Method for manufacturing titanium and titanium alloy bars by means of hot continuous rolling
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A titanium alloy, hot continuous rolling technology, applied in the direction of metal rolling, to achieve the effect of high precision and high quality, strong controllability and uniform structure
Active Publication Date: 2014-11-19
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF6 Cites 15 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0007] At present, the above hot continuous rolling rod production line is mainly used to produce steel rods. Due to the special physical and chemical properties
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0091] Using the above-mentioned hot continuous rolling production line to produce Φ16.0mm titanium alloy rods, the main steps and parameters are as follows:
[0092] a. Heating: keep a forged billet of titanium alloy with a size of 150×150×12000mm at a heating temperature of 900°C for 2 hours;
[0093] b. Rough rolling: rough rolling the heated forged billet, the rolling speed is 0.7m / s, rolling 4 passes, the pass elongation coefficient is 1.2, and the final rolling temperature is controlled at 850°C;
[0094] c. Intermediate rolling: after rough rolling, cut the head of the rolled piece by 50-100mm, then perform intermediate rolling, the rolling speed is 1.2m / s, rolling 6 passes, the elongation coefficient of each pass is 1.3; the final rolling temperature is controlled at 820°C ;
[0095] d. Finish rolling: after the intermediate rolling, the rolled piece is cut to 50-100mm and rolled at a rolling speed of 4.1m / s, rolling 6 times, and the elongation coefficient of each pas...
Embodiment 2～ Embodiment 5
[0099] According to the steps of Example 1, the process parameters are changed to obtain Φ30.0mm pure titanium rods, Φ50.0mm titanium alloy rods, Φ80.0mm titanium alloy rods and Φ90.0mm pure titanium rods. Table 4 lists Φ16 .0mm titanium alloy rod, Φ30.0mm pure titanium rod, Φ50.0mm titanium alloy rod, Φ80.0mm titanium alloy rod and Φ90.0mm pure titanium rod specific production process parameters.
[0100] The titanium rod products produced in Examples 1 to 5 all conform to the diameter, cross-sectional thickness and size tolerance of titanium and titanium alloy rods specified in the GB / T2965-2007 standard.
[0101] Table 4 Specific process parameters of bars with different specifications
[0102]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a method for manufacturing titanium and titanium alloy bars by means of hot continuous rolling, and belongs to the technical field of plastic machining for metal. The method is applicable to manufacturing the titanium and titanium alloy bars on the traditional hot continuous rolling unit for steel. The method for manufacturing the titanium and titanium alloy bars by means of hot continuous rolling includes controlling heating cycles, blooming temperatures, rolling speeds and hole patterns; performing shearing, cooling and bundling processes; primarily heating and discharging titanium and titanium alloy square billets out of furnaces; then rolling the titanium and titanium alloy square billets to obtain the bars with the sizes ranging from phi16mm to phi100mm. The method for manufacturing the titanium and titanium alloy bars by means of hot continuous rolling has the advantage that titanium and titanium alloy bar products which are good in surface quality and roundness and uniform in structure property can be quickly and efficiently manufactured on the traditional hot continuous rolling unit for the steel by the aid of the method.
Description
technical field [0001] The invention relates to a method for producing titanium and titanium alloy rods by continuous hot rolling, and belongs to the technical field of metal plastic processing. Background technique [0002] With the development of metallurgical technology, electric transmission and control technology, and mechanical manufacturing technology, high-speed wire rod mills have also developed rapidly, and have become the most mature rod and wire rod rolling equipment. It is characterized by high speed, single wire, no twist, micro tension, combined structure, tungsten carbide roller ring and automation. Its products are characterized by large disk, high precision, high efficiency and good quality. [0003] Titanium and titanium alloys are important structural metals, they have low density, high specific strength, high temperature resistance, low temperature resistance, acid and alkali corrosion resistance, non-magnetic, small linear expansion coefficient, good d...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.