A technology for leather and raw materials is applied in the field of virus inactivation of animal-derived biological dressings, which can solve the problem of low virus inactivation efficiency and achieve the effects of improving virus inactivation efficiency, improving safety and low cost.

Inactive Publication Date: 2017-09-22
CHANGSHA DARUIQI IND
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Based on this, it is necessary to address the problem of low virus inactivation efficiency and provide a method for preparing dressings with high virus inactivation efficiency and safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0021] The preparation method of the dressing skin of an embodiment, comprises the following steps:

[0022] S100: Depilate the heterogeneous leather material, scrape off the fat and cuticle, and obtain the heterogeneous leather material with a thickness of 0.3-0.5 mm.

[0023] Preferably, the thickness of the different leather material is 0.3mm.

[0024] Preferably, the heterogeneous skin raw material is pigskin raw material, and pigskin is similar to human skin in structure, and it can better adhere to the wound surface, play a role in reducing water evaporation of the wound surface, reducing electrolyte loss, blocking bacteria and controlling infection. The clinical effect is good, and it is a better alternative skin allograft, which has been widely used in the field of burns and scalds.

[0025] As a wound dressing skin of animal origin, pigskin must be strictly controlled for its viral load. Therefore, the choice of virus inactivation process is very important. Accordi...

Embodiment 1

[0056] Depilate the heterogeneous leather raw material, scrape off the fat and cuticle, and obtain the heterogeneous leather material with a thickness of 0.3mm, soak the heterogeneous leather material in 1mol / L NaCl solution at room temperature for 20h, wash with sterile water, and wash with 37℃ Soak in 0.35% neutral protease solution for 4 hours, and then wash with sterile water to obtain xenograft skin.

[0057] Put the xenograft in a shaker with an oscillation frequency of 100 rpm. Control the temperature to 60° C. in a constant temperature water bath, and heat for 120 minutes to obtain the virus-inactivated heterogeneous skin. The heterogeneous skin that has been preliminarily inactivated by the virus is irradiated with gamma rays with an irradiation dose of 25 kGy to obtain the dressing skin.

Embodiment 2

[0059] Depilate the heterogeneous leather raw material, scrape off the fat and cuticle, and obtain the heterogeneous leather material with a thickness of 0.5mm. Soak the heterogeneous leather material in 2mol / L NaCl solution at room temperature for 12h, wash with sterile water, and wash with 37℃ Soak in 0.5% neutral protease solution for 6 hours, and then wash with sterile water to obtain xenograft skin.

[0060] Put the xenograft in a shaker, and the shaking frequency of the shaker is 110rpm. Control the temperature to 55° C. in a constant temperature water bath, and heat for 90 minutes to obtain the heterogeneous skin with the virus initially inactivated. The heterogeneous skin that has been preliminarily inactivated by the virus is irradiated with gamma rays with an irradiation dose of 15 kGy to obtain the dressing skin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a dressing skin, which comprises the following steps: depilating the raw material of the heterogeneous skin, scraping off the fat and the horny layer to obtain the heterogeneous skin material with a thickness of 0.3-0.5 mm; soaking the heterogeneous skin material in NaCl solution in sequence , washing with sterile water, soaking with a neutral protease solution with a mass fraction of 0.2 to 0.5% at 37°C, and washing with sterile water to obtain heterogeneous skins; and inactivating the heterogeneous skins to obtain dressing skins. The inactivation treatment includes: The heterogeneous skin is heated at 50-60° C. for 60-120 minutes, and the heterogeneous skin is irradiated with gamma rays. The preparation method of the above-mentioned dressing skin is simple in operation and low in cost, and can completely inactivate the four viruses of PRV, VSV, PV1 and PPV. , Improve the safety of the dressing skin.

Description

technical field [0001] The invention relates to the technical field of animal-derived biological dressing virus inactivation, in particular to a preparation method of dressing skin. Background technique [0002] Existing heterogeneous skins used for burns, thermal injuries or chemical injuries are often pigskin. The structure of pigskin is similar to that of human skin. It can better adhere to the wound surface, reduce the evaporation of wound surface water, reduce electrolyte loss, block bacteria and control infection. It has good clinical effect and is a good alternative Alternative skin for selection has been widely used in the fields of burns and scalds. As a wound dressing skin of animal origin, pigskin must be strictly controlled for its viral load. Therefore, the choice of virus inactivation process is very important. At present, pigskin for burns and scalds is mainly irradiated with gamma rays (gamma rays) to inactivate viruses. [0003] According to the provisio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L15/40
Inventor 周天行
Owner CHANGSHA DARUIQI IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap