A kind of warm mix asphalt and preparation method thereof

A technology of warm mix asphalt and matrix asphalt, applied in building thermal insulation materials, building components, climate change adaptation, etc. Reduce the high temperature viscosity of asphalt and other problems to achieve the effect of reducing energy consumption, reducing high temperature viscosity, and low high temperature viscosity

Active Publication Date: 2017-01-11
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The viscosity reducer can reduce the viscosity of modified asphalt at 175°C; the synthetic paraffin in the viscosity reducer is a non-elastic material, which is easy to be brittle under low temperature conditions, resulting in a decrease in the low temperature tensile and brittle crack resistance of the asphalt mixture , and most of the low-melting organic waxes reduce the viscosity of asphalt at high temperature, and also reduce the viscosity at 60°C, reducing the anti-rutting performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The mass percentage of warm mix asphalt raw material is:

[0034] Stearic acid: 0.5%;

[0035] Coconut oil fatty acid diethanolamide: 7.5%;

[0036]Base bitumen: 92.0%.

[0037] Add stearic acid and coconut oil fatty acid diethanolamide into the reaction vessel respectively according to the proportion, stir and raise the temperature to 65°C, and the stirring time is 30 minutes, then add it to the base asphalt according to the proportion, the mixing temperature is 147°C, and the stirring time is 50 minutes , made of warm mix asphalt.

Embodiment 2

[0039] The mass percentage of warm mix asphalt raw material is:

[0040] Stearic acid: 7.2%;

[0041] Coconut oil fatty acid diethanolamide: 2.5%;

[0042] Base bitumen: 90.3%.

[0043] Add stearic acid and coconut oil fatty acid diethanolamide into the reaction vessel respectively according to the proportion, stir and heat up to 70°C, and the stirring time is 20 minutes, then add it to the base asphalt according to the proportion, the mixing temperature is 140°C, and the stirring time is 45 minutes , made of warm mix asphalt.

Embodiment 3

[0045] The mass percentage of warm mix asphalt raw material is:

[0046] Stearic acid: 3.6%;

[0047] Coconut oil fatty acid diethanolamide: 1.2%;

[0048] Base bitumen: 95.2%.

[0049] Add stearic acid and coconut oil fatty acid diethanolamide into the reaction vessel respectively according to the proportion, stir and heat up to 85°C, and the stirring time is 25 minutes, then add it to the base asphalt according to the proportion, the mixing temperature is 135°C, and the stirring time is 35 minutes , made of warm mix asphalt.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
penetrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses warm mix asphalt and a preparation method thereof. The warm mix asphalt comprises the following raw materials in percentage by weight: 0.1-10 percent of stearic acid, 0.1-10 percent of cocoanut oil fatty acid diethanolamide, and 80-99.8 percent of matrix asphalt. The preparation method for the warm mix asphalt comprises the following steps: respectively adding the stearic acid and cocoanut oil fatty acid diethanolamide in a reaction vessel according to a ratio, uniformly mixing, adding the mixture in the matrix asphalt according to a ratio, and uniformly mixing to prepare the warm mix asphalt. The warm mix asphalt is environment-friendly, and has a good application prospect in mix asphalt mixing.

Description

technical field [0001] The invention relates to a road asphalt and a preparation method thereof, in particular to a warm-mix asphalt and a preparation method thereof. Background technique [0002] Asphalt mixtures currently used in road engineering are generally divided into two types according to the mixing construction temperature: cold mix asphalt mixture CMA (Cold Mix Asphalt) and hot mix asphalt mixture HMA (Hot Mix Asphalt). Cold-mix asphalt mixture is generally mixed and paved with emulsified asphalt or liquid asphalt and aggregate at room temperature, without heating the aggregate and binder, which can save a lot of energy. However, the initial road performance of cold-mix asphalt mixture is poor, and it is difficult to meet the requirements of important projects such as expressways and heavy-duty traffic roads. Hot mix asphalt mixture is the most widely used mixture with the best road performance. However, in the production process of hot mix asphalt mixture, asph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08K5/09C08K5/20
CPCY02A30/30
Inventor 陈闯范思远陈保莲张静宁爱民李志军程国香
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com