A kind of reduced blow molding packaging barrel and its preparation method

A technology of packaging barrels and weight reduction, applied in the field of blow molding plastics, can solve problems such as cost reduction, and achieve the effects of reducing materials, enhancing anti-oxidation effect, and high output power

Inactive Publication Date: 2017-01-04
JINBIN DONGBAO TIANJIN TECH DEV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Demand always drives technological progress, and technological progress continues to create miracles of high quality and low price. Many materials that used to be expensive have now reduced their cost on a large scale due to large-scale production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The present invention provides a reduced-weight blow-molded packaging barrel and a preparation method thereof, including the following process steps:

[0029] (1) Weigh 100 parts of high-density polyethylene in a mixer, first add 1.5 parts of epoxy linseed oil, 0.1 part of 2-hydroxy-4-n-octoxybenzophenone, 1 part of stearin Calcium acid, 2 parts of nitrile powder rubber, adjust the speed of the mixer to 5m / s and temperature to 30℃, mix and stir for 10 minutes, then add 0.09 parts of antioxidant 1010 and 0.08 parts of dilauryl thiodipropionate , Adjust the speed of the mixer to 4m / s and the temperature to 70°C, mix and stir for 10 minutes, and mix into a mixture;

[0030] (2) Put the mixture in the hopper of the conical twin-screw extruder. The barrel has a seven-segment barrel structure. The seventh barrel is a die. The barrel temperature is set to: 120°C in the first zone and 128 in the second zone. ℃, 130℃ for three zones, 130℃ for four zones, 125℃ for five zones, 120℃ fo...

Embodiment 2

[0036] The present invention provides a reduced-weight blow-molded packaging barrel and a preparation method thereof, including the following process steps:

[0037] (1) Weigh 100 parts of high-density polyethylene in a blender, first add 2.5 parts of epoxy linseed oil, 0.3 parts of 2-hydroxy-4-n-octoxybenzophenone, and 0.5 parts of stearin Calcium acid, 0.5 parts of nitrile powder rubber, adjust the speed of the mixer to 6m / s and the temperature to 45℃, mix and stir for 10 minutes, then add 0.06 parts of antioxidant 1010 and 0.1 parts of dilauryl thiodipropionate , Adjust the speed of the mixer to 5m / s and the temperature to 50°C, mix and stir for 10 minutes, and mix into a mixture;

[0038] (2) Put the mixture in the hopper of the conical twin-screw extruder. The barrel has a seven-section barrel structure. The seventh section barrel is the die. The barrel temperature is set to: 125℃ in the first zone and 135 in the second zone. ℃, three-zone 135℃, four-zone 135℃, five-zone 130℃...

Embodiment 3

[0044] The present invention provides a reduced-weight blow-molded packaging barrel and a preparation method thereof, including the following process steps:

[0045] (1) Weigh 100 parts of high-density polyethylene in a mixer, first add 2 parts of epoxy linseed oil, 0.2 parts of 2-hydroxy-4-n-octoxy benzophenone, 0.8 parts of stearin Calcium acid, 1 part of nitrile powder rubber, adjust the mixer speed to 5m / s and temperature to 40℃, mix and stir for 10 minutes, then add 0.08 parts of antioxidant 1010 and 0.09 parts of dilauryl thiodipropionate , Adjust the speed of the mixer to 5m / s and the temperature to 60°C, mix and stir for 10 minutes, and mix into a mixture;

[0046] (2) Place the mixture in the hopper of the conical twin-screw extruder. The barrel has a seven-segment barrel structure, and the seventh barrel is a die. The barrel temperature is set to: 123℃ in the first zone and 130 in the second zone. ℃, three zone 134℃, four zone 134℃, five zone 128℃, six zone 122℃, die hea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a reducing blow molding packing barrel and a preparation method thereof. The reducing blow molding packing barrel is prepared by raw materials in parts by weight as follows: 100 parts of high-density polyethylene, 1.5-2.5 parts of epoxy linseed oil, 0.1-0.3 parts of an ultraviolet light absorber, 0.5-1 part of calcium stearate, 0.5-2 parts of powdered nitrile rubber, 0.06-0.09 part of a main antioxidant and 0.08-0.1 part of an auxiliary antioxidant. The invention further provides a preparation method of the reducing blow molding packing barrel, and a multipoint wall thickness control system for a hollow blow molding parison is introduced. The reducing blow molding packing barrel and the preparation method have the advantages and the benefits as follows: the heat resistance, the toughness effect and the oxidation resistance of a product are improved, production reduction of the product is realized, relatively uniform wall thickness of the final product is guaranteed, and used materials, product weight and environmental pollution are reduced.

Description

Technical field [0001] The invention belongs to the field of blow molding plastics, and in particular relates to a reduced blow molding packaging barrel and a preparation method thereof. Background technique [0002] Packaging is one of the most important application fields of plastic materials, especially for thermoplastic materials. The needs and development of the packaging industry directly change or guide the development direction of plastic material manufacturing and processing technology. Generally speaking, plastic packaging materials and products are currently facing huge pressure in three aspects: first, improving the performance of products, such as increasing the transparency, heat resistance, mechanical strength and barrier properties of materials and products; The second is the pressure from environmental protection; the third is the pressure to reduce costs. The result of the mutual restriction and interaction of the three aspects is that, except for individu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L9/02C08K5/00C08K5/1515C08K5/098C08K5/132C08K5/134C08K5/372B29C49/04
CPCB29C49/04C08L23/06C08L2201/08C08L2207/062C08L9/02C08K5/00C08K5/1515C08K5/098C08K5/132C08K5/1345C08K5/372
Inventor 张桂英
Owner JINBIN DONGBAO TIANJIN TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap