Highly cold-resistant and toughening color masterbatch and preparation method thereof

A technology of cold-resistant toughening and cold-resistant toughening agent, applied in the field of color masterbatch, can solve the problems of restricting the promotion and application of polypropylene, low notched impact strength, large shrinkage rate, etc., and achieves improved processing rheology, obvious toughening effect, The effect of increasing rigidity

Inactive Publication Date: 2015-03-04
DONGGUAN GOLDCOLOR MASTERBATCH
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Adding color masterbatch can be used to adjust the color of plastic products, but some products such as polypropylene have large molding shrinkage, high brittleness, and low notched impact strength, especially at low temperatures, which greatly limits the promotion and application of polypropylene

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A high cold-resistant and toughened color masterbatch, comprising the following raw materials in parts by weight:

[0052] 45 parts polypropylene resin

[0053] Toner 32 parts

[0054] Dispersant 2 parts

[0055] 1 part of cold-resistant toughening agent;

[0056] Wherein, the polypropylene is a mixture of copolymerized polypropylene and homopolypropylene with a weight ratio of 1:1.4;

[0057] The copolymerized polypropylene is a copolymerized polypropylene whose melt index is 10g / 10min under the test conditions of 230°C and 2.16KG; homopolypropylene.

[0058] The cold-resistant toughening agent is a mixture composed of an amide-based β-crystal nucleating agent and a dicarboxylate-based β-crystal-form nucleating agent at a weight ratio of 1:1.2.

[0059] The dispersant is a mixture of polyethylene wax and spreading oil in a weight ratio of 1:1.

[0060] It also includes 1 part of coupling agent, which is a mixture of titanate coupling agent and aluminate coupling ...

Embodiment 2

[0074] A high cold-resistant and toughened color masterbatch, comprising the following raw materials in parts by weight:

[0075] Polypropylene resin 49 parts

[0076] Toner 7 parts

[0077] Dispersant 3.5 parts

[0078] 2 parts of cold-resistant toughening agent;

[0079] Wherein, the polypropylene is a mixture of copolymerized polypropylene and homopolypropylene with a weight ratio of 1:1.6;

[0080] The copolymerized polypropylene is a copolymerized polypropylene with a melt index of 30g / 10min under the test conditions of 230°C and 2.16KG; the homopolymerized polypropylene is 35g / 10min with a melt index of 230°C and 2.16KG homopolypropylene.

[0081] The cold-resistant toughening agent is a mixture composed of an amide-based β-crystal nucleating agent and a dicarboxylate-based β-crystal-form nucleating agent at a weight ratio of 1:1.4.

[0082] The dispersant is a mixture of polyethylene wax and spreading oil in a weight ratio of 2:1.5.

[0083] It also includes 1.5 p...

Embodiment 3

[0097] A high cold-resistant and toughened color masterbatch, comprising the following raw materials in parts by weight:

[0098] Polypropylene resin 53 parts

[0099] Toner 42.5 parts

[0100] Dispersant 4.5 parts

[0101] 3 parts of cold-resistant toughening agent;

[0102] Wherein, the polypropylene is a mixture of copolymerized polypropylene and homopolypropylene at a weight ratio of 1:1.8;

[0103] The copolymerized polypropylene is a copolymerized polypropylene whose melt index is 50g / 10min under the test conditions of 230°C and 2.16KG; the homopolymerized polypropylene has a melt index of 50g / 10min under the test conditions of 230°C and 2.16KG homopolypropylene.

[0104] The cold-resistant toughening agent is a mixture composed of an amide-based β-crystal nucleating agent and a dicarboxylate-based β-crystal-form nucleating agent at a weight ratio of 1:1.5.

[0105] The dispersant is a mixture of polyethylene wax and spreading oil in a weight ratio of 2.5:2.

[010...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of color masterbatches, and in particular relates to a highly cold-resistant and toughening color masterbatch and a preparation method thereof. The color masterbatch comprises the following raw materials in parts by weight: 45-61 parts of polypropylene resin, 32-53 parts of toner, 2-7 parts of a dispersing agent and 1-5 parts of a cold-resistant and toughening agent, wherein polypropylene is a mixture of co-polypropylene and homo-polypropylene which are in a weight ratio of 1 to 1.4-2.2, and the cold-resistant and toughening agent is a mixture of an amide Beta crystal form nucleating agent and a dicarboxylate Beta crystal form nucleating agent which are in a weight ration of 1 to 1.2-1.8. The highly cold-resistant and toughening color masterbatch has an obvious toughening effect and higher impact strength at a low temperature of -20 DEG C than normal temperature; in addition, the rigidity of the highly cold-resistant and toughening color masterbatch is improved obviously at normal temperature; the addition of the color masterbatch is small; the color masterbatch is convenient and flexible to use and add. The preparation method of the color masterbatch and materials provided by the invention are used together so that the materials can take full effect; the process is simple and convenient to operate and control; the quality is stable, the production efficiency is high, and large-scale industrial production can be realized.

Description

technical field [0001] The invention relates to the technical field of color masterbatches, in particular to a highly cold-resistant and toughened color masterbatch and a preparation method thereof. Background technique [0002] Plastic is mainly composed of carbon, oxygen, hydrogen and nitrogen and other organic or inorganic elements, and can be formed into plastic products of various shapes and colors. It has been widely used in every field of modern life, such as household appliances, instruments Apparatus, wire and cable, construction equipment, communication electronics, automobile industry, aerospace, daily hardware, etc. There are three kinds of coloring methods for producing plastic products in the prior art: toner coloring, dyeing and pulling grain coloring and masterbatch coloring. When directly using toner for coloring, the coloring is very simple, but it has the disadvantages of easy to produce color spots, difficult to control color difference, and great enviro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08L51/06C08K13/06C08K9/12C08K5/10C08K3/22C08K3/04C08K5/134C08K5/526C08K5/03C08K5/523B29C47/92B29C48/92
CPCC08K2003/2241C08L23/12B29C48/92B29C2948/92704C08K2201/003C08K2201/006C08L2201/02C08L2205/025C08L2205/035C08L2205/08C08L2205/24C08L2310/00C08L23/14C08L51/06C08L23/06C08L91/00C08K13/06C08K9/12C08K5/10C08K3/04C08K5/03C08K5/523
Inventor 龙必成
Owner DONGGUAN GOLDCOLOR MASTERBATCH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More