Adhesive for UV-resistant glass functional film

An anti-ultraviolet and adhesive technology, applied in the direction of film/flake adhesive, adhesive, non-polymer adhesive additive, etc. and other problems, to achieve the effect of excellent UV shielding function, low yellow index and cost reduction

Active Publication Date: 2016-08-17
GUANGDONG XINRUI NEW MATERIAL TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the thickness of the coating will affect the clarity of the functional film, the existing functional film generally only adds tris (hydroxyphenyl) triazine compound to the adhesive, but the tris (hydroxyphenyl) triazine compound is expensive and is About 3 times that of mono(hydroxyphenyl) triazine compounds, resulting in high price of this kind of functional film, so it is not conducive to popularization and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive for UV-resistant glass functional film
  • Adhesive for UV-resistant glass functional film
  • Adhesive for UV-resistant glass functional film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1. The formula of adhesive (Tinuvin477:Tinuvin400=2:1)

[0021] 2. Preparation of glass film

[0022] Mix the components of the above formula evenly, and stir for 5-10 minutes to obtain a viscosity of 70-120cps

[0023] The viscose collagen solution is made of PET base film with a thickness of 23um (the transmittance of ultraviolet rays of the base film itself is 80%), and it is coated with a model #20 RDS wire bar to form a viscose layer with a thickness of 7um, which is dried to obtain a UV shielding film. Capability of glass film1.

Embodiment 2

[0025] 1. The formula of adhesive (Tinuvin477:Tinuvin400=1.8:1)

[0026]

[0027] 2. Preparation of glass film

[0028] Mix the components of the above formula evenly, and stir for 5-10 minutes to obtain a viscosity of 70-120cps

[0029] The viscose collagen solution is made of a PET base film with a thickness of 23um (the transmittance of ultraviolet rays of the base film itself is 80%), and it is coated with a model #20 RDS wire bar to form a viscose layer with a thickness of 8um, and dried to obtain a UV shielding Capability of glass film2.

Embodiment 3

[0031] 1. The formula of adhesive (Tinuvin477:Tinuvin400=1:1)

[0032]

[0033] 2. Preparation of glass film

[0034] Mix the components of the above formula evenly, and stir for 5-10 minutes to obtain a viscosity of 70-120cps

[0035] The viscose collagen solution is made of a PET base film with a thickness of 23um (the transmittance of ultraviolet rays of the base film itself is 80%), and it is coated with a model #20 RDS wire bar to form a viscose layer with a thickness of 8um, and dried to obtain a UV shielding Ability of glass film3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention provides an adhesive for an ultraviolet-resistant glass functional film with excellent ultraviolet shielding function, the adhesive comprises a pressure-sensitive adhesive of 44-49% by weight, 2.4-2.7% of an ultraviolet absorber and 48‑54% solvent, and the ultraviolet absorber is composed of a mono(hydroxyphenyl) triazine compound and a tri(hydroxyphenyl) triazine compound in a weight ratio of 1:1.7‑2.2. In the adhesive of the present invention, by selecting a tris(hydroxyphenyl)triazine compound with excellent shielding power for the entire ultraviolet band and a specific ratio of a mono(hydroxyphenyl)triazine compound as an ultraviolet absorber, the obtained adhesive The adhesive has the same UV shielding ability as the single use of tris(hydroxyphenyl)triazine compound when the amount of ultraviolet absorber added is small and the coating is thin, which not only greatly reduces the cost of the adhesive, but also has a lower Yellow index, especially suitable for the use of light-transmitting glass functional films for buildings or vehicles.

Description

technical field [0001] The invention relates to an adhesive, in particular to an adhesive for pasting a functional film on glass, and more particularly to an adhesive for an ultraviolet-resistant glass functional film with excellent ultraviolet shielding function. Background technique [0002] In addition to visible light, sunlight also contains ultraviolet rays and near-infrared rays. In order to reduce the adverse effects of ultraviolet rays and infrared rays on the interior and the human body, various functional films are usually pasted on the transparent glass of buildings or vehicles. Functional films generally include anti-corrosion Scratch layer, main film layer, adhesive layer and release layer, the main film layer is generally composed of polyester film and functional coating coated on the polyester film. In order to improve the clarity of the functional film, a type of protective film that imparts UV protection to the adhesive layer has begun to appear on the marke...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/00C09J11/06C09J7/02
Inventor 施庆元李增李清华
Owner GUANGDONG XINRUI NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com