Glass fiber-reinforced acrylonitrile butadiene styrene (ABS) material
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A glass fiber and component technology, applied in the field of plastics, can solve the problems of small molding shrinkage and poor weather resistance.
Inactive Publication Date: 2012-04-18
WUJIANG MINGFENG POLYURETHANE PROD
View PDF2 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
It has excellent properties such as high surface hardness, toughness, good low temperature resistance, good creep resistance, good dimensional stability, and small molding shrinkage. It is widely used in military industry, automobiles, electronic and electrical components, etc., but ABS is flammable. material, and poor weather resistance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0012] A glass fiber reinforced ABS material, comprising the following components in parts by weight: 100 parts of ABS material, 20 parts of PVC, 15 parts of filler, 1 part of talcum powder, 1 part of antioxidant CA, 5 parts of silane coupling agent 1 part, 1 part of silicone rubber / metal soap, 1 part of zinc stearate, 1 part of stearic acid, 1 part of chitosan, 10 parts of glass fiber. The glass fiber reinforced ABS material is obtained by mixing all the components, drying, extrusion granulation and injection molding.
Embodiment 2
[0014] A glass fiber reinforced ABS material, comprising the following components in parts by weight: 100 parts of ABS material, 35 parts of PVC, 35 parts of filler, 10 parts of talcum powder, 4 parts of antioxidant CA, 20 parts of silane coupling agent 10 parts, 10 parts of silicone rubber / metal soap, 10 parts of zinc stearate, 10 parts of stearic acid, 10 parts of chitosan, 30 parts of glass fiber. The glass fiber reinforced ABS material is obtained by mixing all the components, drying, extrusion granulation and injection molding.
Embodiment 3
[0016] A glass fiber reinforced ABS material, comprising the following components in parts by weight: 100 parts of ABS material, 30 parts of PVC, 20 parts of filler, 2 parts of talcum powder, 2 parts of antioxidant CA, 10 parts of silane coupling agent 5 parts, 5 parts of silicone rubber / metal soap, 5 parts of zinc stearate, 5 parts of stearic acid, 5 parts of chitosan, 15 parts of glass fiber. The glass fiber reinforced ABS material is obtained by mixing all the components, drying, extrusion granulation and injection molding.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
length
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a glass fiber-reinforced acrylonitrile butadiene styrene (ABS) material. The glass fiber-reinforced ABS material is characterized by comprising the following components in part by weight: 100 parts of ABS material, 20 to 40 parts of polyvinyl chloride (PVC), 15 to 35 parts of filling agent, 1 to 10 parts of talcpowder, 1 to 4 parts of antioxidant, 5 to 20 parts of silane coupling agent, 1 to 20 parts of organic silicon rubber/metallic soap, 1 to 10 parts of zinc stearate, 1 to 10 parts of stearic acid, 1 to 10 parts of chitosan and 10 to 40 parts of glass fiber. The ABS material has high heat resistance, toughness and strength, does not crack in the using process, and can be applied to parts such as automobile parts, fan blades and the like.
Description
technical field [0001] The invention relates to an ABS, which belongs to the field of plastics. Background technique [0002] ABS resin refers to the graft copolymer of polybutadiene rubber and monomer styrene and acrylonitrile, where A stands for acrylonitrile, which provides chemical resistance and thermal stability, and B stands for butadiene, which provides toughness and impact resistance , S stands for styrene, which imparts rigidity and ease of processing. It has excellent properties such as high surface hardness, toughness, good low temperature resistance, good creep resistance, good dimensional stability, and small molding shrinkage. It is widely used in military industry, automobiles, electronic and electrical components, etc., but ABS is flammable. material, and poor weather resistance. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a glass fiber reinforced ABS material. [0004] In order to solve t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more