Method for Improving Lamination Performance of Calendered Rubber Wrap Film for Rubber Shoes

A calendering and rubber technology is applied in the field of improving the bonding performance of the calendering rubber strip for rubber shoes, which can solve the problems of strip opening, low flex resistance, shortening the service life of products, etc. Consistent vulcanization performance and improved compatibility

Active Publication Date: 2017-04-19
JIHUA 3537 SHOE MAKING
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the process of rubber shoes production, the method of pasting the strip and the upper is generally to bond the strip film directly with the adhesive. In order to achieve a good bonding effect, the strip rubber must have a high enough glue content. Otherwise, due to insufficient surface viscous properties of the enclosing strips, the bonding effect will be poor, the bonding strength will be insufficient, the flex resistance will be low, quality problems such as enclosing strips will be opened, and the service life of the product will be shortened.
However, the improvement of the glue content, although a good bonding effect is obtained, will greatly increase the cost of the glue material, resulting in excess functions of the enclosure, mismatched product performance, and unsatisfactory economic performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for Improving Lamination Performance of Calendered Rubber Wrap Film for Rubber Shoes
  • Method for Improving Lamination Performance of Calendered Rubber Wrap Film for Rubber Shoes
  • Method for Improving Lamination Performance of Calendered Rubber Wrap Film for Rubber Shoes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1 of the present invention: a method for improving the lamination performance of calendered rubber shroud film for rubber shoes. In the preparation process of the main rubber, the Vickers plasticity of the plasticized rubber used to prepare the main rubber is 0.30, which is used to prepare the main rubber. The Vickers plasticity of the rubber compound is 0.40, and the vulcanization starting point of the main rubber compound is 2 minutes and 30 seconds; during the preparation of the laminating rubber, the Vickers plasticity of the plasticizing rubber used to prepare the laminating rubber is 0.65, the Vickers plasticity of the prepared laminated rubber compound is 0.55, and the vulcanization starting point of the compounded rubber is 2 minutes and 40 seconds; the prepared laminated rubber is calendered by the upper roller and the middle roller of the calender, Then through the middle roller and the lower roller of the calender, the main glue and the calendered l...

Embodiment 2

[0016] Embodiment 2 of the present invention: a method for improving the lamination performance of calendered rubber strips for rubber shoes. During the preparation of the main rubber, the Vickers plasticity of the plasticized rubber used to prepare the main rubber is 0.35. The prepared main rubber The Vickers plasticity of the mixed rubber is 0.50, and the vulcanization starting point of the mixed rubber is 2 minutes and 10 seconds; in the preparation process of the laminating rubber, the Vickers plasticity of the plasticized rubber used to prepare the laminating rubber is 0.63. The Vickers plasticity of the mixed rubber for preparing the laminating rubber is 0.56, and the vulcanization starting point of the mixed rubber is 2 minutes and 40 seconds; the prepared laminating rubber is rolled by the upper roller and the middle roller of the calender, and then rolled The middle roller and the lower roller of the machine calender and laminate the main glue and the calendered lamina...

Embodiment 3

[0017] Embodiment 3 of the present invention: a method for improving the lamination performance of calendered rubber strips for rubber shoes. During the preparation of the main rubber, the Vickers plasticity of the plasticized rubber used to prepare the main rubber is 0.33, which is used to prepare the main rubber. The Vickers plasticity of the rubber compound is 0.45, and the vulcanization starting point of the compound is 2 minutes and 50 seconds; during the preparation process of the laminating glue, the Vickers plasticity of the plasticizing rubber used to prepare the laminating rubber is 0.63 -0.35, the Vickers plasticity of the mixed rubber of the prepared adhesive is 0. 55-0. 60, and the vulcanization starting point of the mixed rubber is 2 minutes 10 seconds-2 minutes 50 seconds; Calendering is carried out by the upper and middle rollers of the calender, and then the main rubber and the calendered laminating glue are calendered and laminated by the middle and lower roll...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for improving the fit performance of a calendering type rubber edge strip adhesive sheet for rubber shoes. According to the invention, by controlling the plastication degree of main rubber and fit rubber in the production process, the edge strip main rubber has sufficient hardness and contraction prevention performance as well as the compatibility with the fit rubber, the malleability, viscosity and durability of the fit rubber are ensured; by controlling indexes of vulcanization starting point of the edge strip main rubber and the fit rubber, the consistent vulcanization performance of the fit rubber and the edge strip main rubber is ensured. The method for improving the fit performance of the calendering type rubber edge strip adhesive sheet for rubber shoes is simple and feasible, is low in cost, and has a good using effect.

Description

technical field [0001] The invention relates to the field of rubber material preparation, in particular to a method for improving the bonding performance of calendered rubber strips for rubber shoes. Background technique [0002] In the process of rubber shoes production, the method of pasting the strip and the upper is generally to bond the strip film directly with the adhesive. In order to achieve a good bonding effect, the strip rubber must have a high enough glue content. Otherwise, due to insufficient surface viscous performance of the enclosure glue, the bonding effect will be poor, the bonding strength will be insufficient, the flex resistance will be low, and quality problems such as the enclosure glue opening will occur, which will shorten the service life of the product. The improvement of the glue content, although a good bonding effect is obtained, will greatly increase the cost of the glue material, resulting in excess functions of the enclosure, mismatched prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B25/04B32B37/02B29C43/58B29C35/02A43B15/00
CPCA43B15/00B32B25/04B32B2250/02B32B2437/02
Inventor 杜江陈松雄周川泉晋齐怀张世林石银平田吉王春桥安廷飞
Owner JIHUA 3537 SHOE MAKING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com