Antioxidant geocell master batch

A geocell masterbatch and anti-oxidation technology, which is applied in the construction field, can solve problems affecting on-site construction and later effects, and achieve the effects of high toughness, reasonable compounding and good stability of the finished product

Inactive Publication Date: 2015-01-07
ANHUI JIEAOMAKE SYNTHETIC MATERIAL TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the preparation of materials for geocells is relatively simple, and most of them are directly extruded from high molecular polymers and carbon black and other reinforcing agents. With the continuous development and progress of society, the research on soil environment, climate environment, etc. Or indirectly affect on-site construction and post-effects, therefore, it is necessary to further improve the performance of traditional simple geocells;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of anti-oxidation geocell masterbatch, it is made up of the raw material of following weight part:

[0023] High-density polyethylene 130, polyurethane 3, calcium hydrogen phosphate 3, silicon carbide 3, potassium tetraborate 2, ammonium metavanadate 0.5, tetradecanedibasic acid 0.4, graphite powder 13, tung oil 0.4, polyethylene Alcohol 3, sodium carboxymethylcellulose 0.5, dilauryl thiodipropionate 0.6, blast furnace slag 12, rare earth additive 3;

[0024] Described rare earth additive is made up of the following raw materials of weight part:

[0025] Boron carbide 40, rare earth chloride 5, attapulgite 18, silicic acid 15, aluminum tripolyphosphate 3, calcium acetate 1, phosphite 0.8, potassium carbonate 2, polyvinylpyrrolidone 0.4, silane coupling agent KH560 0.2,

[0026] Mix calcium acetate with attapulgite, ball mill evenly, add phosphite, keep stirring at 50°C for 10 minutes to obtain a mixture;

[0027] Add aluminum tripolyphosphate to 30 times of wat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antioxidant geocell master batch which comprises the following raw materials in parts by weight: 121-130 parts of high density polyethylene, 1-3 parts of polyurethane, 2-3 parts of calcium hydrophosphate, 2-3 parts of silicon carbide, 1-2 parts of potassium tetraborate, 0.3-0.5 part of ammonium metavanadate, 0.4-1 part of tetradecanedioic acid, 10-13 parts of graphite powder, 0.1-0.4 part of tung oil, 1-3 parts of polyving alcohol, 0.5-2 parts of sodium carboxymethylcellulose, 0.6-1 part of thiodipropionic diglycerol trilaurate, 10-12 parts of blast furnace slag and 2-3 parts of rare earth additive. According to the antioxidant geocell master batch disclosed by the invention, high-strength boron carbide, attapulgite and rare earth elements are fully mixed by the added rare earth additive; the mixture is matched with calcium acetate as a preservative and polyvinylpyrrolidone as a stabilizer; under the surface treatment action of a silane coupling agent, the formed additive has the advantages of good surface strength, toughness, wear resistance and corrosion resistance as well as good stability; the comprehensive quality of the mast batch can be effectively improved, and the adaptability to soil and the resistance to the outside pressure are improved.

Description

technical field [0001] The invention mainly relates to the construction field, in particular to an anti-oxidation geocell masterbatch. Background technique [0002] At present, the preparation of materials for geocells is relatively simple, and most of them are directly extruded from high molecular polymers and carbon black and other reinforcing agents. With the continuous development and progress of society, the research on soil environment, climate environment, etc. Or indirectly affect on-site construction and post-effects, therefore, it is necessary to further improve the performance of traditional simple geocells; [0003] Blast furnace slag is the waste discharged from the blast furnace when smelting pig iron, the main components are CaO, SiO 2 、Al 2 o 3 , my country produces a lot of blast furnace slag waste every year, which is widely used in highways, airports, foundation engineering, railway ballast, concrete aggregate and asphalt pavement, etc., but no blas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L75/04C08L29/04C08K13/06C08K3/38C08K3/34C08K3/32C08K3/26C08K5/098C08K5/372C08J3/22
CPCC08L23/06C08J3/226C08J2323/06C08K2201/014C08L2205/035C08L2207/062C08L75/04C08L29/04C08L1/286C08L39/06C08L91/00C08K13/06C08K9/06C08K3/38C08K3/16C08K3/346C08K3/34C08K2003/327C08K5/098C08K2003/262C08K3/04C08K5/372
Inventor 叶磊
Owner ANHUI JIEAOMAKE SYNTHETIC MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products