A patterned cloth, double-layer technology, which is applied in the field of processing equipment, double-layer burnt-out cloth, and double-layer burnt-out cloth, can solve the problems of long cloth processing time, high processing cost, complex device structure, etc. The effect of practical value, high processing efficiency and short process time

Active Publication Date: 2017-07-25
浙江泛太平洋针织印染有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] It can be seen that the cloth in the above patent is also processed in the same device, and the complex structure of the device also leads to a long time for cloth processing
And the processing cost is higher

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of processing technology and processing device of double-layer burnt-out cloth
  • A kind of processing technology and processing device of double-layer burnt-out cloth
  • A kind of processing technology and processing device of double-layer burnt-out cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] The processing technology of this double-layer burnt-out cloth comprises the following steps:

[0056] A. Material preparation: Prepare the double-layer burnt-out fabric of primary color. Among them, viscose fiber accounts for 33%, cotton accounts for 44%, and polyester accounts for 23% in the double-layer burnt-out gray cloth.

[0057] B. Dyeing: Dye the gray cloth by ordinary dyeing methods. In this example, dyeing was performed in an alkaline bath.

[0058] C. Shaping: After the dyed gray cloth is dried, lay the dried gray cloth flat, then impregnate the resin on the gray cloth, and then send the resin-impregnated gray cloth into the baking furnace for baking. Get shaped embryo cloth. The temperature in the baking oven is 70° C., and the baking time is 4 minutes.

[0059] D. Coating: Coating antistatic agent on the shaped gray cloth to obtain double-layer burnt-out cloth.

[0060] The original color double-layer burnt-out gray cloth can be purchased directly in ...

Embodiment 2

[0078] The processing technology of this double-layer burnt-out cloth comprises the following steps:

[0079] A. Material preparation: Prepare the double-layer burnt-out fabric of primary color. Among them, viscose fiber accounts for 33%, cotton accounts for 44%, and polyester accounts for 23% in the double-layer burnt-out gray cloth.

[0080] B. Dyeing: Dye the gray cloth by ordinary dyeing methods. In this example, dyeing was performed in an alkaline bath.

[0081] C. Shaping: After the dyed gray cloth is dried, lay the dried gray cloth flat, then impregnate the resin on the gray cloth, and then send the resin-impregnated gray cloth into the baking furnace for baking. Get shaped embryo cloth. The temperature in the baking oven is 80° C., and the baking time is 8 minutes.

[0082] D. Coating: Coating antistatic agent on the shaped gray cloth to obtain double-layer burnt-out cloth.

[0083] The original color double-layer burnt-out gray cloth can be purchased directly in ...

Embodiment 3

[0086] The processing technology of this double-layer burnt-out cloth comprises the following steps:

[0087] A. Material preparation: Prepare the double-layer burnt-out fabric of primary color. Among them, viscose fiber accounts for 33%, cotton accounts for 44%, and polyester accounts for 23% in the double-layer burnt-out gray cloth.

[0088] B. Dyeing: Dye the gray cloth by ordinary dyeing methods. In this example, dyeing was performed in an alkaline bath.

[0089] C. Shaping: After the dyed gray cloth is dried, lay the dried gray cloth flat, then impregnate the resin on the gray cloth, and then send the resin-impregnated gray cloth into the baking furnace for baking. Get shaped embryo cloth. The temperature in the baking oven is 75° C., and the baking time is 6 minutes.

[0090] D. Coating: Coating antistatic agent on the shaped gray cloth to obtain double-layer burnt-out cloth.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a processing technology and a processing device for a double-layer burnt-out fabric, belongs to the technical field of textile and solves the problem that the existing processing efficiency of the double-layer burnt-out fabric is low. The processing technology for the double-layer burnt-out fabric comprises the following steps: A, preparing materials; B, dyeing; C, shaping; D, coating. A spreading device for the double-layer burnt-out fabric comprises a hollow shell, wherein an inlet and an outlet which are communicated with the cavity of the shell are respectively formed in the left side and right side of the shell, four shuttling rods including a first shuttling rod, a second shuttling rod, a third shuttling rod and a fourth rod are connected with the interior of the shell, and are arranged in parallel. The technology is high in efficiency, and the inner space of the device is large.

Description

technical field [0001] The invention belongs to the technical field of textiles, and relates to a double-layer burnt-out cloth, in particular to a processing technology for a double-layer burnt-out cloth, and a processing device used in the processing technology. Background technique [0002] Double-layer burnt-out cloth is a general term for concave-convex style fabrics of knitted loops. Because the fabric has uniform and neat concave-convex effect, the surface in contact with the skin is superior to ordinary single-sided jersey in terms of breathability, heat dissipation, and perspiration comfort. [0003] In the existing double-layer burnt-out cloth processing method, the gray cloth is directly dyed and naturally shaped, and its processing efficiency is low, and the processing time is relatively long. [0004] Chinese patent publication No. CN101970737A provides "a method and device for closing a tubular knitted fabric at one axial end of a tubular knitted fabric at the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06P3/82D06B15/00
Inventor 胡道明谢俊刘荣福舒安君
Owner 浙江泛太平洋针织印染有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap