Modified asphalt waterproof coiled material

A technology for modifying asphalt and waterproofing membranes, which is applied in asphalt layered products, building insulation materials, building components, etc., can solve the problems of poor environmental protection effect, low tensile properties of ordinary polymer waterproofing membranes, and ordinary modified asphalt waterproofing. Short coil life and other problems, achieve the effect of small linear expansion coefficient, improved storage stability, and high practicability

Active Publication Date: 2015-10-07
SICHUAN SHUYANG WATERPROOF MATERIAL
View PDF8 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a modified asphalt waterproofing membrane to solve the problems of low tensile performance, poor environmental protection effect, and short service life of ordinary modified asphalt waterproofing membranes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Heat 40 parts of asphalt to 170-180°C and add quantitatively into mixing tank A, start the agitator when the material level of the mixing tank reaches 25%, add 20 parts of measured high-density polyethylene and 15 parts of SBS rubber; after mixing evenly , after being ground by a colloid mill, pumped to the mixing tank B, adding 0.2 parts of stabilizer, 0.5 parts of antioxidant, 0.1 part of light stabilizer and 10 parts of filler, stirred for 30 minutes, and pumped to the colloid mill after grinding Send it to the mixing tank B again for mixing, and repeat this four times to obtain the finished modified asphalt; during the synthesis process, the temperature of the mixing tanks A and B is kept at 190-200°C, the speed of the mixer in the mixing tank A is controlled at 10-20rpm, and the mixing The tank B stirrer speed was controlled at 10-15 rpm. Put the modified asphalt into the screw extruder, and extrude the carcass through the screw extruder. While extruding into the c...

Embodiment 2

[0024] Heat 40 parts of asphalt to 170-180°C and add quantitatively into mixing tank A, start the agitator when the material level of the mixing tank reaches 25%, add 25 parts of measured high-density polyethylene and 15 parts of SBS rubber; after mixing evenly , after being ground by a colloid mill, pumped to the mixing tank B, adding 0.5 parts of stabilizer, 0.7 parts of antioxidant, 1 part of light stabilizer and 15 parts of filler, after stirring for 30 minutes, pumped to the colloid mill after grinding Send it to the mixing tank B again for mixing, and repeat this four times to obtain the finished modified asphalt; during the synthesis process, the temperature of the mixing tanks A and B is kept at 190-200°C, the speed of the mixer in the mixing tank A is controlled at 10-20rpm, and the mixing The tank B stirrer speed was controlled at 10-15 rpm. Put the modified asphalt into the screw extruder, and extrude the carcass through the screw extruder. While extruding into the ...

Embodiment 3

[0026] Heat 45 parts of asphalt to 170-180°C and add quantitatively into mixing tank A, start the agitator when the material level of the mixing tank reaches 25%, add 20 parts of measured high-density polyethylene and 20 parts of SBS rubber; after mixing evenly , after being ground by a colloid mill, pumped to the mixing tank B, adding 1 part of stabilizer, 1 part of antioxidant, 1 part of light stabilizer and 10 parts of filler, stirred for 30 minutes, and then pumped to the colloid mill for grinding Send it to the mixing tank B again for mixing, and repeat this four times to obtain the finished modified asphalt; during the synthesis process, the temperature of the mixing tanks A and B is kept at 190-200°C, the speed of the mixer in the mixing tank A is controlled at 10-20rpm, and the mixing The tank B stirrer speed was controlled at 10-15 rpm. Put the modified asphalt into the screw extruder, and extrude the carcass through the screw extruder. While extruding into the carcas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of waterproof building materials, in particular to a modified asphalt waterproof coiled material, and aims to solve the problems such that the common polymer waterproof coiled material is low in tensile performance and poor in environment friendliness and the common modified asphalt waterproof coiled material is short in life. The modified asphalt waterproof coiled material comprises modified asphalt, polypropylene fiber cloth and PE (polyethylene) film; the modified asphalt is synthetically made from, by weight, 40 to 50 parts of asphalt, 20 to 30 parts of high-density polyethylene, 15 to 30 parts of SBS (styrene butadiene styrene) rubber, 0.2 to 2 parts of stabilizer, 0.5 to 1 part of antioxidant, 0.1 to 2 parts of photo-stabilizer, and 10 to 20 parts of filler.

Description

technical field [0001] The invention relates to the field of waterproof building materials, in particular to a modified bitumen waterproof coiled material. Background technique [0002] Since the 1970s, developed countries in the world have begun to change in the structure of waterproof materials, gradually developing to new waterproof materials such as modified asphalt, self-adhesive, and synthetic polymer materials. At present, foreign new waterproof materials have accounted for more than 90% of the total market, and product quality, function, and service life have reached a relatively high level. Since the application of asphalt membranes in my country's waterproof projects in the 1970s, asphalt waterproof materials have always been the leading product for building waterproofing, accounting for about 70% of the total market recently, and polymer waterproof materials accounted for only about 10%. Others For waterproof coatings and other waterproof materials. Polyethylene ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B11/10B32B27/02B32B27/12B32B27/18C08L95/00C08L23/06C08L53/02C08K13/02C08K5/5425C08K5/13C08K3/26C08K3/04C08K3/06
CPCB32B11/10B32B27/12B32B27/18B32B2262/0253B32B2307/712B32B2307/714B32B2307/73B32B2419/06C08L95/00C08L2205/03C08L2207/062C08L23/06C08L53/02C08K13/02C08K5/5425C08K5/13C08K2003/265C08K3/04C08K3/06
Inventor 骆晓彬
Owner SICHUAN SHUYANG WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap