Explosion-proof energy-absorbing polyurea elastic coating and preparation method thereof

An elastic coating and polyurea technology, applied in polyurea/polyurethane coatings, anti-corrosion coatings, coatings, etc., can solve problems such as damage and loss, achieve corrosion-resistant adhesion, reduce damage, and improve protection capabilities

Inactive Publication Date: 2015-04-08
SHANGHAI ORIENTAL YUHONG WATERPROOF TECH
View PDF1 Cites 53 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, military facilities such as warehouses and fortifications are also easily damaged by explosive shock waves, causing greater losses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment l

[0023] The A component is a semi-prepolymer synthesized by the following raw materials in parts by weight: 70 parts of diphenylmethane diisocyanate WANNATE MDI-50 (Yantai Wanhua), polytetrahydrofuran ether glycol PTMEG 2000 (Germany BASF) 18 parts 1,4 butanediol (Shanxi Sanwei) 4 parts; propylene carbonate Jeffsol TM PC (Huntsman, USA) 8 parts.

[0024] The B component is made of the following raw materials in parts by weight: 7 parts of amino-terminated polyether JEFFAMINE T-5000 (U.S. Huntsman), 60 parts of amino-terminated polyether JEFFAMINE D-2000 (U.S. Huntsman) , amino-terminated polyether JEFFAMINE D-400 (U.S. Huntsman Company) 4 parts, amine chain extender diethyltoluenediamine Ethacure-100 (U.S. Albemarle) 25 parts, titanium dioxide R902 (U.S. DuPont Company) 1 part, 1 part of carbon black MA100 (Mitsubishi, Japan), 2 parts of ultraviolet absorber B97 (Basf, Germany).

[0025] The preparation method of the anti-explosion energy-absorbing polyurea elastic coating o...

Embodiment 2

[0032] The A component is a semi-prepolymer synthesized by the following raw materials in parts by weight: 67 parts of diphenylmethane diisocyanate WANNATE MDI-100 (Yantai Wanhua), polytetrahydrofuran ether glycol PTMEG 1000 (Germany BASF) 20 parts 1,4 butanediol (Shanxi Sanwei) 3 parts; propylene carbonate Jeffsol TM PC (American Huntsman) 10 copies.

[0033] The B component is made of the following raw materials in parts by weight: 5 parts of amino-terminated polyether JEFFAMINE T-5000 (Hunsman, USA), 62 parts of amino-terminated polyether JEFFAMINE D-2000 (Hunsman, USA) , amino-terminated polyether JEFFAMINE D-400 (U.S. Huntsman Company) 4 parts, amine chain extender diethyltoluenediamine Ethacure-100 (U.S. Albemarle) 25 parts, titanium dioxide R902 (U.S. DuPont Company) 1 part, 1 part of carbon black MA100 (Mitsubishi, Japan), 2 parts of ultraviolet absorber B97 (Basf, Germany).

[0034] The preparation method of the anti-explosion energy-absorbing polyurea elastic coat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses an explosion-proof energy-absorbing polyurea elastic coating and a preparation method thereof. The explosion-proof energy-absorbing polyurea elastic coating comprises an ingredient A and an ingredient B. The ingredient A comprises, by weight, 40-80 parts of isocyanate, 15-35 parts of polyether polyol, 0-10 parts of a chain extender and 5-15 parts of a diluent. The ingredient B comprises, by weight, 40-80 parts of amine-terminated polyether, 20-40 parts of an amine chain extender, 0-10 parts of a filler and 0-10 parts of an auxiliary agent. The invention discloses the preparation method of the explosion-proof energy-absorbing polyurea elastic coating. A coating layer obtained by spray-coating of the explosion-proof energy-absorbing polyurea elastic coating has ultrahigh strength and good flexibility, can effectively resist explosive shock wave and fragments and is especially suitable for being used as a weapon equipment composite armour and a protective coating of military facility.

Description

technical field [0001] The invention relates to an elastic coating and a preparation method thereof, in particular to an explosion-proof energy-absorbing polyurea elastic coating and a preparation method thereof. Background technique [0002] Military vehicles such as tanks, armored vehicles, and off-road vehicles are easily penetrated by explosive fragments due to the strong rigidity of the metal materials used, causing serious injuries to personnel inside. In addition, military facilities such as warehouses and fortifications are also easily damaged by the shock wave of explosives, causing greater losses. [0003] Due to its high strength and high toughness, the sprayed polyurea elastic material can absorb energy well without damage. Combined with the composite armor at the bottom of the vehicle, it can effectively resist the damage to the bottom of the vehicle by explosive fragments; after spraying on the surface of military facilities, it will greatly improve the protec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/02C09D5/08C09D7/12C08G18/66C08G18/50C08G18/48C08G18/32
CPCC09D175/02C08G18/3206C08G18/324C08G18/4804C08G18/4854C08G18/5024C08G18/6674C08G18/6685C08G18/7671C08K3/04C08K3/22C08K2003/2241C09D5/08C09D7/61
Inventor 王新锋段文锋李红英
Owner SHANGHAI ORIENTAL YUHONG WATERPROOF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap