Anti-rutting additive containing coal direct liquefaction residue, its preparation method and application

An anti-rutting additive and coal direct liquefaction technology, applied to building components, building insulation materials, buildings, etc., to achieve good low-temperature cracking performance, improve stability, and reduce segregation

Active Publication Date: 2018-05-04
RES INST OF HIGHWAY MINIST OF TRANSPORT +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] There is no report on the preparation of anti-rutting additives from coal direct liquefaction residue and thermoplastic elastomers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-rutting additive containing coal direct liquefaction residue, its preparation method and application
  • Anti-rutting additive containing coal direct liquefaction residue, its preparation method and application
  • Anti-rutting additive containing coal direct liquefaction residue, its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Extrude 4000g of TPE, 2000g of coal direct liquefaction residue, 480g of naphthenic oil, and 60g of C5 petroleum resin at 120°C using a twin-screw extruder (Zhangjiagang Chuangjia Machinery Co., Ltd., SJ series), and then pass through an air-cooled mold Noodle granulation equipment (Nanjing Guangda Rubber and Plastic Machinery Factory) granulated to obtain anti-rutting additives.

[0042] The particle sizes obtained after granulation are all less than 4mm, and the melt index is 3.5g / 10min (190°C, 2.16kg). The density is 1.085g / cm 3 .

Embodiment 2

[0044]Extrude SBS3200g, coal direct liquefaction residue 2000g, rubber oil 480g, C9 petroleum resin 460g at 120°C with a single-screw extruder (Zhangjiagang Chuangjia Machinery Co., Ltd., SJ series), and then air-cool the die surface Pelletizing equipment (Nanjing Guangda Rubber and Plastic Machinery Factory) granulated to obtain anti-rutting additives.

[0045] The particle sizes obtained after granulation are all less than 4mm, and the melt index is 3.0g / 10min (190°C, 2.16kg). The density is 1.1.05g / cm 3 .

Embodiment 3

[0047] Extrude 2000g of SBS, 2000g of coal direct liquefaction residue, 480g of rubber oil, and 480g of C9 petroleum resin at 120°C using a single-screw extruder (Zhangjiagang Chuangjia Machinery Co., Ltd., SJ series), and then cut through the air-cooled die surface. Granulation equipment (Nanjing Guangda Rubber and Plastic Machinery Factory) was used to granulate to obtain anti-rutting additives.

[0048] The particle sizes obtained after granulation are all less than 4mm, and the melt index is 3.8g / 10min (190°C, 2.16kg). The density is 1.045g / cm 3 .

[0049] The melt index of the anti-rutting additive obtained in Examples 1-3 was tested. And put the above additives into the asphalt mixture to observe the dispersion uniformity, see Table 2.

[0050] Table 2 Melt index and dispersibility results

[0051]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
sizeaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of road engineering, and provides an anti-rutting additive containing coal direct liquefaction residue, which includes coal direct liquefaction residue, thermoplastic elastomer and additive, and the weight ratio of the coal direct liquefaction residue and thermoplastic elastomer is 1: 1-4, the additive accounts for 5%-20% of the weight sum of the direct coal liquefaction residue and thermoplastic elastomer. From the perspective of resource conservation and environmental friendliness, the present invention utilizes the comprehensive advantages of coal direct liquefaction residue and polymers to prepare asphalt mixture with excellent anti-rutting performance, good low-temperature performance and durability, and can be used in the middle surface layer to improve The anti-rutting performance of the road can reduce the construction cost and prolong the service life of the road.

Description

technical field [0001] The invention belongs to the field of road engineering, and in particular relates to an asphalt mixture additive containing thermoplastic elastomer polymers, a preparation method and application thereof. Background technique [0002] Asphalt pavement is crushed by heavy-duty vehicles for a long time, and rutting will occur, which will have a negative impact on traffic safety and transportation energy consumption. Adding anti-rutting additives to asphalt mixture is an effective way to solve the above problems. At present, the anti-rutting agent products successfully used in the world include PR series products produced in France, Duroflex and Lufu 8000 asphalt mixture additives in Germany, and SEAM sulfur asphalt modifier produced by Shell in the United States. The high price of the above products has caused the cost of road construction to increase significantly, and its popularization and application has been restricted. In recent years, domestic re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L53/02C08L57/02C08L21/00C08L23/06C08L95/00C08K5/01C04B24/36C04B24/26C04B26/26
Inventor 曹东伟季节张海燕
Owner RES INST OF HIGHWAY MINIST OF TRANSPORT