Production process for lowering fabric noises
A production process and fabric technology, applied in the direction of textiles, fabrics, multi-strand fabrics, etc., can solve the problems of insufficient feather resistance, static electricity, stuffy heat, etc., and achieve the effect of increasing density, improving sleep quality, and improving sleep
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
specific Embodiment 1
[0011] A production process for reducing the noise of fabrics. The fabric is a double-layer fabric woven with warp yarns and weft yarns of 80s yarn count. The specific steps are as follows: spinning → weaving → finishing with a softening agent → drying, and the warp yarns are long Velvet cotton, the weft yarn is superfine polyester fiber, bamboo carbon fiber. The mass ratio of warp yarns to weft yarns is 1.2:0.7. The softening finishing agent contains a special aliphatic polymer compound emulsion containing silicone and a hydrophilic softening agent. The drying temperature is 80° C. and the drying time is 30 minutes.
specific Embodiment 2
[0012] A production process for reducing the noise of fabrics. The fabric is a double-layer fabric woven with warp and weft yarns of 100s yarn count. The specific steps are as follows: spinning→weaving→finishing with a softening agent→drying, and the warp is long Velvet cotton, the weft yarn is superfine polyester fiber, bamboo carbon fiber. The mass ratio of warp yarns to weft yarns is 2.4:1.9. The softening finishing agent contains a special aliphatic polymer compound emulsion containing silicone and a hydrophilic softening agent. The drying temperature is 125° C. and the drying time is 45 minutes.
specific Embodiment 3
[0013] A production process for reducing the noise of fabrics. The fabric is a double-layer fabric woven with warp yarns and weft yarns of 80s yarn count. The specific steps are as follows: spinning → weaving → finishing with a softening agent → drying, and the warp yarns are long Velvet cotton, the weft yarn is superfine polyester fiber, bamboo carbon fiber. The mass ratio of warp yarns to weft yarns is 1.7:1.1. The softening finishing agent contains a special aliphatic polymer compound emulsion containing silicone and a hydrophilic softening agent. The drying temperature is 114° C. and the drying time is 38 minutes.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com