A technology of oil-resistant rubber and anti-aging agent, applied in the field of rubber soles, can solve the problems of needing plasticization, consuming manpower and material resources, increasing costs, etc., and achieving the effects of excellent oil resistance, saving manpower and energy consumption
Inactive Publication Date: 2015-03-25
天津市富华皮革制品有限公司
View PDF0 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Due to the use of natural rubber, plastication is required, which consumes manpower and material resources and increases costs
On the other hand, it is difficult to control the acidity and alkalinity of the mixed rubber during the preparation process with carbon black for rubber reinforcement, and it is difficult to meet the requirements of the subsequent vulcanization process.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0011] A preparation method for oil-resistant rubber soles, comprising the following steps:
[0012] (1) Weigh by weight (kg):
[0013] NBR / PVC840,
[0014] Magnesium oxide 40,
[0015] Stearic acid 12,
[0016] Antiaging agent 12,
[0017] Coupling agent 18,
[0018] Dioctyl 110,
[0019] polyethylene glycol 8,
[0020] Sulfur 12,
[0021] Accelerator 14.
Embodiment 2
[0023] A preparation method for oil-resistant rubber soles, comprising the following steps:
[0024] (1) Weigh by weight (kg):
[0025] NBR / PVC960,
[0026] Magnesium oxide 50,
[0027] Stearic acid 24,
[0028] Antiaging agent 16,
[0029] Coupling agent 22,
[0030] Dioctyl 130,
[0031] polyethylene glycol 10,
[0032] sulfur 17,
[0033] Accelerator 30.
Embodiment 3
[0035] A preparation method for oil-resistant rubber soles, comprising the following steps:
[0036] (1) Weigh by weight (kg):
[0037] NBR / PVC900,
[0038] Magnesium oxide 45,
[0039] Stearic acid 18,
[0040] Antiaging agent 14,
[0041] Coupling agent 20,
[0042] Dioctyl 120,
[0043] polyethylene glycol 9,
[0044] Sulfur 15,
[0045] Accelerator 17.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to an oil-resistant rubber shoe sole which is prepared from the following raw materials in parts by weight: 840-960 parts of NBR / PVC, 40-50 parts of magnesium oxide, 12-24 parts of stearic acid, 12-16 parts of an antiager, 18-22 parts of a coupling agent, 110-130 parts of dioctyl-phthalate, 8-10 parts of polyethylene glycol, 12-17 parts of sulphur and 14-30 parts of an accelerant. Rubber-plastic alloy (NBR / PVC=70 / 30) is used as a main rubber material, the rubber-plastic alloy has excellent oil resistance, for meeting environmental protection needs, conventional carbon black is replaced by the white carbon black in the formula to reinforce a sizing material, the coupling agent is added in the formula to improve the bonding strength of the white carbon black and the NBR / PVC simultaneously, and the polyethylene glycol is used to adjust the acid-base property of rubber compound to meet the normal vulcanizing process. Synthetic rubbers are used in formula, plastication is not needed in the production process, the NBR / PVC can be directly poured into an internal mixer to intermix, and manpower and energy consumption are greatly saved.
Description
technical field [0001] The invention relates to a rubber sole, in particular to an oil-resistant rubber sole. Background technique [0002] Rubber soles are generally made of natural rubber as a raw material, after mastication, plus other ingredients for mixing and refining to make rubber soles. Since what is used is natural rubber, plastication is required, which consumes manpower and material resources and increases the cost. On the other hand, it is difficult to control the acidity and alkalinity of the mixed rubber during the preparation process with carbon black for rubber reinforcement, and it is difficult to meet the subsequent vulcanization process. Contents of the invention [0003] The object of the present invention is to overcome above-mentioned deficiency and provide a kind of oil resistant rubber sole. [0004] The purpose of the present invention can be achieved through the following technical solutions: [0005] An oil-resistant rubber sole prepared from...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.