ABS resin composition for electroplating and preparation method thereof

A technology of ABS resin and composition, applied in the polymer field, can solve the problems of difficult control, complicated synthesis process of grafted ABS polymer, etc., and achieve the effect of excellent thermal stability and electroplatability

Inactive Publication Date: 2014-08-27
SHANGHAI KUMHO SUNNY PLASTICS
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The patent with the publication number CN102653582A discloses a method for preparing electroplated ABS resin by controlling the rubber morphology, rubber particle size and graft thickness in the grafted ABS polymer. The synthesis process of the grafted ABS polymer is complicated and difficult to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ABS resin composition for electroplating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention will be described in detail below in conjunction with specific embodiments. The following examples will help those skilled in the art to further understand the present invention, but do not limit the present invention in any form. It should be noted that those skilled in the art can make several modifications and improvements without departing from the concept of the present invention. These all belong to the protection scope of the present invention.

[0017] The invention discloses an ABS resin composition for electroplating and a preparation method thereof, which comprises a grafted ABS polymer with a weight percentage of 20-50% and a SAN copolymer with a weight percentage of 50-80%. The graft ratio of the grafted ABS polymer is 45%-75%, and the total amount of residual single and oligomer composed of styrene monomer and acrylonitrile monomer in the SAN copolymer is lower than 5000ppm.

[0018] The weight percentage of butadiene in the grafted...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Relative molecular massaaaaaaaaaa
Login to view more

Abstract

The invention discloses ABS resin composition for electroplating and a preparation method thereof. The electroplating ABS resin composition with excellent heat stability and electroplating practicability is prepared by controlling the grafting ratio of grafted ABS polymer, the total amount of oligomers and residual monomers in SAN copolymer and the vacuum degree during extrusion mixing, and the molding yield of electroplated products and the electroplating yield are substantially improved.

Description

technical field [0001] The invention belongs to the technical field of macromolecules, and in particular relates to an ABS resin composition for electroplating and a preparation method thereof. Background technique [0002] Plastic electroplating parts are widely used in interior and exterior decorative parts of automobiles, such as automobile signs, word marks, anti-scratch trims, radiator grilles, wheel covers, inner door handles, gear panels and so on. More than 90% of electroplated parts on the market use ABS or a blend of ABS as the electroplating substrate. With the increasingly fierce market competition, it is required to improve the molding yield and electroplating yield of plastic blanks. Therefore, higher requirements are put forward for the thermal stability and electroplatability of ABS materials. If the thermal stability of ABS is not good, the amount of smoke and smell will be large during injection molding, and silver wires, air marks, white fog, yellowing an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L55/02C08L25/12C08F279/04C08F212/10
Inventor 单桂芳周霆罗明华辛敏琦
Owner SHANGHAI KUMHO SUNNY PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap