Thermosetting resin and preparation method thereof

A thermosetting and resin technology, applied in the field of chemical materials, can solve the problems of low temperature resistance and achieve the effects of low volatile matter, strong adhesion, and excellent mechanical properties of the cured product
CN104559062AInactive Publication Date: 2015-04-29HENGSHEN
2 Cites 12 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
HENGSHEN
Publication Date
2015-04-29
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
Patent Text Reader

Abstract

The invention discloses thermosetting resin used for pultrusion and a preparation method of the thermosetting resin. The thermosetting resin is composed of the following components by weight percentage: 35-60% of an epoxy resin mixture, 5-15% of a flexibilizer, 35-60% of a curing agent, 0-10% of a catalyst and 0-3% of an internal releasing agent. The preparation method of the thermosetting resin comprises the following steps: uniformly dispersing the epoxy resin mixture and the flexibilizer to be used as a component A by a high-speed dispersing agent at 60 DEG C, stirring the curing agent, an accelerant and the internal releasing agent at a high speed to uniformly disperse to be used as a component B, uniformly mixing the component A and the component B at normal temperature, and finally defoaming the mixture resin in a vacuum oven to prepare a resin casting body. Compared with unsaturated polyester resin, the thermosetting resin is low in volatile component, low in pollution, good in heat resistance, strong in adhesive force, excellent in mechanical property of a cured material and wide in designable range in terms of temperature tolerance.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to the field of chemical materials, and in particular relates to a thermosetting resin for pultrusion molding and a preparation method thereof. Background technique

[0002] The pultrusion process is the only process that can continuously mechanize the production of fiber-reinforced composite materials. At present, unsaturated polyester is widely used to match glass fibers to prepare various types of materials. With the continuous expansion of applications, the mechanical properties, temperature resistance and environmental friendliness of unsaturated resin systems cannot meet the requirements of use. Contents of the invention

[0003] The purpose of the present invention is to overcome the above disadvantages, and provide a thermosetting resin for pultrusion and its preparation method, which can meet the requirements of the pultrusion process, and can be used for a long time at 140 ° C, solving the current problems. Because of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine