Calcium carbide powder dust forming inhibitor, and preparation and application thereof

A technology of calcium carbide powder and molding agent, which is applied in other chemical processes, chemical instruments and methods, grain processing, etc., can solve problems such as decreased work efficiency, high processing cost, and no discovery, so as to improve work efficiency, clean the work environment, Suppress the flying effect

Inactive Publication Date: 2014-11-12
ELION RESOURCE GROUP +1
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The generation of calcium carbide powder has the following major problems: first, the dust of calcium carbide powder is very serious, which brings great difficulties to the operation of workshop workers and reduces work efficiency; second, the processing cost is high, 50 yuan / ton, Yili Chemical The annual direct treatment cost reaches 300,000 yuan; third, the calcium carbide powder becomes solid waste accumulation and pollutes the environment; fourth, if the calcium carbide powder is recycled and reused, the calculation is based on 3,000 yuan / ton of calcium carbide, and the recycling of the recycled calcium carbide powder Calculating that the gas generation is 20% of the gas generation of calcium carbide, it can bring economic benefits of about 3.9 million yuan to Elion Chemical every year
At present, no technology has been found to control calcium carbide powder, the source of dust generation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The calcium carbide powder dust-suppressing forming agent of the present embodiment is made of the following components in parts by weight:

[0039] 1250 mesh light activated calcium carbonate 100;

[0040] Talc powder 10;

[0041] Polyvinyl acetate emulsion 2;

[0042] Borax 1.5.

[0043] Preparation method: take each component, blend and stir evenly to obtain calcium carbide powder dust-suppressing molding agent.

[0044] Application 1: Take 1 ton of crushed calcium carbide as an example, put in 1.5kg of dust suppression molding agent, weigh 1.5kg of the dust suppression molding agent mixed uniformly above, and sprinkle it evenly into the crushing bin before the calcium carbide powder is crushed.

[0045] Application 2: Take the crushed calcium carbide block weighing 1 ton as an example, put in 6.25kg of dust suppression molding agent, weigh 6.25kg of the dust suppression molding agent mixed uniformly above, and sprinkle it evenly into the crushing bin before the c...

Embodiment 2

[0052] The calcium carbide powder dust-suppressing forming agent of the present embodiment is made of the following components in parts by weight:

[0053] 800 mesh light active calcium carbonate 100;

[0054] Talc powder 5;

[0055] Polyvinyl acetate emulsion 2;

[0056] Borax 1.

[0057] Preparation method: take each component, blend and stir evenly to obtain calcium carbide powder dust-suppressing molding agent.

[0058] Application 1: Take 1 ton of crushed calcium carbide as an example, put in 1.5kg of dust suppression molding agent, weigh 1.5kg of the dust suppression molding agent mixed uniformly above, and sprinkle it evenly into the crushing bin before the calcium carbide powder is crushed.

[0059] Application 2: Take the crushed calcium carbide block weighing 1 ton as an example, put in 6.25kg of dust suppression molding agent, weigh 6.25kg of the dust suppression molding agent mixed uniformly above, and sprinkle it evenly into the crushing bin before the calcium ca...

Embodiment 3

[0066] The calcium carbide powder dust-suppressing forming agent of the present embodiment is made of the following components in parts by weight:

[0067] 1250 mesh light active calcium carbonate 100;

[0068] Talc powder 30;

[0069] Polyvinyl acetate emulsion 5;

[0070] Borax 2.

[0071] Preparation method: take each component, blend and stir evenly to obtain calcium carbide powder dust-suppressing molding agent.

[0072] Application 1: Take 1 ton of crushed calcium carbide as an example, put in 1.5kg of dust suppression molding agent, weigh 1.5kg of the dust suppression molding agent mixed uniformly above, and sprinkle it evenly into the crushing bin before the calcium carbide powder is crushed.

[0073] Application 2: Take the crushed calcium carbide block weighing 1 ton as an example, put in 6.25kg of dust suppression molding agent, weigh 6.25kg of the dust suppression molding agent mixed uniformly above, and sprinkle it evenly into the crushing bin before the calciu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a calcium carbide powder dust forming inhibitor, and a preparation and an application thereof. The calcium carbide powder dust forming inhibitor mainly contains calcium carbonate. The calcium carbide powder dust forming inhibitor can inhibit the fly of calcium carbide dusts in air, cleans the work environment, improves the work efficiency, and enables recovered calcium carbide to be molded and reused.

Description

technical field [0001] The invention belongs to the field of environmental protection dust suppression and solid waste utilization, and in particular relates to a calcium carbide powder dust suppression molding agent and its preparation and application. Background technique [0002] In 2012, the national calcium carbide production of PVC reached 9.81 million tons, and the amount of calcium carbide required for one ton of PVC was 1.45-1.5 tons. The annual calcium carbide consumption reached 14.2245-14.715 million tons, and the calcium carbide consumption was very large. The amount of calcium carbide powder produced during the production of acetylene from calcium carbide is 1.5%-2.5%. There are probably two sources of calcium carbide powder: the process of crushing calcium carbide blocks and the process of conveying calcium carbide fragments by belts. Elion Chemical produces about 6,000 tons of calcium carbide powder every year. [0003] The generation of calcium carbide pow...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/22B02C23/00
Inventor 刘珊周玉生刘建辉周明吉郭娟丽
Owner ELION RESOURCE GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka