Insole of rubber foamed shoe and preparation method thereof

A rubber foaming and natural rubber technology, applied in the field of shoes, can solve the problems of degumming of the upper and sole, easy environmental pollution, trouble, etc., and achieve the effects of good sole rebound, comfortable wearing and simple process.

Inactive Publication Date: 2015-08-05
郭萧
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional shoe-making process is cumbersome and requires the use of glue adhesives. Glue adhesives are generally toxic to a certain extent. They produce harmful gases through volatilization, which pose a threat to human health, and are easy to pollute the environment and are not environmentally friendly.
In addition, shoes made of traditional crafts are prone to degumming of the upper and sole after being worn by consumers for a period of time, and are even prone to breakage in low temperature weather.
Consumers generally report that traditional shoe-making products are heavy in weight, poor in rebound effect, and not comfortable enough to wear. There is a realistic demand for new and improved formulas for shoes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Insole of rubber foamed shoe and preparation method thereof
  • Insole of rubber foamed shoe and preparation method thereof
  • Insole of rubber foamed shoe and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] A kind of midsole of rubber foam shoe, described midsole comprises the raw material of following weight part:

[0068] 70-80 parts of natural rubber

[0069] Talc powder 0-10 parts

[0070] Rubber accelerator DM0.8-2.5 parts

[0071] Rubber accelerator M0.5-0.9 parts

[0072] Rubber accelerator D0.5-1 part

[0073] Zinc oxide 8-80 parts

[0074] 3-8 parts of stearic acid

[0075] Wear-resistant particles 0.9-1 part

[0076] MB anti-fog agent 2-2.5 parts

[0077] AC foaming agent 4-5 parts

[0078] 1-2 parts of sulfur

[0079] Paraffin 2-2.5 parts

[0080] Titanium dioxide 5-10 parts

[0081] SPC anti-aging agent 2-2.5 parts

[0082] 10-15 parts of white ointment.

Embodiment 2

[0084] Described middle end comprises the raw material of following weight portion:

[0085] 70-80 parts of natural rubber

[0086] Butadiene rubber 0-30 parts

[0087] 0-20 parts of styrene-butadiene rubber

[0088] Nitrile rubber 0-5 parts

[0089] Talc powder 0-5 parts

[0090] Rubber accelerator DM0.8-2.5 parts

[0091] Rubber accelerator M0.5-0.8 parts

[0092] Rubber accelerator D0.5-0.6 parts

[0093] Zinc oxide 8-80 parts

[0094] 3-8 parts of stearic acid

[0095] Wear-resistant particles 1 part

[0096] MB anti-fog agent 2-2.5 parts

[0097] AC foaming agent 4 parts

[0098] Sulfur 1.5-2 parts

[0099] Paraffin 2-2.5 parts

[0100] Titanium dioxide 8-10 parts

[0101] SPC anti-aging agent 2-2.5 parts

[0102] 10 parts of white ointment.

Embodiment 3

[0104] Described middle end comprises the raw material of following weight portion:

[0105] 80 parts of natural rubber

[0106]Butadiene rubber 20 parts

[0107] Rubber accelerator DM2.5 parts

[0108] Rubber accelerator M0.8 parts

[0109] 0.6 parts of rubber accelerator D

[0110] 8 parts of zinc oxide

[0111] 8 parts stearic acid

[0112] Wear-resistant particles 1 part

[0113] MB anti-fog agent 2 parts

[0114] AC foaming agent 4 parts

[0115] 1 part sulfur

[0116] 2 parts paraffin

[0117] 10 parts of titanium dioxide

[0118] SPC anti-aging agent 2 parts

[0119] 10 parts of white ointment.

[0120] A method for preparing the midsole of rubber foam shoes, comprising the following steps:

[0121] (1) Prepare foamed rubber sheet: put the sole raw material of each weight part described in the formula into a rubber mixer and mix for 30-35min to obtain foamed rubber sheet;

[0122] (2) Prepare upper mold, bottom mold and last;

[0123] (3) Put the rubber f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an insole of a rubber foamed shoe and a preparation method thereof. The insole comprises the following raw materials in parts by weight: 70-80 parts of natural rubber, 0-30 parts of cis-polybutadiene, 0.8-2.5 parts of rubber accelerator DM, 0.5-0.9 part of rubber accelerator M, 0.5-1 part of rubber accelerator D, 8-80 parts of zinc oxide, 3-8 parts of stearic acid, 0.9-1 part of wearproof particles, 2-2.5 parts of antifogging agent MB, 4-5 parts of foaming agent AC, 1-2 parts of sulfur, 2-2.5 parts of paraffin, 5-10 parts of titanium dioxide, 2-2.5 parts of anti-aging agent SPC and 10-15 parts of white factice. The preparation method comprises the following steps: putting the raw materials in the formula in a rubber mixing mill to be mixed for 30-35 minutes, thus obtaining a rubber foamed sheet; putting the prepared rubber foamed sheet in a bottom die, fixing a shoe last in a corresponding position on an upper die, sleeving the shoe last with an upper and carrying out foaming molding at a certain temperature for a certain time; removing the shoe last and the die, thus preparing the integrally formed rubber foamed shoe. The insole and the preparation method have the beneficial effects that the formula is environment-friendly; the process is simple; the shoe sole has good resilience; glue is not needed during one-time forming; the insole is free from debonding at high temperature and free from slipping at low temperature, is not broken, has light whole weight and is comfortable to wear.

Description

technical field [0001] The invention relates to a shoe, in particular to a midsole of a rubber foam shoe and a preparation method thereof. Background technique [0002] The shoes on the existing market are roughly composed of three parts: the outsole, the midsole and the upper of a shoe. The manufacturing process is generally to make the outsole, the midsole and the upper of a shoe respectively first, and then glue the outsole, the midsole and the upper of a shoe together. Glued together to form a complete shoe, the midsole and upper can also be joined by sewing. The traditional shoe-making process is cumbersome and requires the use of glue adhesives. Glue adhesives are generally toxic to a certain extent. They produce harmful gases through volatilization, which pose a threat to human health, and are easy to pollute the environment and are not environmentally friendly. In addition, shoes made by traditional techniques are prone to degumming of the upper and sole after being...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/00C08L9/06C08L9/02C08L91/06C08K13/02C08K3/34C08K3/22C08K5/09C08K3/06C08J9/10B29D35/12
CPCC08L7/00A43B13/04B29D35/122C08J9/103C08J2203/04C08J2307/00C08L2203/14C08L2205/02C08L2205/035
Inventor 郭萧
Owner 郭萧
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products