Roller coating type simulated face brick coating and construction method

A technology of simulation and roller coating, applied in the direction of coating, etc., can solve the problems of increased anti-pollution performance, and achieve the effects of saving materials, reducing loss and pollution, and high efficiency

Active Publication Date: 2014-05-14
BAOJI JIALILAI BUILDING DECORATION
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of roller coating type imitation facing brick coating and construction method for the construction of roller coating in order to solve the above technical problems. During the roller coating process, there will be no waste and pollution caused by the rebound of sand particles; and the simulation effect after roller coating is good, and there will be no blooming phenomenon; due to its fine and dense surface, the anti-pollution performance is greatly improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Roller coating type simulated face brick coating and construction method
  • Roller coating type simulated face brick coating and construction method
  • Roller coating type simulated face brick coating and construction method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 150 parts by weight of water, 20 parts by weight of ethylene glycol, 3 parts by weight of dispersant, 1 part by weight of AMP95, 50 parts by weight of 2% hydroxyethyl cellulose solution, 30 parts by weight of 10% inorganic gel, 1 part by weight of wetting agent Add the parts by weight into the dispersing tank to disperse evenly, then add 2 parts by weight of defoamer, adjust the speed to 800-1200r / min and disperse for 20 minutes, after adjusting the speed to 600r / min, add 550 parts by weight of natural stone powder and disperse for 3 minutes, then follow the order Add 4 parts by weight of defoamer, 50 parts by weight of elastic polymer emulsion, 100 parts by weight of rigid polymer emulsion, 10 parts by weight of film-forming aid and stir for 5 minutes, then add 9 parts by weight of hydrophobically modified alkali-swellable thickening type thickener , 2 parts by weight of hydrophobically modified alkali-swellable associative thickener, 1.5 parts by weight of bactericide,...

Embodiment 2

[0040] 135 parts by weight of water, 10 parts by weight of ethylene glycol, 4 parts by weight of dispersant, 1.5 parts by weight of AMP95, 75 parts by weight of 2% hydroxyethyl cellulose solution, 30 parts by weight of 10% inorganic gel, 1.5 parts by weight of wetting agent Add parts by weight into the dispersing tank to disperse evenly, then add 3 parts by weight of defoamer and adjust the speed to 800-1200r / min to disperse for 20 minutes, after adjusting the speed to 600r / min, add 550 parts by weight of natural stone powder and disperse for 3 minutes, then follow the order Add 4 parts by weight of defoamer, 75 parts by weight of elastic polymer emulsion, 75 parts by weight of rigid polymer emulsion, 7 parts by weight of film-forming aid and stir for 5 minutes, then add 7 parts by weight of hydrophobically modified alkali-swellable thickening type thickener , 3 parts by weight of hydrophobically modified alkali-swellable associative thickener, 1.5 parts by weight of bactericid...

Embodiment 3

[0042]120 parts by weight of water, 10 parts by weight of ethylene glycol, 3 parts by weight of dispersant, 2 parts by weight of AMP95, 50 parts by weight of 2% hydroxyethyl cellulose solution, 30 parts by weight of 10% inorganic gel, and 2 parts by weight of wetting agent Add parts by weight into the dispersing tank to disperse evenly, and then add 3 parts by weight of defoamer to adjust the speed to 800-1200r / min and disperse for 20 minutes. After adjusting the speed to 600r / min, add 600 parts by weight of natural stone powder to disperse for 3 minutes, and then Add 4 parts by weight of defoamer, 100 parts by weight of elastic polymer emulsion, 50 parts by weight of rigid polymer emulsion, 5 parts by weight of film-forming aid and stir for 5 minutes, then add 5 parts by weight of hydrophobically modified alkali-swellable thickening type thickener , 5 parts by weight of hydrophobically modified alkali-swellable associative thickener, 1.5 parts by weight of bactericide, and 10 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
minimum film forming temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of coatings, and particularly relates to a roller coating type simulated face brick coating and a construction method. The roller coating type simulated face brick coating is prepared by dispersing the following components in parts by weight in a dispersing kettle: 10-20 parts of ethylene glycol, 2-6 parts of dispersing agents, 1-2 parts of AMP 95, 50-100 parts of 2% hydroxy ethyl cellulose solutions, 30-50 parts of 10% inorganic gels, 1-2 parts of wetting agents, 3-9 parts of defoaming agents, 500-600 parts of natural rock flour, 50-100 parts of rigid polymer emulsions, 50-100 parts of elastic polymer emulsions, 5-10 parts of film forming auxiliary agents, 5-10 parts of hydrophobic modified alkali swelling thickening type thickening agents, 1-6 parts of hydrophobic modified alkali swelling associating type thickening agents, 1-2 parts of sterilizing agents and 110-240 parts of water. According to the invention, a coated film grain obtained after roller coating is more similar to that of an exterior wall tile.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a roller-coated imitation brick coating and a construction method. Background technique [0002] As a kind of building exterior wall decoration materials, ceramic tiles are widely loved by users because of their good durability, strong anti-contamination and beautiful appearance. However, due to the frequent occurrence of external wall tiles falling off and injuring people (things), many places have banned the use of tiles on high-rise buildings because the original tiles have too much weight, high water absorption, and poor bonding. At present, the surface of the mainstream external thermal insulation system has limited bearing capacity, so it is easy to peel off and cause unnecessary losses and dangers. However, the building's demand for ceramic tile modeling has not decreased, which has prompted the rapid development and expansion of the paint imitation brick system. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D101/26C09D7/12
Inventor 李喜杨锐毛宝文龙军林
Owner BAOJI JIALILAI BUILDING DECORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap