Super-cold-resistant impact-resistant high-toughness PP-R pipe material and preparation method thereof

A PP-R, impact-resistant technology, applied in the field of polymers, can solve the problems of PP-R pipes such as poor toughness, high low-temperature brittleness, and inability to transport water, so as to enhance toughness and impact resistance, enhance low-temperature resistance, and prolong pipe life. The effect of service life

Inactive Publication Date: 2015-09-16
CHANGZHOU UNIV
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main technical problem to be solved by the present invention is to solve the problems that the current PP-R pipe itself has poor toughness, easy aging, high low-temperature brittleness and the existing method can only be used at ultra-lo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] Example 1

[0018] A PP-R pipe material with super cold resistance, impact resistance and toughness and a preparation method thereof. The raw materials are calculated in parts by weight: 85 parts of PP-R resin and 15 parts of cold-resistant toughened masterbatch. The raw materials of cold-resistant and toughened masterbatch are: 55 parts of polypropylene, 20 parts of pigments, 20 parts of polyimide, 5 parts of nano calcium carbonate. The above ingredients are mixed, dried and granulated to obtain a particle size of 80 mesh. Cold-resistant and toughened masterbatch. A PP-R pipe material with super cold resistance, impact resistance and toughness and a preparation method thereof: it comprises the following steps: first, according to the weight of raw materials, 85 parts of PP-R resin, and 80 mesh of cold-resistant toughening masterbatch are mixed; The configured raw materials are added to the twin-screw extruder, mixed and molded, cooled, and pelletized to obtain modified m...

Example Embodiment

[0019] Example 2

[0020] A PP-R pipe material with super cold resistance, impact resistance and strong toughness and its preparation method. The raw materials are calculated in parts by weight: 95 parts of PP-R resin and 5 parts of cold-resistant toughened masterbatch. The raw materials of the cold-resistant and toughened masterbatch are: 30 parts of polypropylene, 20 parts of pigments, 40 parts of polyimide parts, and 10 parts of nano calcium carbonate. The above ingredients are mixed, dried and granulated to obtain a particle size of 100 mesh. Cold-resistant and toughened masterbatch. A PP-R pipe material with super cold resistance, impact resistance and strong toughness and its preparation method: it comprises the following steps: first, according to the weight of the raw material, 95 parts of PP-R resin, 100 mesh of cold-resistant toughening masterbatch are mixed, and then The configured raw materials are added to the twin-screw extruder, mixed and molded, cooled, and pelle...

Example Embodiment

[0021] Example 3

[0022] A PP-R pipe material with super cold resistance, impact resistance and strong toughness and its preparation method. The raw materials are calculated in parts by weight: PP-R resin 88 and cold-resistant toughened masterbatch 12. The raw materials of the cold-resistant and toughened masterbatch are: 40 parts of polypropylene, 20 parts of pigments, 35 parts of polyimide, and 5 parts of calcium carbonate. The above ingredients are mixed and dried, and granulated to obtain a particle size of 90 mesh. Tough masterbatch. A PP-R pipe material with super cold resistance, impact resistance and toughness and a preparation method thereof, which comprises the following steps: first, according to the weight of raw materials, 88 parts of PP-R resin, and 90 mesh of cold-resistant toughening masterbatch are mixed; The configured raw materials are added to the twin-screw extruder, mixed and molded, cooled, and pelletized to obtain modified material A. In the twin-screw e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a super-cold-resistant impact-resistant high-toughness PP-R pipe material and a preparation method thereof, belonging to the field of macromolecules. The method comprises the following steps: preparing materials by virtue of a PP-R resin and a cold-resistant toughened color master batch; adding the prepared raw materials into a twin-screw extruder, mixing, molding, cooling, and performing grain-sized dicing, thereby obtaining a modified material A; drying the modified material A in a drying box, thereby obtaining a modified material B; and finally, putting the modified material B on an injection molding machine, and performing injection molding to obtain the PP-R pipe. The PP-R pipe disclosed by the invention can be used at the temperature of 50 DEG C below zero to 30 DEG C below zero, the low temperature resistance of the pipe is enhanced, the water delivery problem in the northern area in winter is solved, the toughness and impact resistance of the PP-R pipe are enhanced, the PP-R pipe is difficult to age, and the service life is prolonged.

Description

technical field [0001] The invention discloses a PP-R pipe material with super cold resistance, impact resistance and toughness and a preparation method thereof, belonging to the polymer field. Background technique [0002] PP-R (polypropylene random) pipe is also called three-type polypropylene pipe and random copolymerized polypropylene pipe or PPR pipe. With the advantages of easy maintenance and long service life, it is widely used in construction, municipal, industrial and agricultural fields such as building water supply and drainage, urban and rural water supply and drainage, city gas, electric power and optical cable sheathing, industrial fluid transportation, and agricultural irrigation. The PP-R pipe is made of random copolymerized polypropylene, which is extruded into pipes and injection molded into pipe fittings. The PPR pipe itself has the disadvantages of poor toughness, easy aging, and high low temperature brittleness. [0003] At present, there are many way...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/14C08L23/12C08L79/04C08K3/26C08J3/22B29C47/92B29C45/77B29C45/78F16L9/12B29C48/92
CPCC08L23/14B29C45/77B29C45/78B29C48/92B29C2948/9258B29C2948/92704C08J3/226C08J2323/14C08J2423/12C08K2201/011C08L2203/18C08L2205/03C08L2205/06C08L2310/00F16L9/12C08L23/12C08L79/04C08K2003/265
Inventor 郭迎庆薛红娟
Owner CHANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap