Rubber gloves capable of preventing ultraviolet and preparation method thereof

An anti-ultraviolet and rubber glove technology, which is applied in the field of gloves, can solve the problems of unprotected and cared hands and no anti-ultraviolet rays, and achieve the effects of convenient operation, improved production quality, and injury prevention

Inactive Publication Date: 2015-04-22
ZHENJIANG SUHUI LATEX PROD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to its different uses, it can be divided into medical gloves, industrial gloves and household gloves. At present, gloves only play a simple role in isolation and protection for human hands, but do not have the effect of UV protection, so that users environment, hands are not properly protected and cared for

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber gloves capable of preventing ultraviolet and preparation method thereof
  • Rubber gloves capable of preventing ultraviolet and preparation method thereof
  • Rubber gloves capable of preventing ultraviolet and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] With nitrile rubber: natural rubber is the ratio of 70:30 to prepare rubber-based rubber, by weight; with 15 parts of phenyl-o-hydroxybenzoate and 13.5 parts of oleic acid, stir evenly, mix phenyl-o-hydroxybenzoate and oleic acid Mix and heat to 90-95°C to obtain liquid A; then mix and heat 13.5 parts of KOH (KOH with a mass percentage concentration of 20%) and 58 parts of soft water to 90-95°C to obtain liquid B; Pour liquid B into the homogenizer, fully stir evenly, and stir clockwise at a stirring rate of 105-130r / min, add liquid A at the same time, the injection speed of liquid A is 1L / min, slowly add and stir for at least 20 minutes, The anti-ultraviolet emulsion is obtained; the anti-ultraviolet emulsion is added with ethanol, and the anti-ultraviolet mixed liquid can be obtained by stirring evenly; the anti-ultraviolet liquid emulsion: ethanol is 1:12, by weight; the anti-ultraviolet mixed liquid is added to the rubber base glue, The ratio of rubber base glue to ...

Embodiment 2

[0042] With fluorine rubber: silicone rubber: polyurethane rubber is the ratio of 68:35:28 to prepare rubber-based rubber, by weight; with 15 parts of phenyl-o-hydroxybenzoate and 13.5 parts of oleic acid, stir evenly, and phenyl-o-hydroxybenzoate Ester and oleic acid are mixed and heated to 90-95°C to obtain liquid A; then 13.5 parts of KOH (KOH with a mass percentage concentration of 20%) and 58 parts of soft water are mixed and heated to 90-95°C to obtain liquid B Pour liquid B into the homogenizer, stir well and evenly, stir clockwise, stirring speed is 105-130r / min, add liquid A at the same time, the injection speed of liquid A is 1L / min, add slowly and stir for at least 20 minutes to prepare an anti-ultraviolet emulsion; add ethanol to the anti-ultraviolet emulsion and stir evenly to obtain an anti-ultraviolet mixed liquid; anti-ultraviolet liquid emulsion: ethanol is 1:12, by weight; add anti-ultraviolet to the rubber base Mixed liquid, the ratio of rubber base glue and...

Embodiment 3

[0048] With nitrile rubber: natural rubber: fluorine rubber: silicone rubber is the ratio of 70:35:23:15 to prepare rubber-based rubber, in parts by weight; with 15 parts of phenyl o-hydroxybenzoate and 13.5 parts of oleic acid, stir evenly, Mix and heat phenyl o-hydroxybenzoate and oleic acid to 90-95°C to obtain liquid A; then mix and heat 13.5 parts of KOH (KOH with a mass percentage concentration of 20%) and 58 parts of soft water, and heat to 90- Prepare liquid B at 95°C; pour liquid B into the homogenizer, stir well, and stir clockwise at a stirring rate of 105-130r / min, add liquid A at the same time, the injection speed of liquid A is 1L / min, Slowly add and stir for at least 20 minutes to prepare an anti-ultraviolet emulsion; add ethanol to the anti-ultraviolet emulsion and stir evenly to obtain an anti-ultraviolet mixed liquid; anti-ultraviolet liquid emulsion: ethanol is 1:12 by weight; Add the anti-ultraviolet mixed solution to the base rubber, the ratio of the rubbe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses rubber gloves capable of preventing ultraviolet and a preparation method thereof. Each rubber glove comprises a glove body, and an ultraviolet-proof coating is arranged on the surface of the glove surface. The glove body comprises rubber-based glue and ultraviolet-proof mixed liquid in a weight ratio of 95:5. Improved formula and process are adopted, so that the aging rate of the gloves prepared by the method can be effectively reduced in a place with poor environment and high corrosivity intensity, hands can be effectively protected simultaneously to prevent damage to skin by the ultraviolet, and hand skin is not easy to be damaged as the gloves are worn for long term. In addition, the invention also provides a preparation method, and the method is convenient to operate. By utilizing the preparation method, the production quality is greatly improved. By utilizing the gloves prepared by the method, ultraviolet can be effectively prevented and the effects of whitening and softening skin are achieved in the open air and a specific environment.

Description

technical field [0001] The invention relates to a glove, in particular to a rubber glove with anti-ultraviolet effect. Background technique [0002] Gloves have been widely used in people's production and life because of their barrier protection and can well protect the safety of users. According to its different uses, it can be divided into medical gloves, industrial gloves and household gloves. At present, gloves only play a simple role in isolation and protection for human hands, but do not have the effect of UV protection, so that users Under the environment, the hands do not get the protection and care they deserve. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a rubber glove with anti-ultraviolet function for the above disadvantages, and to provide a preparation method of the glove, which is easy to operate. [0004] For solving the problems of the technologies described above, technical scheme of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08L7/00C08L27/12C08L83/04C08K13/02C08K5/13C08K5/09C08K3/22C08J7/06A41D19/015B29C41/00
CPCC08L9/02A41D19/0055B29C41/003B29K2007/00B29K2009/00B29K2027/12B29K2075/00B29K2083/00C08J7/06C08J2309/02C08J2327/12C08J2407/00C08J2475/04C08J2483/04C08L27/12C08L2201/08C08L2205/03C08L2205/035
Inventor 王学斌施鹏飞
Owner ZHENJIANG SUHUI LATEX PROD