A technology of imitating granite paint and granite stone powder, applied in the field of paint, can solve the problems of complicated operation procedures, fogging and pollution of sprayed real stone paint, and achieve the effects of improving stain resistance, unique decorative beauty and strong simulation effect.

Inactive Publication Date: 2015-09-30
TIANJIN WANGJIU SCI & TECH DEV
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the need for relatively large air pressure during spraying, the sand particles will cause waste and pollution due to rebound, and the technical requirements for spraying construction are relatively strong, and the operation procedures are cumbersome, so there is a certain difficulty in popularization. will affect the overall effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] In parts by weight, add 100 parts of water, 15 parts of ethylene glycol, 2 parts of dispersant, 40 parts of 3% hydroxyethyl cellulose solution, 30 parts of 10% inorganic gel, and 1 part of wetting agent into the dispersion tank Disperse evenly, then add 2 parts of defoamer, adjust the speed to 1000r / min and disperse for 20min, after adjusting the speed to 600r / min, add 500 parts of granite stone powder, after dispersing for 3min, add 3 parts of defoamer, elastic 50 parts of polymer emulsion, 50 parts of rigid polymer emulsion, 5 parts of film-forming auxiliary agent, stirred for 5 minutes, then added 10 parts of thickener, 20 parts of water, dispersed for 30 minutes, and the imitation granite coating I was prepared.

Embodiment 2

[0027] In parts by weight, add 140 parts of water, 15 parts of ethylene glycol, 3 parts of dispersant, 45 parts of 3% hydroxyethyl cellulose solution, 35 parts of 10% inorganic gel, and 2 parts of wetting agent into the dispersion tank Disperse evenly, then add 3 parts of defoamer, adjust the speed to 1000r / min and disperse for 20min, after adjusting the speed to 600r / min, add 525 parts of granite stone powder, after dispersing for 3min, add 3 parts of defoamer, elastic 55 parts of polymer emulsion, 60 parts of rigid polymer emulsion, 6 parts of film-forming aid, stirred for 5 minutes, then added 15 parts of thickener and 20 parts of water, dispersed for 30 minutes, and the imitation granite coating II was prepared.

Embodiment 3

[0029] In parts by weight, add 160 parts of water, 15 parts of ethylene glycol, 4 parts of dispersant, 50 parts of 3% hydroxyethyl cellulose solution, 40 parts of 10% inorganic gel, and 2 parts of wetting agent into the dispersion tank Disperse evenly, then add 3 parts of defoamer, adjust the speed to 1000r / min and disperse for 20min, after adjusting the speed to 600r / min, add 550 parts of granite stone powder, disperse for 3min, then add 3 parts of defoamer in order, 60 parts of elastic polymer emulsion, 70 parts of rigid polymer emulsion, 6 parts of film-forming aid, stir for 5 minutes, then add 15 parts of thickener and 20 parts of water, disperse for 30 minutes, and then make imitation granite paint III.

[0030] The imitation granite coating that preparation method is made by above-mentioned embodiment, the effect that test data and actual construction produce are as follows:

[0031] Sample serial number

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
minimum film forming temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of paints, and particularly relates to a granite-like paint which is prepared by the following steps: adding 15 parts by weight of ethylene glycol, 2-4 parts by weight of dispersing agent, 40-50 parts by weight of 3% hydroxyethyl cellulose solution, 30-40 parts by weight of 10% inorganic gel, 1-2 parts by weight of wetting agent and 100-160 parts by weight of water into a dispersion kettle, dispersing uniformly, adjusting the rotation speed to 600 r/min, adding 500-550 parts by weight of granite powder, dispersing for 3-5 minutes, sequentially adding 3-4 parts by weight of defoaming agent, 50-70 parts by weight of rigid polymer emulsion, 50-60 parts by weight of elastic polymer emulsion and 5-6 parts by weight of film-forming assistant, stirring for 5 minutes, adding 10-15 parts by weight of thickener and 20 parts by weight of water, and dispersing for 30 minutes to obtain the granite-like paint. The granite-like paint has the stone sensation of the traditional natural stone paint. The coated film has comparable textures with the external wall ceramic tile, and has high simulation effect.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to a granite imitation coating. Background technique [0002] As an important decorative material for building exterior walls, ceramic tiles have the characteristics of good durability, strong stain resistance and elegant appearance, but due to their excessive weight, it is difficult to firmly bond them to buildings, and they are often injured due to falling off. People (objects), and the bearing capacity of the surface of the external thermal insulation system is limited, which will cause unnecessary losses and dangers due to easy peeling off. [0003] At present, the mainstream method of replacing ceramic tiles is to achieve by spraying real stone paint. The realization method is to use granite stone powder and organic polymer emulsion to compound, and spray it on the wall through a pressure spray gun. However, due to the need for relatively large air pressure during spraying, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B24/38C04B14/04
Inventor 王启旺
Owner TIANJIN WANGJIU SCI & TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap