A technology of graphene and composites, which is applied in the field of activated carbon/graphene composites and its preparation, can solve the problems of high production cost, increased cost of electrode materials, and inability to fully exert the performance of activated carbon/graphene, and achieve simple and easy materials Obtained, the method is simple and the effect

Inactive Publication Date: 2014-10-29
WUHAN INSTITUTE OF TECHNOLOGY
View PDF4 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the preparation of activated carbon/graphene is mainly to physically incorporate graphene into activated carbon, but the cost of electrode materi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Activated carbon / graphene composites are prepared from organic biomass through the following steps:

[0028] (1) Take each component raw material by the following mass fractions: straw crumbs 45%, melamine 50%, iron nitrate 5%;

[0029] (2) After mixing the above-mentioned components evenly, put them into a furnace with a temperature of 300° C. and heat for 3 hours to obtain a gray bulky material with a fluffy structure;

[0030] (3) Put the block material obtained above into a furnace with nitrogen at 600° C. and heat for 10 minutes to obtain an activated carbon / graphene composite.

[0031] Performance characterization, when the current is 0.5A / g, its specific capacitance reaches 180F / g.

Embodiment 2

[0033] Activated carbon / graphene composites are prepared from organic biomass through the following steps:

[0034] (1) Take each component raw material according to the following mass fractions: 80% of straw crumbs, 12% of melamine, and 8% of ferric nitrate;

[0035] (2) After mixing the above-mentioned components evenly, put them into a furnace with a temperature of 500° C. and heat for 3 hours to obtain a gray bulky material with a fluffy structure;

[0036] (3) Put the block material obtained above into a furnace with nitrogen at 900° C. and heat for 5 minutes to obtain an activated carbon / graphene composite.

[0037] Performance characterization, when the current is 0.5A / g, its specific capacitance reaches 170F / g.

Embodiment 3

[0039] Activated carbon / graphene composites are prepared from organic biomass through the following steps:

[0040] (1) Take each component raw material by the following mass fraction: 90% of straw crumbs, 5% of melamine, and 5% of ferric nitrate;

[0041] (2) After mixing the above-mentioned components evenly, put them into a furnace with a temperature of 400° C. and heat for 3 hours to obtain a gray bulky material with a fluffy structure;

[0042] (3) Put the block material obtained above into a furnace with nitrogen at 800° C. and heat for 30 minutes to obtain an activated carbon / graphene composite.

[0043] Performance characterization, when the current is 0.5A / g, its specific capacitance reaches 176F / g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific capacitanceaaaaaaaaaa
Specific capacitanceaaaaaaaaaa
Specific capacitanceaaaaaaaaaa
Login to view more

Abstract

A preparing method of an active-carbon/graphene composite is disclosed. The active-carbon/graphene composite is prepared by uniformly mixing raw materials comprising 45-90% by weight of biomass, 5-50% by mass of carbonitride and 5-10% by mass of a transition-metal-containing compound, heating the material mixture at 300-500 DEG C for 2-5 h to obtain a gray block material with a fluffy structure, and heating the block material in a protective gas atmosphere at 600-900 DEG C for 5-60 min. The biomass is any one or a mixture of straw, saccharose residue, saw dust and rice straw. The method utilizing the biomass for directly synthesizing the active-carbon/graphene composite material is simple. Raw materials are simple and easily available. The obtained active-carbon/graphene composite material has the specific capacitance meeting requirements of electrode materials and is suitable for large-scale production and application.

Description

technical field [0001] The invention belongs to the field of composite material preparation, in particular to an activated carbon / graphene composite and a preparation method thereof Background technique [0002] At present, the capacitor electrode material is mainly activated carbon, but due to the complex structure of activated carbon, the pore utilization rate is low, the conductivity is poor, and the charging is slow. [0003] Since its discovery, graphene has attracted widespread attention for its special structure and excellent properties. It has a high specific surface area, excellent electrical conductivity and capacitive properties. [0004] The introduction of graphene into activated carbon can optimize the structure of activated carbon mesopores, and at the same time enhance the conductivity of activated carbon, shorten the charging time and increase the specific capacitance. [0005] At present, the preparation of activated carbon / graphene is mainly to physicall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B31/08C01B31/04
Inventor 王升高皮晓强李鹏飞孔垂雄杜祖荣邓泉荣王戈民王传新张维
Owner WUHAN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap