Preparation method for silver golden regenerated cellulose fiber/silver golden regenerated cellulose fiber fabric

A technology of regenerated cellulose and fiber fabrics, applied in the field of dyeing and finishing of regenerated cellulose fibers/regenerated cellulose fiber fabrics, can solve the problem that natural cotton fibers do not have sweat absorption, breathability, comfort, no shielding, antibacterial effect, difficult to use It can achieve the effect of good wearing comfort, good decorative effect and high added value due to taking and other problems.

Active Publication Date: 2014-05-28
QINGDAO UNIV
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are obvious defects in these two types of golden yellow fibers. On the one hand, the former is expensive. For example, in 2011, Nylstar Corporation of the United States developed a 24K Nylgold gold fiber, which is said to have skin care, beauty, and anti-aging effects, but the price per gram exceeds 90. US dollars; the latter has no shielding and antibacterial effects, and due to the introduction of chrome yellow and medium chrome yellow chemical pigments containing toxic elements chromium, the fastness of the combination between fibers and pigments cannot be compared with "plating", it is difficult to avoid There is a certain degree of pollution, which is not suitable for home textile products
On the other hand, the golden-yellow fiber prepared by the pure gold drawing method does not have the sweat-absorbing, breathable, and comfortable wearing properties of natural cotton fibers, so it is difficult to be used for taking; Fiber, because chemical fiber is used as the base material, the waste after use is difficult to degrade in nature, which is not conducive to environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for silver golden regenerated cellulose fiber/silver golden regenerated cellulose fiber fabric
  • Preparation method for silver golden regenerated cellulose fiber/silver golden regenerated cellulose fiber fabric
  • Preparation method for silver golden regenerated cellulose fiber/silver golden regenerated cellulose fiber fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) Put 100Kg of degreased and cleaned viscose fiber into the spray-type finishing processing equipment according to the bath ratio of 1:4, add 1.6Kg of silver nitrate into the batching kettle, prepare a solution and enter the circulation system, React at 35°C for 100 min.

[0034] (2) Following step (1), mix the five components of ethylenediamine, tetraacetic acid sodium salt, benzotriazole, thiosemicarbazide, and ammonia water in a ratio of 1:0.2:0.1:0.3:1 in parts by weight Form a compound stabilizer, weigh 1Kg to prepare a solution, enter the circulation system, and react at 40°C for 30 minutes.

[0035] (3) Following step (2), weigh 0.01Kg of palladium dichloride to prepare a solution and enter the circulation system for 30 minutes;

[0036] Then weigh 2Kg of glucose to prepare a solution, drop it into the circulation system, and react at a constant temperature of 45°C for 70min.

[0037] (4) Following step (3), the treated regenerated fiber or its fabric is firs...

Embodiment 2

[0040] (1) 100Kg of degreased and cleaned wood pulp regenerated fiber fabric (modal fiber) is placed in the spray-type finishing processing equipment at a bath ratio of 1:4, and 0.065Kg of silver acetate is added to the batching tank to prepare After forming a solution, it enters the circulation system and reacts at 75°C for 60 minutes.

[0041] (2) Following step (1), mix the five components of ethylenediamine, tetraacetic acid sodium salt, benzotriazole, thiosemicarbazide, and ammonia water in a ratio of 1:0.2:0.1:0.3:3 in parts by weight Form a compound stabilizer, weigh 1.3Kg to prepare a solution, enter the circulation system, and react at 75°C for 40 minutes.

[0042] (3) Following step (2), weigh 0.05Kg of ammonium hexachloroplatinate to prepare a solution and enter the circulation system for 40 minutes;

[0043] Then weigh 20Kg of sodium hypophosphite to prepare a solution, drop it into the circulation system, and react at a constant temperature of 65°C for 45min.

...

Embodiment 3

[0047] (1) Put 100Kg of degreased and cleaned bamboo pulp regenerated fiber (Tencel) in the overflow finishing processing equipment at a liquor ratio of 1:100, and add 0.11Kg of iminodisulfonic acid into the batching tank Acid-complexed silver concentrate (silver content 27%), prepared into a solution, enters the circulation system, and reacts at 45°C for 60 minutes.

[0048] (2) Following step (1), mix the five components of ethylenediamine, tetraacetic acid sodium salt, benzotriazole, thiosemicarbazide, and ammonia water in a ratio of 1:0.2:0.1:0.3:4 in parts by weight Form a compound stabilizer, weigh 5Kg to prepare a solution, enter the circulation system, and react at 45°C for 50min.

[0049] (3) Following step (2), weigh 2Kg of nickel dichloride to prepare a solution and enter the circulation system for 40 minutes;

[0050] Then weigh 20Kg of glucose to prepare a solution, drop it into the circulation system, and react at a constant temperature of 50°C for 20min.

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
antibacterial rateaaaaaaaaaa
antibacterial rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for a silver golden regenerated cellulose fiber / silver golden regenerated cellulose fiber fabric. According to the preparation method, regenerated cellulose fiber and / or regenerated cellulose fiber fabric is taken as a raw material and soluble silver salts are adopted to obtain the golden regenerated cellulose fiber / golden regenerated cellulose fiber fabric, under the action of lewis acid catalysts and by adopting a catalytic nano chemical plating technology. The silver golden regenerated cellulose fiber / silver golden regenerated cellulose fiber fabric has the functions of antibiosis, deodorization, static electricity resistance and anti-electromagnetic radiation, and can be applied to the fields of military, medical treatment, public health, home furnishing and clothing. The regenerated cellulose fiber, adopted as the raw material by the invention, is cotton pulp regenerated cellulose fiber, wood pulp regenerated cellulose fiber, bamboo pulp regenerated cellulose fiber, or sodium alginate regenerated cellulose fiber; the regenerated cellulose fiber fabric, adopted as the raw material by the invention, is pure fabrics or blended fabrics of the regenerated cellulose fibers, or the blended fabrics of the regenerated cellulose fibers and other chemical fibers.

Description

technical field [0001] The invention relates to a dyeing and finishing method of regenerated cellulose fibers / regenerated cellulose fiber fabrics, in particular to a preparation method of silver golden regenerated cellulose fibers / regenerated cellulose fiber fabrics. Background technique [0002] Silver is the metal with the lowest resistivity among all metals, so it has high conductivity and can resist 5000 volts of static electricity. No static comfort, so the silver fiber can conduct static electricity very quickly and efficiently, which can protect the human body from electromagnetic waves, especially for pregnant women, protect the fetus in the abdomen from electromagnetic waves, and ensure long-term work near electromagnetic sources such as computers The health of personnel plays an important role in health care. The mechanism of metal silver sterilization is to block the physiological process of bacteria. Under wet conditions, silver ions can coagulate the proteins ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/83D06M11/60D06M13/332D06M101/06
Inventor 李群赵昔慧夏延致王艳玮王力平
Owner QINGDAO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap