A kind of production technology of gold-plated brick

A production process, brick adobe technology, which is applied in the field of gold-plated brick production process, can solve the problems of complex production process and low yield, and achieve the effect of simple production process, strong three-dimensional effect and crystal clear surface

Inactive Publication Date: 2016-09-07
FOSHAN CITY SANSHUI KAILELAI CRAFT PROD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the current production process of K crystal bricks is very complicated and the yield rate is low, how to improve production efficiency, improve decorative effects and reduce production costs is the goal that producers are striving to pursue in order to increase competitiveness and production capacity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] In the present embodiment, the production technology of gold-plated brick, it comprises the steps:

[0030] 1. Preparation of white-glazed vitrified brick adobe. The specification of the adobe is 300*300mm. The adobe is made of (vitrified brick powder) as a raw material, and is prepared into a porcelain adobe through crushing, stirring and pressing molding processes;

[0031] 2. Apply an appropriate amount of medium on the surface of the brick. The applied medium is made of surface glaze 9613 and CMC·H 2 O is a glaze prepared by adding water after mixing. The specific gravity of the glaze is 1.4-1.41 at room temperature and standard atmospheric pressure, 9613 and CMC·H 2 The mixture formula of O includes by weight: surface glaze 9613 has 75 parts, CMC·H 2 O 2 copies;

[0032] 3. Preset the patterns to be printed in the ceramic inkjet printer, send the adobe with the medium into the ceramic inkjet printer for printing, and print platinum glitter powder 9722, gold glitt...

Embodiment 2

[0037] In the present embodiment, the production technology of gold-plated brick, it comprises the steps:

[0038] 1. Preparation of white glaze vitrified brick adobe, the size of the adobe is 600*600mm, the adobe is made of (vitrified brick powder) as raw material, and is prepared into porcelain adobe through crushing, stirring and pressing molding processes;

[0039] 2. Apply an appropriate amount of medium on the surface of the brick. The applied medium is made of surface glaze 9613 and CMC·H 2 O is a glaze prepared by adding water after mixing. The specific gravity of the glaze is 1.4-1.41 at room temperature and standard atmospheric pressure. The surface glaze is 9613 and CMC·H 2 The mixture formula of O includes by weight: surface glaze 9613 has 77 parts, CMC·H 2 O 2.3 parts;

[0040] 3. Preset the pattern to be printed in the ceramic inkjet printer, send the adobe with the medium into the ceramic inkjet printer for printing, and print platinum glitter powder M01 on th...

Embodiment 3

[0045] In the present embodiment, the production technology of gold-plated brick, it comprises the steps:

[0046] 1. Preparation of white glaze vitrified brick adobe, the size of the adobe is 800*800mm, the adobe is made of (vitrified brick powder) as raw material, and is prepared into porcelain adobe through crushing, stirring and pressing molding processes;

[0047] 2. Apply an appropriate amount of medium on the surface of the brick. The applied medium is made of surface glaze 9613 and CMC·H 2 O is a glaze prepared by adding water after mixing. The specific gravity of the glaze is 1.4-1.41 at room temperature and standard atmospheric pressure. The surface glaze is 9613 and CMC·H 2 The mixture formula of O includes by weight: surface glaze 9613 has 78 parts, CMC·H 2 O 2.4 parts;

[0048] 3. Preset the pattern to be printed in the ceramic inkjet printer, send the adobe with the medium into the ceramic inkjet printer for printing, and print gold glitter 235 on the surface o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process of a gold-plated brick. The production process is characterized by comprising the following steps: (a) preparing a white glaze vitrified brick blank; (b) applying a proper amount of mediums to the surface of the brick blank; (c) carrying out ink-jet printing, and printing the surfaces of the mediums of the brick blank with shimmering powder; (d) stacking polishing materials by virtue of a 55-65mesh silk screen; (e) carrying out intermediate temperature sintering at 900-920 DEG C for 70-120 minutes, and plating gold; and (f) carrying out polishing, edging, brick cutting, grading and packaging. The production process has the beneficial effects that steps are simple, the surface of the gold-plated brick is crystal clear, and the gold-plated brick is similar to crystals and agates and is very high in stereoscopic impression.

Description

technical field [0001] The invention relates to the technical field of lighting, and more specifically relates to a production process of gold-plated bricks. Background technique [0002] K crystal tiles, also known as gold-plated tiles, have the characteristics of rich decoration of glazed tiles and low water absorption and good material performance of porcelain tiles. The disadvantages of simple decoration methods of porcelain tiles. Compared with traditional tile products, its biggest advantages are wear resistance and pressure resistance, acid and alkali resistance, non-slip, no radiation and no pollution; it also has the characteristics of health massage. In addition, after K crystal tiles are processed by mosaic art modeling and glaze polishing technology, the surface luster is crystal clear and the three-dimensional effect is very strong, which greatly improves the taste of the polished crystal tile decoration industry and becomes the most high-end product. At prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/89C04B41/86
Inventor 范柏良
Owner FOSHAN CITY SANSHUI KAILELAI CRAFT PROD