Gelatin sponge for trauma hemostasis, as well as preparation method of gelatin sponge

A technology of gelatin sponge and trauma, applied in bandages, absorbent pads, medical science, etc., can solve the problems that need to be further improved, and the treatment effect of trauma hemostasis is not good, and achieve the effect of good sterilization and hemostasis, remarkable effect, and simple preparation method

Inactive Publication Date: 2014-11-05
张秀华
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In short, traditional Chinese medicine has achieved certain results in the development of gelatin sponge, but there are also the following problems: the existing gelatin sponge is not developed for traumatic hemostasis, and the therapeutic effect of traumatic hemostasis is not good, and needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gelatin sponge for trauma hemostasis, as well as preparation method of gelatin sponge

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Example 1 The gelatin sponge for trauma hemostasis is prepared from the main raw materials in the following weight proportions (10 g per part): 3 parts of gelatin, 0.5 part of formaldehyde solution, and 50 parts of water for injection.

[0032] The preparation method of above-mentioned trauma hemostasis gelatin sponge, the steps are as follows:

[0033] (1) Take the gelatin that has been processed into powder and soak it in water for injection for 0.6 hours to make it fully absorb water and swell;

[0034] (2) Heat the expanded gelatin obtained in step (1) on a water bath at 35°C, stir continuously to dissolve, take it out, and cool to 15°C;

[0035] (3) Stir the product obtained in step (2) in a high-speed mixer to produce a large amount of foam, add formaldehyde solution, continue to stir for 0.5 minutes, then pour it into a plastic sand gauze box, put it in a blast chamber, and send it to 26°C The hot air is fully dried to obtain a sponge;

[0036](4) Remove the h...

Embodiment 2

[0037] Example 2 The gelatin sponge for trauma hemostasis is prepared from the main raw materials in the following weight proportions (15 g per part): 9 parts of gelatin, 2.5 parts of formaldehyde solution, and 150 parts of water for injection.

[0038] The preparation method of above-mentioned trauma hemostasis gelatin sponge, the steps are as follows:

[0039] (1) Take the gelatin that has been processed into powder and soak it in water for injection for 1.5 hours to make it fully absorb water and swell;

[0040] (2) Heat the expanded gelatin obtained in step (1) on a water bath at 55°C, stir continuously to dissolve, take it out, and cool to 30°C;

[0041] (3) Stir the product obtained in step (2) in a high-speed mixer to produce a large amount of foam, add formaldehyde solution, continue to stir for 1.5 minutes, then pour it into a plastic sand gauze box, put it into a blast chamber, and send it to 46°C The hot air is fully dried to obtain a sponge;

[0042] (4) Remove...

Embodiment 3

[0044] Example 3 The gelatin sponge for trauma hemostasis is prepared from the main raw materials in the following weight proportions (20 g per part): 5 parts of gelatin, 1 part of formaldehyde solution, and 80 parts of water for injection.

[0045] The preparation method of above-mentioned trauma hemostasis gelatin sponge, the steps are as follows:

[0046] (1) Take the gelatin that has been processed into powder and soak it in water for injection for 0.8 hours to make it fully absorb water and swell;

[0047] (2) Heat the expanded gelatin obtained in step (1) on a water bath at 40°C, stir continuously to dissolve, take it out, and cool to 20°C;

[0048] (3) Stir the product obtained in step (2) in a high-speed mixer to produce a large amount of foam, add formaldehyde solution, continue stirring for 0.8 minutes, then pour it into a plastic sand gauze box, put it in a blast chamber, and send it to 30°C The hot air is fully dried to obtain a sponge;

[0049] (4) Remove the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a gelatin sponge for trauma hemostasis. The gelatin sponge is prepared from the following main active ingredients in parts by weight: 3-9 parts of gelatin, 0.5-2.5 parts of formaldehyde solution, and 50-150 parts of water for injection. The preparation method of the gelatin sponge for trauma hemostasis is simple, and the gelatin sponge for trauma hemostasis is low in manufacturing cost, very obvious in trauma hemostasis effect, and capable of conducting disinfection and hemostasis.

Description

technical field [0001] The invention relates to the field of traditional Chinese medicine, in particular to a sponge for trauma hemostasis and a preparation method. Background technique [0002] Trauma refers to external damage to the body or objects caused by blows, collisions from external objects, or erosion by chemical substances. Refers to emotions such as resentment and worry caused by external stimuli. For example, Dong Zhongshu of the Han Dynasty recorded in "Chunqiu Fanlu · Xuntian Zhidao": "Those who are harmonious and happy are born with external beauty; those who are spiritual are born with internal abundance. External beauty is not as good as internal energy, and what's more, it hurts externally?" Those who hate are born to be injured; those who speak and persuade good people are born to be nurtured.” [0003] Trauma, the words come out of "Plain Questions·Yi Jing Chang Qi Theory". ① One of the classifications of injury syndromes. Generally refers to the dam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/32A61L15/44
Inventor 张秀华
Owner 张秀华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com