Composite dental resin material containing macropore molecular sieves

A macroporous molecular sieve and composite resin technology, used in dentistry, dental preparations, dental prostheses, etc., can solve the problems of poor durability and easy wear of the repair surface, and achieve the effect of improving the bonding force and reducing the amount of wear.

Active Publication Date: 2014-08-27
吉林省登泰克牙科材料有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved in the present invention is to introduce macroporous molecular sieves as fillers so that small molecular monomers enter the molecular sieve pores in advance. After polymerization, the molecular sieves and the resin matrix form an inorganic-organic interpenetrating network, and the molecular sieves are fixed in the resin network. Improve the bonding force between the resin matrix and the filler, reduce the wear of the material, and overcome the problems of easy wear and poor durability of the repair surface existing in the technical background

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite dental resin material containing macropore molecular sieves
  • Composite dental resin material containing macropore molecular sieves
  • Composite dental resin material containing macropore molecular sieves

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A monomer: 10% of 1,6-hexanediol dimethacrylate;

[0029] B monomer: bisphenol A diglycidyl dimethacrylate 70%, UDMA10%;

[0030] Monomer C: polyethylene glycol dimethacrylate 8%;

[0031] Initiator 2%.

Embodiment 2

[0033] A monomer: 1,4-butanediol dimethacrylate 10%;

[0034] B monomer: UDMA10%, trihydroxypropane trimethacrylate 70%;

[0035] C monomer: polyethylene glycol dimethacrylate 9.5%;

[0036] Initiator 0.5%.

Embodiment 3

[0038] A monomer: 20% of diethylene glycol dimethacrylate;

[0039] B monomer: UDMA20%, trihydroxypropane trimethylmethacrylate 10%, bisphenol A diglycidyl dimethacrylate 38%;

[0040] C monomer: methoxypolyethylene glycol methacrylate 10%;

[0041] Initiator 2%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite dental resin material containing macropore molecular sieves, and belongs to the technical field of dental repair materials. Dental resins are prepared from acrylic monomers, initiators, inorganic fillers and dyes; in the inorganic fillers, the macropore molecular sieves, of which the average apertures are not less than 7nm and the using amount accounts for 5-85 percent of the inorganic fillers, are introduced. According to the composite dental resin material containing macropore molecular sieves, the macropore molecular sieves are introduced and used as fillers, so that molecular monomers enter the molecular sieve holes in advance; and after polymerization, an inorganic-organic interpenetrating network is formed by the molecular sieves and a resin basal body, or the molecular sieves and the resin basal body are embedded into the molecular sieve holes, so that the molecular sieves are fixed in a resin network, thereby obviously improving the binding force between the resin basal body and the fillers and reducing the abrasion value of the materials.

Description

technical field [0001] The invention belongs to the technical field of dental restorative materials, and relates to a novel photocurable resin dental material containing macroporous molecular sieves in fillers. technical background [0002] Composite resins have two main problems as dental restorative materials, one is high polymerization shrinkage and the other is poor wear resistance. The former will lead to micro-leakage, while the latter will make the repair surface easy to wear and poor durability. People try to reduce the polymerization shrinkage by adding macromolecular monomers or polymerizing expansion monomers, but the effect is not satisfactory. [0003] The wear resistance of the material is not only related to the wear resistance of the resin matrix and the filler, but also depends on the bonding ability between the resin matrix and the filler. At present, the method of surface treatment is mainly used to improve the bonding force between the filler and the re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K6/083A61K6/027C08F290/06C08F222/20C08F2/44
Inventor 闫鹏涛吴慧穆琪闫刚马荣堂
Owner 吉林省登泰克牙科材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products