Magnetic rubber material and preparation method thereof

A technology of magnetic rubber and standard rubber, which is applied in the field of magnetic rubber materials and its preparation, can solve the problems that the magnetic properties of magnetic rubber cannot be maintained, and the plasticity of rubber is not high, so as to achieve the effect of maintaining magnetism and improving plasticity

Active Publication Date: 2014-08-13
NANJING DONGYA RUBBER & PLASTICS
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the existing magnetic rubber materials are mixed with rubber materials, and then the materials are magnetized. As a result, the existing magnetic rubber has various deficiencies such as inability to maintain magnetism and low rubber plasticity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Example 1: A magnetic rubber material comprising the following components:

[0047] 60 copies of standard glue;

[0048] Neoprene 25 parts;

[0049] 20 parts of carbon black;

[0050] 15 parts of dibutyl fat;

[0051] 3 parts of zinc oxide;

[0052] 1 part of magnesium oxide;

[0053] 40 parts of nickel zinc ferrite;

[0054] 1.5 parts of stearic acid;

[0055] Accelerator M 0.3 parts;

[0056] Accelerator DM 0.5 parts;

[0057] Accelerator NA-22 0.3 parts;

[0058] Accelerator TT 0.03 parts;

[0059] Antiaging agent 4010 0.4 parts;

[0060] Anti-aging agent RD 0.4 parts;

[0061] Sulfur 1.4 parts

[0062] In parts by weight.

[0063] The preparation method comprises the steps of:

[0064] (1) Mixing: mix each component by weight and mix;

[0065] (2) Magnetization: Magnetize the mixed rubber material, the magnetic field strength is 1000GS, and the magnetization time is 18min;

[0066] (3) Vulcanization: After the rubber material is magnetized, it is se...

Embodiment 2

[0067] Example 2: A magnetic rubber material comprising the following components:

[0068] 80 copies of standard glue;

[0069] Neoprene 35 parts;

[0070] 30 parts of carbon black;

[0071] 25 parts of dibutyl fat;

[0072] 7 parts of zinc oxide;

[0073] 5 parts of magnesium oxide;

[0074] 50 parts of nickel zinc ferrite;

[0075] 2.5 parts of stearic acid;

[0076] Accelerator M 0.7 parts;

[0077] Accelerator DM 1.5 parts;

[0078] Accelerator NA-22 0.7 parts;

[0079] Accelerator TT 0.07 parts;

[0080] Antiaging agent 4010 0.8 parts;

[0081] 0.8 parts of antioxidant RD;

[0082] Sulfur 1.8 parts

[0083] In parts by weight.

[0084] The preparation method comprises the steps of:

[0085] (1) Mixing: mix each component by weight and mix;

[0086] (2) Magnetization: Magnetize the mixed rubber material, the magnetic field strength is 1200GS, and the magnetization time is 22min;

[0087] (3) Vulcanization: The rubber material is magnetized and then sent to ...

Embodiment 3

[0088] Example 3: A magnetic rubber material comprising the following components:

[0089] 70 copies of standard glue;

[0090] Neoprene 30 parts;

[0091] 25 parts of carbon black;

[0092] 20 parts of dibutyl fat;

[0093] 5 parts of zinc oxide;

[0094] 3 parts of magnesium oxide;

[0095] 46 parts of nickel zinc ferrite;

[0096] 2 parts stearic acid;

[0097] Accelerator M 0.5 part;

[0098] Accelerator DM 1 part;

[0099] Accelerator NA-22 0.5 part;

[0100] Accelerator TT 0.05 parts;

[0101] Antiaging agent 4010 0.6 parts;

[0102] 0.6 parts of antioxidant RD;

[0103] Sulfur 1.6 parts

[0104] In parts by weight.

[0105] The preparation method comprises the steps of:

[0106] (1) Mixing: mix each component by weight and mix;

[0107] (2) Magnetization: Magnetize the mixed rubber material, the magnetic field strength is 1100GS, and the magnetization time is 20min;

[0108] (3) Vulcanization: The rubber material is magnetized and then sent to the vulc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a magnetic rubber material. The magnetic rubber material is characterized by comprising the following components in parts by weight: 60-80 parts of standard rubber, 25-35 parts of chloroprene rubber, 20-30 parts of carbon black, 15-25 parts of dibutyl ester, 3-7 parts of zinc oxide, 1-5 parts of magnesium oxide, 40-50 parts of nickel zinc ferrite, 1.5-2.5 parts of stearic acid, 0.3-0.7 part of accelerant M, 0.5-1.5 parts of accelerant DM, 0.3-0.7 part of accelerant NA, 0.03-0.07 part of accelerant TT, 0.4-0.8 part of anti-aging agent 4010, 0.4-0.8 part of anti-aging agent RD and 1.4-1.8 parts of sulphur. The magnetic rubber material has the advantages that mixing and vulcanization steps are adopted, so that plasticity of the magnetic rubber material can be effectively improved, and the plasticity of the magnetic rubber material is more than 0.55; the magnetic rubber material is sulphurized after being magnetized, so that magnetic property of the magnetic rubber material can be permanently maintained.

Description

technical field [0001] The invention relates to a rubber material and a preparation method thereof, in particular to a magnetic rubber material and a preparation method thereof. Background technique [0002] Magnetic rubber is a general term for magnetic elastomers, which are prepared from rubber, magnetic powder and other additives. Magnetic rubber materials have very broad application prospects in many fields, such as the field of radio communications, electronic computers, etc., all of which require the use of magnetic rubber materials. [0003] Most of the existing magnetic rubber materials are mixed with rubber materials and then magnetized. As a result, the existing magnetic rubbers have various deficiencies such as inability to maintain magnetism and low rubber plasticity. Contents of the invention [0004] Object of the invention: The object of the invention is to address the deficiencies of the prior art, to provide a magnetic rubber material with strong plastici...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L11/00C08K13/02C08K3/04C08K5/12C08K3/22C08K5/09C08K3/06C08J3/24
Inventor 葛胜超
Owner NANJING DONGYA RUBBER & PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka