Spray film waterproof material capable of preventing splashing and its preparation and use method

A spray film waterproof and raw material technology, applied in the direction of coating, etc., can solve the problems of splashing on the builder's body, construction difficulty, splashing on the ground, etc., to prevent splashing and rebounding, reduce rebounding splash, reduce Rebound splash effect

Inactive Publication Date: 2017-06-06
成都市嘉洲新型防水材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the process of spraying the waterproof membrane on the wall or wall on the surface of the main body of the project, it is found that there is a common problem in the above-mentioned prior art, that is, when the waterproof coating is sprayed on the wall or the wall, its contact with the wall or the wall In an instant, under the injection pressure of the spray gun, after the liquid waterproof coating touches the wall, some of the liquid material will collide with the wall or the wall and splash outwards, thus splashing on the builder or splashing on the ground, especially Especially in the construction of waterproof spray film coating in special tunnels with poor working environment, the phenomenon of splash rebound is particularly serious. The splash rebound during the spraying process of this kind of paint not only brings construction difficulty to the staff, but also greatly reduces The utilization rate of acrylate materials has caused a high degree of waste and loss of materials, and the waterproof spray coating that splashes and rebounds is easy to be inhaled by construction operators and damage their health
[0005] In the prior art, in order to alleviate the splash rebound phenomenon in the paint spraying process, it is usually adjusted by adjusting the air pressure of the spray gun, but the effect of this adjustment is not ideal, and when the air pressure is adjusted to be small, the spraying efficiency is greatly improved. reduce, and this method also increases equipment cost and operational difficulty

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] A kind of spray film waterproof material that can prevent splashing proposed by the present invention, its raw material is divided into A component and B component, and its A component raw material comprises by weight:

[0057] Magnesium Acrylate Monomer Solution................................100 parts,

[0058] Polyvinyl alcohol solution ................................ 2 parts,

[0059] Kaolin ............................................. 2 parts,

[0060] Silica .............................................. 2 parts,

[0061] Calcium Carbonate ................................. 2 parts,

[0062] Alkaline conditioner—sodium hydroxide................................1~2 parts;

[0063] Its method for preparing A component raw material comprises the steps:

[0064] Step A: Add 2 parts of polyvinyl alcohol solution to 100 parts of magnesium acrylate monomer solution, and stir evenly for 30 minutes at a stirring speed of 1000 r / min;

[0065] Step B: Add 2 parts of kao...

Embodiment 2

[0088] A kind of spray film waterproof material that can prevent splashing proposed by the present invention, its raw material is divided into A component and B component, and its A component raw material comprises by weight:

[0089] Magnesium Acrylate Monomer Solution................................100 parts,

[0090] Polyvinyl alcohol solution ................................. 5 parts,

[0091] Kaolin ............................................10 parts,

[0092] Silica .............................................10 parts,

[0093] Calcium Carbonate ................................. 10 parts,

[0094] Alkaline conditioner——sodium hydroxide............ 3-4 parts;

[0095] Its method for preparing A component raw material comprises the steps:

[0096] Step A: Add 5 parts of polyvinyl alcohol solution to 100 parts of magnesium acrylate monomer solution, stir evenly for 30 minutes, and the stirring speed is 1200r / min;

[0097] Step B: add 10 parts of kaolin, 10 parts of w...

Embodiment 3

[0120] A kind of spray film waterproof material that can prevent splashing proposed by the present invention, its raw material is divided into A component and B component, and its A component raw material comprises by weight:

[0121] Magnesium Acrylate Monomer Solution................................100 parts,

[0122] Polyvinyl alcohol solution................................10 parts,

[0123] Kaolin ................................. 20 parts,

[0124] Silica .............................................10 parts,

[0125] Calcium Carbonate ................................. 20 parts,

[0126] Alkaline conditioner——sodium hydroxide................................4~5 parts;

[0127] Its method for preparing A component raw material comprises the steps:

[0128] Step A: Add 10 parts of polyvinyl alcohol solution to 100 parts of magnesium acrylate monomer solution, stir evenly for 30 minutes, and the stirring speed is 1500 r / min;

[0129] Step B: Add 20 parts of kaolin, 20 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a spraying-film waterproof material capable of preventing splashing, and a preparation and application method thereof. The spraying-film waterproof material is prepared from the following raw materials in parts by weight: 100 parts of magnesium acrylate monomer solution, 2-10 parts of polyvinyl alcohol solution, 2-20 parts of kaolin, 2-20 parts of silica white and 2-20 parts of calcium carbonate. By utilizing the technical characteristics of adhesiveness in the polyvinyl alcohol solution and compatibility in the magnesium acrylate monomer solution, after the main material and reducer of the spraying-film waterproof material are mixed and the auxiliary material and oxidizer are mixed, when the main material and auxiliary material are sprayed to a wall surface or any other application substance surface by a two-inlet one-outlet spray gun, the adhesive action of the polyvinyl alcohol is utilized to promote the components A and B of the spraying-film waterproof material to be quickly bound with the coating substance surface, thereby preventing the phenomena of splashing and rebounding, enhancing the use rate of the acrylate material and reducing the material waste. The spraying-film waterproof material is convenient for construction, and better protects good health of the constructors.

Description

technical field [0001] The invention relates to a spray-film waterproof material, in particular to a liquid spray-coat waterproof material, in particular to a spray-film waterproof material capable of preventing splashing and its preparation and use methods, belonging to the technical field of waterproof coatings. Background technique [0002] In tunnels and other underground projects of basic engineering facilities, the requirements for anti-leakage water are very high. The waterproofing measures currently adopted are usually by spraying film construction, that is, spraying the main material of spraying film in liquid state on the surface of the main body of the project or geomembrane that needs to be waterproofed, and the coating will solidify after drying to form a layer. Waterproof membrane to achieve the purpose of waterproofing. In order to speed up the formation time of the waterproof film, the prior art is to divide the waterproof spray film material into two parts,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/12
Inventor 杨其新刘东民盛草樱蒋雅君张玉兰
Owner 成都市嘉洲新型防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products