Composite Initiator and Its Application

A composite initiator and application technology, applied in the direction of adhesive types, adhesive additives, graft polymer adhesives, etc., can solve the problems of high toxicity of vinyl acetate, poor environmental protection performance, poor comprehensive performance, etc. The effect of excellent curing time, excellent comprehensive performance and excellent bond strength

Active Publication Date: 2017-01-04
海安县紫石涂料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The vinyl acetate used in this glue is highly toxic and not environmentally friendly
[0007] Chinese invention patent application 201410004735.1 (public date: April 16, 2014) discloses an adhesive, the glue includes: polyvinyl alcohol PVA, vinyl acetate VAC, acrylic acid AA, acrylamide AM, ammonium persulfate , anionic emulsifier A-102, alkyl polyoxyethylene ether LCN-287 nonionic emulsifier; corn starch, transparent powder, plasticizer, diethylene glycol dibenzoate DEDB, preservative KSG-201, hydroxide Sodium, and methanol; but this glue still uses toxic vinyl acetate, which has poor environmental performance
[0008] At the same time, the related glue disclosed in the prior art has poor comprehensive performance in terms of use effect and cannot meet the stringent demands of the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite Initiator and Its Application
  • Composite Initiator and Its Application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present embodiment relates to a composite initiator, the adhesive prepared therefrom and its preparation method; the adhesive comprises the following components in parts by weight:

[0022] Polyvinyl acetate 700,

[0023] Vinyl acetate 300,

[0024] polyvinyl alcohol 120,

[0025] Dibutyl phthalate 60,

[0026] Diethylene glycol dibenzoate 20,

[0027] Octanol 10,

[0028] Isopropanol 30,

[0029] Allyl methacrylate 10,

[0030] Ethylene glycol dimethacrylate 5,

[0031] Toluene diisocyanate 3,

[0032] Sodium bicarbonate 35,

[0033] water 1400,

[0034] Emulsifier 40, the emulsifier is sodium oleate (i.e. sodium octadecenoate);

[0035] Composite initiator 5,

[0036] Methylolacrylamide 20,

[0037] waxy cornstarch 10,

[0038] sodium hypochlorite 2,

[0039] The composite initiator is composed of the following components in weight ratio: potassium persulfate, ammonium persulfate, sodium bisulfite, sodium persulfate, and kaolin in a weight ratio of 3...

Embodiment 2

[0047] The present embodiment relates to a kind of composite initiator, and the adhesive prepared by the same and its preparation method; the preparation method of the adhesive refers to Example 1, and the adhesive includes the following components in parts by weight:

[0048] Polyvinyl acetate 1050,

[0049] Vinyl acetate 350,

[0050] polyvinyl alcohol 145,

[0051] Dibutyl phthalate 100,

[0052] Diethylene glycol dibenzoate 40,

[0053] Octanol 15,

[0054] Isopropanol 45,

[0055] Allyl methacrylate 25,

[0056] Ethylene glycol dimethacrylate 10,

[0057] Toluene diisocyanate 7,

[0058] Sodium bicarbonate 50,

[0059] water 1500,

[0060] Emulsifier 50, the emulsifier is sodium dodecylbenzenesulfonate;

[0061] Composite initiator 9,

[0062] Methylolacrylamide 32,

[0063] waxy cornstarch 15,

[0064] Sodium hypochlorite 7,

[0065] The composite initiator is composed of the following components in weight ratio: potassium persulfate, ammonium persulfate, s...

Embodiment 3

[0067] The present embodiment relates to a kind of composite initiator, and the adhesive prepared by the same and its preparation method; the preparation method of the adhesive refers to Example 1, and the adhesive includes the following components in parts by weight:

[0068] Polyvinyl acetate 800,

[0069] Vinyl acetate 315,

[0070] Polyvinyl alcohol 125,

[0071] Dibutyl phthalate 80,

[0072] Diethylene glycol dibenzoate 25,

[0073] Octanol 12,

[0074] Isopropanol 35,

[0075] Allyl methacrylate 15,

[0076] Ethylene glycol dimethacrylate 7,

[0077] Toluene diisocyanate 4,

[0078] Sodium bicarbonate 39,

[0079] water 1450,

[0080] Emulsifier 45, the emulsifier is sodium dodecylbenzenesulfonate;

[0081] Composite initiator 6,

[0082] Methylolacrylamide 25,

[0083] waxy cornstarch 12,

[0084] Sodium hypochlorite 4,

[0085] The composite initiator is composed of components in the following weight ratios: potassium persulfate, ammonium persulfate, sodiu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a composite initiator and use of the composite initiator. The composite initiator comprises the following components in parts by weight: 3-4 parts of potassium persulfate, 1-2 parts of ammonium persulfate, 2-4 parts of sodium hydrogen sulfite, 1-2 parts of sodium persulfate and 1-3 parts of kaoline. The invention also relates to use of the composite initiator in preparation of an adhesive. The adhesive prepared by using the composite initiator is high in environmental friendliness, high in heat stability, quick in initial drying time, high in waterproof performance, high in bonding strength, quick in curing time and excellent in comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of initiators, in particular to a composite initiator and its application. Background technique [0002] At present, the threshold industry of doors and windows is relatively low, and the competition in the industry is relatively chaotic. In order to improve product quality and market competitiveness, continuous improvement is required. High-grade energy-saving wooden doors and windows widely used in building exterior windows include: pure wood doors and windows, aluminum-clad wood doors and windows, and wood-aluminum composite doors and windows. The wood-aluminum composite doors and windows are more suitable for the rainy, high temperature and humid climate conditions in the south because the outer side is made of heat-insulating aluminum alloy profiles and the inner side is made of wood decorative profiles. At present, the structure of wood-aluminum composite doors and windows processed and produced in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F4/40C09J151/00C09J11/08C09J11/04C09J11/06
Inventor 董德明
Owner 海安县紫石涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com