Medical perfusion tube material

An infusion tube and raw material technology, applied in the field of medical infusion tube materials, can solve the problems of high cost, patient injury, poor elasticity, etc., and achieve the effects of low cost, improved flame retardancy, and excellent elasticity

Inactive Publication Date: 2015-06-24
刘泽华
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary PVC hoses have poor elasticity and are not suitable for infusion tubes connected to scalp needles, which may cause harm to patients
Although there are PVC materials modified with TPU on the market, the cost is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A medical transfusion tube material is characterized in that the components of the raw materials are grouped by weight as follows:

[0016] 15 parts of PVC resin powder with a polymerization degree of 1500-2200, 8 parts of oxidized polyethylene wax, 3 parts of polycaprolactam resin, 0.5 part of silicone defoamer, 4 parts of polyisoprene, 0.8 part of paste calcium zinc, 2 parts of monophenylenedioctyl phosphite, 3 parts of glass fiber, 1.2 parts of stearic acid amide, 0.4 parts of antioxidant composed of trinonylphenyl phosphite and trioctyl trimellitate in a molar ratio of 1:1 , 0.5 parts of phenylmethyl silicone oil.

Embodiment 2

[0018] A medical transfusion tube material is characterized in that the components of the raw materials are grouped by weight as follows:

[0019] 18 parts of PVC resin powder with a degree of polymerization of 1500-2200, 10 parts of oxidized polyethylene wax, 4 parts of polycaprolactam resin, 0.6 part of silicone defoamer, 5 parts of polyisoprene, 0.9 part of paste calcium zinc, 3 parts of phenylenedioctyl phosphite, 4 parts of glass fiber, 1.3 parts of stearic acid amide, 0.5 parts of antioxidant composed of trinonylphenyl phosphite and trioctyl trimellitate in a molar ratio of 1:1 , 0.5 parts of phenylmethyl silicone oil.

Embodiment 3

[0021] A medical transfusion tube material is characterized in that the components of the raw materials are grouped by weight as follows:

[0022] 20 parts of PVC resin powder with a polymerization degree of 1500-2200, 12 parts of oxidized polyethylene wax, 5 parts of polycaprolactam resin, 0.7 parts of silicone defoamer, 6 parts of polyisoprene, 1 part of paste calcium zinc, 0.6 parts of antioxidant composed of 4 parts of monophenylenedioctyl phosphite, 5 parts of glass fiber, 1.5 parts of stearic acid amide, trinonylphenyl phosphite and trioctyl trimellitate in a molar ratio of 1:1 , 0.5 parts of phenylmethyl silicone oil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a medical perfusion tube material. The medical perfusion tube material comprises, by weight, 15-20 parts of PVC resin powder, 8-12 parts of oxidized polyethlene wax, 3-5 parts of polyamide resin, 0.5-0.7 parts of an organosilicon antifoaming agent, 4-6 parts of polyisoprene, 0.8-1 part of calcium-zinc paste, 2-4 parts of diisooctyl phenyl phosphate, 3-5 parts of glass fibers, 1.2-1.5 parts of octadecanamide, 0.4-0.6 parts of an anti-oxidant and 0.5 parts of benzyl silicone oil. The medical perfusion tube material utilizes medical PVC paste as a main raw material and other accessory materials. A medical perfusion tube prepared from the medical perfusion tube material has a low cost, is conducive to flame retardation and strength improvement, and has tensile strength of 130-135MPa, bending strength of 230-240MPa and excellent elasticity.

Description

technical field [0001] The invention belongs to the technical field of medical materials, in particular to a medical infusion tube material. Background technique [0002] Ordinary PVC infusion tubes also contain plasticizers, which increase the elasticity of the tubes and help maintain the accuracy of flow rate adjustment. At present, the plasticizer of the highly elastic precision filter infusion sets used in many hospitals is much higher than that of ordinary transparent tube infusion sets. During infusion, this plasticizer generally does not separate out from the tube material, only when infusion of paclitaxel chemotherapeutics, this DEHP plasticizer will obviously separate out. There is no need to add plasticizers to general plastic products, unless it is necessary to increase the elasticity of the plastic. [0003] Medical infusion tube is a general term for lumen products that connect the inside and outside of the human body. There are metal, plastic, rubber and oth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/30C08L77/02C08K13/04C08K7/14C08K5/526C08K5/12C08K5/20
CPCC08L27/06C08K2201/014C08L2201/02C08L2203/18C08L2205/035
Inventor 刘泽华
Owner 刘泽华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com