Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Abrasion-resistant aluminum alloy doorframe

A technology of aluminum alloy and door frame, applied in the direction of window/door frame, coating, conjugated diene coating, etc., can solve the problems of poor use effect, corrosion of aluminum alloy door frame, shortened service life, etc., and achieve good use effect , the effect of high mechanical strength and long service life

Inactive Publication Date: 2015-04-29
重庆市银泉实业有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because it is directly made of aluminum alloy, it is very easy to be scratched by foreign objects during use, which will cause the entire aluminum alloy door frame to be corroded by air and other substances, resulting in aging and damage of the entire aluminum alloy door frame, and shortening the service life. Frequent replacement of the door frame increases the cost and the use effect is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] The preferred embodiments of the present invention are described in detail below, so that the advantages and features of the present invention can be more easily understood by those skilled in the art, so as to define the protection scope of the present invention more clearly.

[0009] The invention describes a door frame for wear-resistant aluminum alloy, which includes an aluminum alloy body and a wear-resistant paint coated on the surface of the aluminum alloy body. The aluminum alloy is formed by melting aluminum and chromium at high temperature. The percentages by weight of the components are respectively: the aluminum accounts for 68%, the chromium accounts for 32%, and the wear-resistant coating is composed of butadiene rubber, filler, plasticizer and coupling agent, and the filler is oxidized Aluminum powder, the plasticizer is diethylene glycol di-m-toluate, the coupling agent is isopropyl titanate tristearate, and the percentage by weight of each component in t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an abrasion-resistant aluminum alloy doorframe. The abrasion-resistant aluminum alloy doorframe comprises an aluminum alloy body and an abrasion-resistant coating which is coated on the surface of the aluminum alloy body, wherein the aluminum alloy is formed by fusing aluminum and chromium at high temperature; the abrasion-resistant coating comprises cis-polybutadiene, a filling agent, a plasticizing agent and a coupling agent; the filling agent is aluminum oxide powder; the plasticizing agent is diethylene glycol binary m-methyl benzoate; the coupling agent is isopropyl titanate tristearate; the percentages by weight of components in the abrasion-resistant coating are as follows: the cis-polybutadiene accounts for 57-77%; the aluminum oxide powder accounts for 17-24%; the diethylene glycol binary m-methyl benzoate accounts for 4-11%; the isopropyl titanate tristearate accounts for 2-8%. The aluminum alloy itself is high in mechanical strength; the surface of the aluminum alloy is protected by the abrasion-resistant coating; the aluminum alloy has the characteristics of sagging resistance, abrasion resistance, impossibility in damage, long service life and good using effect.

Description

technical field [0001] The invention relates to an aluminum alloy door frame, in particular to a wear-resistant aluminum alloy door frame. Background technique [0002] The aluminum alloy door frame is a door frame component made of surface-treated aluminum alloy profiles through blanking, drilling, milling, tapping, manufacturing and other processing processes, and then used with connectors, sealing materials and opening and closing hardware accessories Assembled. Because it is directly made of aluminum alloy, it is very easy to be scratched by foreign objects during use, which will cause the entire aluminum alloy door frame to be corroded by air and other substances, resulting in aging and damage of the entire aluminum alloy door frame, and shortening the service life. Frequent replacement of the door frame increases the cost, and the use effect is poor. Contents of the invention [0003] The purpose of the present invention is to provide a door frame for wear-resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E06B1/52E06B1/12C22C38/18C09D109/00C09D7/12
Inventor 吴金良
Owner 重庆市银泉实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products