A concrete curing protective agent

A protective agent and concrete technology, applied in the field of building materials, can solve the problem of low brightness, and achieve the effects of short curing time, improved brightness, and excellent waterproof and oil resistance.

Inactive Publication Date: 2017-07-18
湖南交泰建材有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned concrete sealing and curing agent has the advantages of short curing time, thick surface hardened layer and high surface hardness, but the brightness of the concrete surface after curing needs to be polished to reflect, and the brightness is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A concrete curing protective agent
  • A concrete curing protective agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The concrete surface curing protective agent of this embodiment is made of the following raw materials in terms of weight percentage: nano-silica (5-10nm) 20wt.%, lithium silicate 20wt.%, acrylate emulsion (solid content 50%) 20wt.%, sodium methyl silicate 8wt.%, benzyl alcohol 1wt.%, and the rest is deionized water. Dissolve nano-silica, silicate, acrylate, water-repellent and film-forming aids in deionized water, stir quickly and evenly, and obtain a milky white liquid, which is the concrete curing and protecting agent.

[0030] After using the above-mentioned curing protective agent on the concrete surface, the ground performance test results are as follows (as a blank control with the concrete test block without curing protective agent):

[0031] Table 1

[0032]

Embodiment 2

[0034] The concrete surface curing protective agent of this embodiment is made of the following components in terms of weight percentage: nano-silica (30-40nm) 28wt.%, sodium silicate 10wt.%, styrene-acrylate emulsion ( Solid content 50%) 32wt.%, siloxane 12wt.%, propylene glycol butyl ether 5wt.%, the rest is deionized water. The preparation method is the same as in Example 1.

[0035] After using the above-mentioned curing protective agent on the concrete surface, the ground performance test results are as follows (as a blank control with the concrete test block without curing protective agent):

[0036] Table 2

[0037]

[0038] For better reflecting performance advantage of the present invention, also made following several comparative experiments, other unmarked conditions are identical with embodiment 1;

[0039] table 3

[0040] Nano silica Silicate Acrylate Hydrophobic agent Coalescent Example 1 20wt.% 20wt.% 20wt.% 8wt.% 1wt.% ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a concrete curing protective agent, which is prepared from the following components by weight percent: 20-30wt.% of nano-silica, 10-20wt.% of silicate, 20-35wt.% of acrylic ester, 8-15wt.% of a water repellent, 1-5wt.% of a film-forming assistant, and the balance water. The curing protective agent can improve the hardness and wear resistance of concrete ground, effectively solves the problems of concrete ground sugaring, dusting and the like, also can endow concrete with excellent waterproof and oil resistant properties, and can greatly improve the brightness of concrete ground without polishing.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a curing protective agent applied to concrete floors. Background technique [0002] At present, concrete floors are widely used in shopping malls, docks, parking lots, logistics centers and 4S stores. However, during the long-term use of the traditional concrete floor, there will be problems such as sanding, dusting, surface hardness and brightness reduction. [0003] The curing agent currently on the market can effectively solve the problems of sanding and dusting, but its brightness can only be reflected through polishing, and it does not have good waterproof and oil-resistant properties. [0004] The Chinese invention patent application with application number 201110152386.4 discloses an improved liquid concrete sealing and curing agent. It consists of the following components: 70-90wt% silicate, 0.05-0.2wt% penetrant, 0.3-0.5wt% surfactant, 0.4-0.6wt% surface m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/26C04B41/50C04B14/06C04B24/04
Inventor 杨建西韩燕余旦
Owner 湖南交泰建材有限公司