic resin, wherein the glass transition temperature of the formed styrene-acrylic resin is 15-30 DEG C, and the damping coefficient of the formed styrene-acrylic resin is greater than 0.3; (2) adopting a hot-melting coating machine for coating so as to form a thin film with the thickness of 0.05-1.0mm; and (3) compounding common glass films at the two sides of the styrene-acrylic resin thin film in a thermal compounding manner. The production method of the glass film with excellent sound-proof performance index, provided by the invention, has the advantages that the styrene-acrylic resin thin film with a large damping coefficient is compounded between two layers of common glass films, so that the glass film formed in the end has soundproof property, the selectivity of laminated glass production is improved, and the whole production process is concise, clear and easy to operate.

Description

technical field [0001] The invention belongs to the technical field of glass film production, and in particular relates to a production method of a transparent sound-insulating film. Background technique [0002] In the field of architectural decoration, laminated glass has been more and more widely used due to its excellent characteristics such as beauty and firmness. Laminated glass includes a glass film layer in the center and glass on both sides. The existing laminated glass (glass film) generally focuses on the aesthetic effect of decoration, and invests in research and development of color, pattern, etc., but pays less attention to other performance indicators, such as sound insulation performance. As people pay more attention to the comprehensive performance of laminated glass products, the above-mentioned sound insulation performance indicators have gradually attracted attention. Contents of the invention [0003] The invention provides a production method of a tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/00C09J151/06C08F257/02
Inventor 李国勇
Owner TIANJIN SUNRAY PLASTIC PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap