Chromium-free passivation solution and preparation method and use thereof, and metal material

A chromium-free passivation, metal material technology, applied in the preparation of chromium-free passivation solution, metal materials, chromium-free passivation solution field, can solve the problem of poor corrosion resistance of protective film, achieve excellent storage resistance, corrosion resistance excellent effect

Inactive Publication Date: 2014-09-24
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the invention is to overcome the poor corrosion resistance defect of the protective film formed by the existing chromium-free passivation solution, and provide a chromium-free passivation solution capable of forming a better protective film with corrosion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chromium-free passivation solution and preparation method and use thereof, and metal material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0013] The invention provides a method for preparing a chromium-free passivation solution, which method comprises mixing water, a silane coupling agent, a water-soluble silicate, an accelerator, a silicon oxide filler and a water-soluble film-forming resin in sequence; The silane coupling agent is CH 2 =C(CH 3 )COO(CH 2 ) 3 Si(OCH 3 ) 3 、CH 2 =C(CH 3 )COO(CH 2 ) 3 Si(OC 2 h 5 ) 3 、CH 2 =C(CH 3 )COO(CH 2 ) 3 SiCH 3 (OCH 3 ) 2 and CH 2 =C(CH 3 )COO(CH 2 ) 3 SiCH 3 (OC 2 h 5 ) 2 At least one of them; the accelerator is thiourea and / or urea.

[0014] Wherein, in detail, the method includes: (1) uniformly mixing water and the silane coupling agent to obtain a uniform liquid A; (2) uniformly mixing the uniform liquid A and a water-soluble silicate to obtain a uniform liquid B; (3) uniformly mix the uniform liquid B and accelerator to obtain uniform liquid C; (4) uniformly mix the uniform liquid C and silicon oxide filler to obtain uniform liquid D; (5) uni...

Embodiment 1

[0051] 28 parts by weight of water and 1.6 parts by weight of silane coupling agent (CH 2 =C(CH 3 )COO(CH 2 ) 3 Si(OCH 3 ) 3, purchased from Hubei Debang Chemical New Material Co., Ltd., brand DB-570) and mixed until uniform at a stirring speed of 1500 rpm to obtain a uniform liquid A.

[0052] Mix all the uniform liquid A and 1 part by weight of water-soluble silicate (sodium metasilicate pentahydrate, purchased from Qingdao Darun Chemical Co., Ltd.) at a stirring speed of 1500 rpm until uniform to obtain uniform liquid B .

[0053] All of the homogeneous liquid B and 0.6 parts by weight of accelerator (thiourea) were mixed until uniform at a stirring speed of 1500 rpm to obtain a homogeneous liquid C.

[0054] All the homogeneous liquid C and 0.72 parts by weight of silica filler (nano silica sol, purchased from Shandong Baite New Material Co., Ltd., the brand is SS-30, and the weight is calculated as silica) at 1500 rpm Mix until homogeneous at stirring speed to obta...

Embodiment 2

[0063] 25 parts by weight of water and 1.4 parts by weight of silane coupling agent (CH 2 =C(CH 3 )COO(CH 2 ) 3 Si(OCH 3 ) 3 , purchased from Hubei Debang Chemical New Material Co., Ltd., brand DB-570) and mixed until uniform at a stirring speed of 1500 rpm to obtain a uniform liquid A.

[0064] All of the uniform liquid A and 1 part by weight of water-soluble silicate (potassium silicate, purchased from Baoding Runfeng Industrial Co., Ltd.) were mixed until uniform at a stirring speed of 1500 rpm to obtain a uniform liquid B.

[0065] All of the homogeneous liquid B and 0.5 parts by weight of accelerator (an equal weight mixture of thiourea and urea) were mixed until uniform at a stirring speed of 1500 rpm to obtain a homogeneous liquid C.

[0066] Mix all the homogeneous liquid C and 0.6 parts by weight of silica filler (nano silica sol, purchased from ADEKA Co., Ltd., the brand is AT-30, and the weight is calculated as silica) at a stirring speed of 1500 rpm until uni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of a chromium-free passivation solution. The method comprises successively mixing evenly water, silane coupling agents, water-soluble silicate, an accelerant, a silica filler and water-soluble film-forming resin. The invention also provides the chromium-free passivation solution prepared according to the preparation method and a use thereof in preparation of metal materials. The invention further provides a metal material which comprises a metal substrate and a coating layer adhering onto the metal substrate, wherein the coating layer is a cured product of the chromium-free passivation solution. A protective film formed by the chromium-free passivation solution provided by the invention is quite excellent in corrosion resistance. In addition, the chromium-free passivation solution provided by the invention is quite excellent in storage resistance, and can be stored for 180 days at room temperature after completion of preparation but does not generate obvious character changes and performance reduction.

Description

technical field [0001] The invention relates to the field of metal protection, in particular to a preparation method of a chromium-free passivation solution, a chromium-free passivation solution obtained by the preparation method, applications of the chromium-free passivation solution and metal materials. Background technique [0002] Metal materials, including hot-dip galvanized metal materials and hot-dip galvanized metal materials, in order to prevent corrosion, a layer of chromium-free passivation solution will be applied on the surface of the metal materials to form a protective film. Therefore, the performance of chromium-free passivation solution is very important for the anti-corrosion of metal materials. [0003] For example, CN101608306A discloses a passivation solution, which also belongs to a chromium-free passivation solution, and is characterized in that the passivation solution is an aqueous solution containing water-soluble molybdenum compound, boric acid, wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D125/14C09D163/00C09D175/04C09D133/04C09D127/12C09D7/12C09D5/08B32B15/08
Inventor 许哲峰陈永徐权冉长荣汤佩林周一林
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap