Environment-friendly and waterproof heat-insulating coating

A heat-insulating coating and environmental protection technology, applied in cement coatings, reflective/signal coatings, coatings, etc., can solve problems such as waterproof and heat insulation contradictions, and achieve the effects of reduced building energy consumption, excellent waterproof, and long service life

Inactive Publication Date: 2015-07-01
安徽顺金浩科技有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in general, as far as the coating itself is concerned, waterproofing requires a dense coating, while heat insulation requires a loose and porous coating. There is a contradiction between waterproofing and heat insulation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly and waterproof heat-insulating coating
  • Environment-friendly and waterproof heat-insulating coating
  • Environment-friendly and waterproof heat-insulating coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Example 1: Mix sepiolite powder, diatomite powder, attapulgite, mica powder, heavy calcium, light calcium, titanium dioxide, talcum powder and white cement in a mixer, then add HPMC and renewable latex powder , hollow glass microspheres, ultrafine active dicyandiamide, calcium stearate and organic silicon water repellent are mixed evenly. Each component is configured by weight percentage as shown in Table 1 below:

[0018] Table 1

[0019]

Embodiment 2

[0020] Embodiment 2: Mix sepiolite powder, diatomite powder, attapulgite, mica powder, heavy calcium, light calcium, titanium dioxide, talcum powder and white cement in a mixer, and then add HPMC and renewable latex powder , hollow glass microspheres, ultrafine active dicyandiamide, calcium stearate and organic silicon water repellent are mixed evenly. Each component is configured by weight percentage as shown in Table 2 below:

[0021] Table 2

[0022]

Embodiment 3

[0023] Embodiment 3: Mix sepiolite powder, diatomite powder, attapulgite, mica powder, heavy calcium, light calcium, titanium dioxide, talcum powder and white cement in a mixer, and then add HPMC and renewable latex powder , hollow glass microspheres, ultrafine active dicyandiamide, calcium stearate and organic silicon water repellent are mixed evenly. Each component is configured by weight percentage as shown in Table 3 below:

[0024] table 3

[0025]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an environment-friendly and waterproof heat-insulating coating, which is mainly prepared from a base material, a pigment, a filler and an assistant, wherein the base material is formed by cold mixing renewable rubber powder, white cement and an organosilicone water repellent; and the pigment and the filler are prepared from a heat-insulating functional material, a heat-reflecting functional material and a filler. The environment-friendly and waterproof heat-insulating coating provided by the invention is capable of effectively isolating heat, and has excellent waterproof property, damp-proof property, corrosion resistance, ultraviolet ageing resistance, acid and alkali resistance, salt spray resistance and the like.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an environmentally friendly waterproof and heat-insulating coating. Background technique [0002] In industrial production, the waterproof and heat-insulating effect of coatings has attracted more and more attention. Due to the long-term harsh working environment, losses caused by poor waterproof and heat-insulating effects are inevitable. People's requirements for both waterproof and heat-insulating coatings growing day by day. In recent years, with the development of science and technology, the requirements for waterproof and heat-insulating coatings are getting higher and higher. However, in general, as far as the coating itself is concerned, waterproofing requires a dense coating, while thermal insulation requires a loose and porous coating, so there is a contradiction between waterproofing and thermal insulation. Contents of the invention [0003] The object of the present invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/08C09D5/33C09D7/12
Inventor 胡宏德
Owner 安徽顺金浩科技有限公司