Low-smoke halogen-free flame-retardant polyethylene cable material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of flame-retardant polyethylene and cable materials, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problem that the flame-retardant performance cannot meet market demand, and achieve good flame-retardant performance, broad application prospects, excellent durability The effect of heat aging
Inactive Publication Date: 2015-02-18
安徽电信器材贸易工业有限责任公司
View PDF7 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, with the expansion of wire and cable applications, the performance requirements for polyethylene cable sheathing materials continue to increase, and the flame retardant properties of general polyethylene cable sheathing materials currently on the market can no longer meet market demand.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0012] A low-smoke halogen-free flame-retardant polyethylene cable material, made of the following raw materials by weight (kg): medium density polyethylene 42, polyamide imide 30, diacetyl epoxy glycerin soybean oleate 8, antimony acid Sodium 6, bisphenol A polycarbonate 22, calcium stearate 3, ammonium metatungstate 8, benzyl benzoate 13, zinc ricinoleate 2.5, strong powder 18, toluene diphenyl phosphate 11, tin Magnesium acid 4.5, 2,5-di-tert-amyl hydroquinone 1.5, triethylene glycol methyl ether borate triester 10, flame retardant 12, bis(2,4-di-tert-butylphenyl) pentaerythritol diethylene Phosphate 2.5, cresyl trisiloxane 2;
[0013] The preparation method of the flame retardant is as follows: a, weigh boehmite, brucite, and montmorillonite in a ratio of 6:5:3 by mass, mix them evenly, pulverize them, pass through a 200-mesh sieve, and then add water to make an oar Concentration is 50% slurry, then add 5% ZnO, 27% NaOH and 21% Na 2 Sn(OH) 6 , heated to 75°C in ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a low-smoke halogen-free flame-retardant polyethylene cable material and a preparation method thereof. The low-smoke halogen-free flame-retardant polyethylene cable material is prepared from the following raw materials in parts by weight: 34-48 parts of medium-density polyethylene, 22-36 parts of polyamide-imide, 5-10 parts of diacetyl epoxy soybean oleic acid glyceride, 4-8 parts of sodium antimonite, 16-28 parts of bisphenol A polycarbonate, 3-4 parts of calcium stearate, 5-10 parts of ammonium metatungstate, 10-15 parts of methyl benzoate, 2-3 parts of zinc ricinoleate, 15-20 parts of StronWiTM powder, 10-15 parts of diphenyl benzyl phosphate, 3-6 parts of magnesium stannate, 1-2 parts of 2,5-di-tert-amyl hydroquinone, 8-12 parts of tris [2-[2-(2-methoxyethoxy)ethoxy]ethyl] orthoborate, 10-15 parts of a flame retardant, 2-3 parts of bi-(2,4-di-t-butylphenyl) pentaerythritol diphosphite and 1.5-2.5 parts of drometrizole trisiloxane. The low-smoke halogen-free flame-retardant polyethylene cable material and the preparation method thereof have the benefits that the cable material has good flame-retardant property, the flame-retardant grade reaches UL94V0, and the cable material is low-smoke halogen-free, cannot release toxic and harmful gas, is safe and environment-friendly and has excellent thermal aging resistance, oil resistance, wear resistance, fatigue resistance and corrosion resistance, thereby having a wide application prospect.
Description
technical field [0001] The invention relates to a low-smoke halogen-free flame-retardant polyethylene cable material and a preparation method thereof, belonging to the field of cable materials. Background technique [0002] Polyethylene cable material has the incomparable advantages of PVC cable material, its light weight, good heat resistance, strong load capacity, no melting, chemical corrosion resistance, high mechanical strength, widely used in distribution network, industrial equipment or other large capacity electricity field. However, with the expansion of wire and cable applications, the performance requirements for polyethylene cable sheathing materials continue to increase, and the flame retardancy of general polyethylene cable sheathing materials currently on the market can no longer meet market demand. Contents of the invention [0003] The object of the present invention is to provide a low-smoke halogen-free flame-retardant polyethylene cable material and...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.