Process for manufacturing glass craft by using ceramic mold

A technology for ceramic molds and handicrafts, applied in decorative art, special decorative structures, etc., can solve the problems of not being able to meet the needs of mass production for multiple times, low mold reuse rate, and sand spots on glass handicrafts, etc., to meet Multiple production requirements in batches, simple and convenient mold pattern making, good glass pattern forming effect

Inactive Publication Date: 2015-04-22
GUANGDONG JIANGMEN JINDA GLASS CULTURE
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Glass handicrafts generally need to form various beautiful patterns on the glass by heating up the furnace and die-casting, which requires the use of molds, while sand molds are generally used in traditional technology. The production process is relatively complicated, the reuse rate of the mold is not high, and the glass crafts produced may have defects such as sand spots, which can no longer meet the needs of mass production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be described in further detail below.

[0019] A kind of technology that utilizes ceramic mold to make glass handicraft of the present invention is characterized in that, comprises the steps:

[0020] a. Prepare ordinary ceramic tiles and clean them. Ceramic tiles can be made of ordinary tiles such as floor tiles, wall tiles, etc. The materials are convenient and quick, and the cost is also low;

[0021] b. Use manual engraving or laser engraving to engrave the required process patterns on the surface of ceramic tiles; for enterprises with slightly poor production conditions, they can directly make patterns on the surface of ceramic tiles by hand engraving, and for enterprises with financial advantages, they can Using multiple means such as laser engraving or etching to engrave the process pattern on the surface of the ceramic tile, so that this process can be flexibly adopted by different manufacturers;

[0022] c. Put the prepared ceramic m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a process for manufacturing a glass craft by using a ceramic mold. The process comprises the following steps: (a) preparing an ordinary ceramic tile and washing the ordinary ceramic tile; (b) engraving required patterns in the surface of the ceramic tile by hands or laser; (c) putting the manufactured ceramic mold into a furnace, sweeping the surface of the ceramic mold with a bristle broom to remove dust, spraying a mold releasing agent or isolating powder on the surface of the ceramic mold; (d) cleaning a piece of glass, irradiating the tin coating of the glass with a lamp, putting the glass in the furnace, wherein the glass is put on the ceramic mold with the tin coating upward; and covering the furnace with a furnace cover; (e) starting the furnace for casting, increasing the temperature of the furnace to 700 DEG C, and keeping the temperature at 700 DEG C for 25 minutes (f) decreasing the temperature of the furnace to 60 DEG C and shutting down the furnace; and (g) taking the product out of the furnace. The repeated utilization factor of the mold is high and the manufactured glass craft has a good effect.

Description

technical field [0001] The invention relates to glass handicrafts, in particular to a process for making glass handicrafts using ceramic moulds. Background technique [0002] Glass handicrafts, also known as glass handicrafts, are products with artistic value made by processing glass raw materials or glass semi-finished products by hand. They are often used as decorative materials or high-end business gifts, and have a good effect on decorating and beautifying the indoor environment. The majority of consumers love. [0003] Glass handicrafts generally need to form various beautiful patterns on the glass by heating up the furnace and die-casting, which requires the use of molds, while sand molds are generally used in traditional technology. The production process is relatively complicated, the mold reuse rate is not high, and the produced glass handicrafts may have defects such as sand spots, which can no longer meet the needs of mass production. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B44C5/00
Inventor 陈永乐
Owner GUANGDONG JIANGMEN JINDA GLASS CULTURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products